Electric cable

A kind of cable and plant ash technology, which is applied in the direction of insulating cables, cables, circuits, etc., can solve unsatisfactory problems, achieve strong flame retardancy, significant economic and environmental benefits, and reduce production costs

Active Publication Date: 2016-01-13
正规电线电缆(东莞)有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these current cable sheathing tubes are still not ideal in terms of strength, rigidity and flame retardancy, or there is only a certain improvement in the performance of a certain aspect, and there is a lot of room for further improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A cable, which sequentially includes a wire core, an insulating layer, an inner sheath and a sheath tube from the inside to the outside, and the raw materials of the sheath tube, in parts by weight, include:

[0039] Ethylene-octene copolymer (Foshan Jinzeqiang Plastic Raw Materials Co., Ltd. ENGAG8003) 90 parts

[0040] Plant ash 5 parts

[0041] 3 parts gum

[0042] 0.8 parts of butadienyl triethoxysilane

[0043] 2 parts stearic acid

[0044] White carbon black 0.8 parts

[0045] 5 parts of electrolytic zinc acid leaching residue;

[0046] Preparation method: comprising the following steps:

[0047] (1) Melt blending: Mix polyolefin, plant ash, silane coupling agent, stearic acid, and electrolytic zinc acid leaching residue according to the above ratio, stir at a speed of 600r / min for 10min, and then melt blend at 170°C for 10min , get rubber;

[0048] (2) Cross-linking: After cross-linking the rubber obtained in step (1) at 170°C for 30 minutes, then add gum ...

Embodiment 2

[0053] A cable, which sequentially includes a wire core, an insulating layer, an inner sheath and a sheath tube from the inside to the outside, and the raw materials of the sheath tube, in parts by weight, include:

[0054] Ethylene-octene copolymer (ENGAG8003, Foshan Jinzeqiang Plastic Raw Materials Co., Ltd.) 80 parts

[0055] Plant ash 2 parts

[0056] 1 part gum

[0057] 0.5 parts of butadienyl triethoxysilane

[0058] 1 part stearic acid

[0059] White carbon black 0.6 parts

[0060] 3 parts of electrolytic zinc acid leaching residue;

[0061] Preparation method: comprising the following steps:

[0062] (1) Melt blending: Mix polyolefin, plant ash, silane coupling agent, stearic acid, and electrolytic zinc acid leaching residue according to the above ratio, stir at a speed of 600r / min for 10min, and then melt blend at 170°C for 10min , get rubber;

[0063] (2) Cross-linking: After cross-linking the rubber obtained in step (1) at 170°C for 30 minutes, then add gum a...

Embodiment 3

[0068] A cable, which sequentially includes a wire core, an insulating layer, an inner sheath and a sheath tube from the inside to the outside, and the raw materials of the sheath tube, in parts by weight, include:

[0069] Ethylene-octene copolymer (Foshan Jinzeqiang Plastic Raw Materials Co., Ltd. ENGAG8003) 85 parts

[0070] 3 parts plant ash

[0071] 2 parts gum

[0072] 0.6 parts of butadienyl triethoxysilane

[0073] 1.5 parts of stearic acid

[0074] 0.7 parts of white carbon black

[0075] 4 parts of electrolytic zinc acid leaching residue;

[0076] Preparation method: comprising the following steps:

[0077] (1) Melt blending: Mix polyolefin, plant ash, silane coupling agent, stearic acid, and electrolytic zinc acid leaching residue according to the above ratio, stir at a speed of 600r / min for 10min, and then melt blend at 170°C for 10min , get rubber;

[0078] (2) Cross-linking: After cross-linking the rubber obtained in step (1) at 170°C for 30 minutes, then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses an electric cable, and relates to the field of electricity facility. Raw materials of the sheath tube of the cable comprise, by weight, 85 parts of polyolefin, 3 parts of plant ash, 2 parts of gum, 0.6 parts of a silane coupling agent, 1.5 parts of stearic acid, 0.7 parts of white carbon black, and 4 parts of electrolytic zinc acid leaching residue. The tensile strength of the cable sheath tube is higher than 26 MPa. The breaking elongation of the cable sheath tube is higher than 750%. The oxygen index of the cable sheath tube is higher than 36. The flame retarding performance of the cable sheath tube reaches the A level. The cable sheath tube also has significant characteristics of high strength and high flame retarding performance. Also, plant ash and electrolytic zinc acid leaching residue are recycled, such that environment pollution is reduced, and production cost is reduced. The electric cable has significant economic and environmental benefits.

Description

[0001] This application is a divisional application of Chinese Patent Application No.: 2014101586477; Invention Name: High Strength High Flame Retardancy Cable; Application Date: 2014.04.21. technical field [0002] The invention relates to the field of electric facilities, in particular to a cable with high strength and high flame retardancy. Background technique [0003] With the gradual acceleration of the urbanization process, urban planning is becoming more and more modern. In the process of urban construction, cable entry into the ground has become the minimum construction requirement. At the same time, in the process of urban transformation, it is also necessary to put various cables erected in the air into the ground. At present, the construction of cables into the ground often adopts non-excavation technology. This construction method has the advantages of no impact on traffic, little damage to the stratum structure, and short cycle. , has the performance: the ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L5/00C08K13/02C08K5/09C08K3/36C08K3/34C08J3/24H01B3/44
CPCC08J3/24C08J3/246C08J2323/08C08J2405/00C08L23/0815C08L2201/02C08L2203/20C08L2203/202H01B3/441H01B7/18C08L5/00C08K13/02C08K3/36C08K5/09C08K3/34C08K5/5425C08K3/22
Inventor 赵月
Owner 正规电线电缆(东莞)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap