Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Novel antibacterial textile fabric special for infants and preparing method thereof

A technology for textile fabrics and babies, which is applied in the field of new antibacterial textile fabrics and its preparation, which can solve the problems of newborn skin screening and fabrics that cannot meet the special physiological characteristics of newborn babies, and achieve strong strength, simple manufacturing process, and strong moisture absorption. performance effect

Active Publication Date: 2016-01-13
安徽京威纺织服饰有限公司
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] It can be seen from the above prior art that there are not many antibacterial textiles for babies at present. Most of them use ordinary antibacterial fabrics selectively for baby clothes, and most of them use fibers with antibacterial properties or antibacterial agents to give fabrics antibacterial properties. Chemical textile auxiliaries are used to improve the durability of antibacterial fabrics, but they have not been screened for the characteristics of newborn skin, and the prepared fabrics cannot meet the needs of special physiological characteristics of newborn babies. Therefore, it is very necessary to develop a special antibacterial fabric for babies. fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel antibacterial textile fabric special for infants and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) The flat ribbon multifilament helix fiber composed of 4 3μm monofilaments is extracted by physical method as the weft, and the 13tex cotton fiber is used as the warp. The dosage ratio of the lotus fiber to the cotton fiber is 1:1.5. Using double-layer plain weave as the organizational structure, weaving to form a fiber layer of 189g / ㎡.

[0031] (2) In parts by weight, dissolve 20 parts of hydrolyzed chitosan with a molecular weight of 2000 in water, add 15 parts of aloe extract, stir well, and finally add 35 parts of sodium alginate. Dissolve to form a transparent and uniform antibacterial viscous liquid.

[0032] (3) After tentering and finishing the fiber layer prepared in step (1), the surface of the fiber layer is coated with the antibacterial viscous liquid prepared in step (2), dried, washed with water, and dried to obtain an antibacterial textile fabric for babies. The thickness of the antibacterial finishing layer is 0.2mm.

Embodiment 2

[0034] (1) The flat ribbon-shaped multifilament helix fiber composed of 8 monofilaments of 4μm is used as the weft and the cotton fiber of 15tex is used as the warp, which is extracted by physical method. The dosage ratio of the helix fiber and the cotton fiber is 1:2.7. Using double-layer plain weave as the organizational structure, weaving to form a fiber layer of 204g / ㎡.

[0035] (2) In parts by weight, dissolve 35 parts of hydrolyzed chitosan with a molecular weight of 5000 in water, add 30 parts of tea extract and honeysuckle extract, stir evenly, and finally add 55 parts of sodium alginate, When the sodium alginate is dissolved, a transparent and uniform antibacterial viscous liquid is formed.

[0036] (3) After tentering and finishing the fiber layer prepared in step (1), the surface of the fiber layer is coated with the antibacterial viscous liquid prepared in step (2), dried, washed with water, and dried to obtain an antibacterial textile fabric for babies. The thickness ...

Embodiment 3

[0038] (1) The flat ribbon multifilament helix fiber composed of 5 3.2μm monofilaments extracted by physical method is used as the weft, and the cotton fiber of 14tex is used as the warp. The dosage ratio of the lotus fiber to the cotton fiber is 1:1.8 , Using double-layer plain weave as the organizational structure, weaving to form a fiber layer of 193g / ㎡.

[0039] (2) In parts by weight, dissolve 25 parts of hydrolyzed chitosan with a molecular weight of 3000 in water, add 20 parts of honeysuckle extract, stir evenly, and finally add 40 parts of sodium alginate. Dissolve to form a transparent and uniform antibacterial viscous liquid.

[0040] (3) After tentering and finishing the fiber layer prepared in step (1), the surface of the fiber layer is coated with the antibacterial viscous liquid prepared in step (2), dried, washed with water, and dried to obtain an antibacterial textile fabric for babies. The thickness of the antibacterial finishing layer is 0.25 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Finenessaaaaaaaaaa
Square meter weightaaaaaaaaaa
Login to View More

Abstract

The invention provides novel antibacterial textile fabric special for infants and a preparing method thereof. The method comprises the specific operation steps that 1, lotus fibers extracted through a physical method serve as weft, cotton fibers serve as warp, double-layer plain weave is adopted as a weave structure, and weaving is carried out so that a fiber layer can be formed; 2, hydrolyzed chitosan is dissolved into water, a plant antibacterial extracting solution is added, the mixture is stirred uniformly, finally sodium alginate is added, and after sodium alginate is dissolved, transparent and uniform antibacterial viscous fluid is formed; 3, after the fiber layer prepared in the step 1 is tentered and finished, the surface of the fiber layer is coated with the antibacterial viscous fluid prepared in the step 2, and baking, washing and drying are carried out to obtain the antibacterial textile fabric special for the infants. The antibacterial property is still excellent after the prepared antibacterial textile fabric special for the infants is washed with water for 100 times, the textile fabric has excellent wet absorbing and ventilating properties, is soft and comfortable in handfeel and environmentally friendly, meets the requirement of clothes of the newborn infants and is antibacterial textile fabric special for the infants, and safety is guaranteed.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, and specifically relates to a new type of antibacterial textile fabric for babies and a preparation method thereof. Background technique: [0002] Baby textiles are specially developed for newborn babies and suitable for their special physiological characteristics. With the advancement of science and technology and people's awareness of their own health protection, infant textiles have developed from the original 100% pure cotton to functional performance, subdivision, serialization, and green production process. [0003] Antibacterial textiles are mainly obtained through two ways, one is to modify fiber raw materials to make the fiber raw materials have antibacterial properties, and the other is to perform antibacterial post-finishing processing on textiles. The first method is mainly to mix the antibacterial agent into the spinning dope to prepare antibacterial fibers, or to blend the anti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/13D06M15/03D06M11/00D06M13/00D03D15/00D06M101/06
Inventor 董荣琴
Owner 安徽京威纺织服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com