A UV cut-off antifouling coating composition, hardened film and preparation method

A composition and coating technology, applied in the direction of antifouling/underwater coatings, coatings, polyester coatings, etc., to achieve the effects of hydrophobic and oleophobic antifouling performance, scratch resistance, and excellent scratch resistance

Active Publication Date: 2017-11-21
NINGBO SOKEN CHEM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the wide application of hardened film, its performance requirements are getting higher and higher, and the single-performance hardened film can no longer meet the needs of the market. A hardened film with anti-fingerprint pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A UV cut-off antifouling coating composition, hardened film and preparation method
  • A UV cut-off antifouling coating composition, hardened film and preparation method
  • A UV cut-off antifouling coating composition, hardened film and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The components and parts by weight of the UV cut-off antifouling coating composition in the present embodiment are:

[0026]

[0027] Under the condition of avoiding sunlight or ultraviolet light irradiation, relative air humidity less than 60%, to 40 parts of polyester acrylate prepolymer CN2254NS (manufactured by American Sartomer, functionality 2) and 12 parts of dipentaerythritol hexaacrylate DPHA ( Made by Ningbo Jinteng Chemical Co., Ltd., functionality 6) add 1.0 part of modified perfluoropolyether DAC-HP (manufactured by Daikin Corporation of Japan, solid content is 20%), 0.3 part of leveling agent 401LS (manufactured by Dow Corning Company), 50 parts of methyl isobutyl ketone, after fully stirring, add 5 parts of UV absorber OC-T20K (manufactured by Nissan Chemical, with a solid content of 20%) after continuing to stir, add 7 parts of 184 photoinitiators (manufactured by BASF) and stir evenly , and remove impurities with a 1um filter to obtain a photohardeni...

Embodiment 2

[0030] The components and parts by weight of the UV cut-off antifouling coating composition in the present embodiment are:

[0031]

[0032] Under the condition of avoiding sunlight or ultraviolet light irradiation, relative air humidity less than 60%, to 40 parts of polyester acrylate prepolymer CN2254NS (manufactured by American Sartomer, functionality 2) and 12 parts of dipentaerythritol hexaacrylate DPHA ( Manufactured by Ningbo Jinteng Chemical Co., Ltd., functionality 6) Add 1.0 part of modified perfluoropolyether DAC-HP (manufactured by Daikin Corporation of Japan, solid content is 20%), 0.2 part of leveling agent 401LS (manufactured by Dow Corning Company), 50 parts of methyl isobutyl ketone, stir well and then add 2 parts of UV absorber OC-T20K (manufactured by Nissan Chemical, solid content is 20%) After continuing to stir, add 7 parts of 184 photoinitiators (manufactured by BASF) and stir evenly , and remove impurities with a 1um filter to obtain a UV cut-off ant...

Embodiment 3

[0035] The components and parts by weight of the UV cut-off antifouling coating composition in the present embodiment are:

[0036]

[0037] Under the condition that avoids sunlight or ultraviolet light irradiation, air relative humidity is less than 60%, to 25 parts of aliphatic urethane acrylate prepolymers CN9006NS (manufactured by U.S. Sartomer, functionality 6) and 20 parts of pentaerythritol triacrylate PETA ( Manufactured by Ningbo Jinteng Chemical Co., Ltd., functionality 3) Add 2 parts of modified perfluoropolyether DAC-HP (manufactured by Daikin Corporation of Japan, solid content is 20%), 0.3 part of leveling agent 401LS (manufactured by Dow Corning Company), 50 parts of methyl isobutyl ketone, stir well and then add 4 parts of UV absorber OC-T20K (manufactured by Nissan Chemical, solid content is 20%) After continuing to stir, add 3 parts of 184 photoinitiator (manufactured by BASF) and stir evenly , and remove impurities with a 1um filter to obtain a UV cut-off...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a UV blocking and antifouling coating composition, a hardened film and a preparation method, wherein the components and parts by weight of the coating composition are: 20-40 parts of multifunctional acrylate prepolymer, UV active single 10-35 parts of body, 2-8 parts of photoinitiator, 0.1-0.5 parts of leveling agent, 2-6 parts of ultraviolet absorber, 0.5-2 parts of fluorine-containing antifouling agent, 0-50 parts of organic solvent. The UV cut-off antifouling coating composition is coated on the substrate and heated at 60-100°C for 30-100 seconds, and then the coating layer is irradiated with UV by a high-pressure mercury lamp. The irradiation intensity is 150-300w / cm, and the energy is 200-400mj / cm2, the UV cut-off anti-fouling hardened film can be obtained. In the present invention, a fluorine-containing antifouling agent and an ultraviolet absorber are added to the coating composition, so that the cured film made of the coating composition not only has high hardness and optical properties possessed by conventional cured films, but also has UV barrier High performance, hydrophobic and oleophobic antifouling performance and excellent scratch resistance can be widely used in the fields of display screens, glass exterior walls and injection molding, etc., to block ultraviolet rays, antifouling, easy to clean and anti-scratch effects.

Description

technical field [0001] The invention relates to the field of hardened films, in particular to a UV blocking and antifouling coating composition, a hardened film and a preparation method. Background technique [0002] With the rapid development of smart phones, personal tablet computers, LCD TVs, digital cameras and other products, touch screen technology has been widely used. Touch screens are generally composed of transparent composite film layers, glass or plexiglass layers, and outer plastic layers. On the one hand, hardened films are widely used as an important optical substrate to make ITO conductive films, explosion-proof films, etc. It is used for full bonding or frame bonding of optical devices inside the touch screen. On the other hand, on the outside of the touch screen, with the country's mandatory requirements for the safety of large-size glass during transportation and use, hardened films are widely used for explosion-proof and splash-proof protection of variou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/06C09D175/14C09D5/16C08J7/04
Inventor 柳彬彬王旭辉余欣蔚
Owner NINGBO SOKEN CHEM