Method of controlling n content in gcr15 bearing steel

A bearing steel, content technology, applied in the field of controlling N content in GCr15 bearing steel, can solve the problems such as technological measures without N content, and achieve the effects of improving cost performance and market competitiveness, reducing costs, saving energy and protecting the environment

Active Publication Date: 2018-06-19
武汉钢铁有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent "a production method of high-clean high-carbon chromium bearing steel" (patent number: ZL200410025102.5) adopts a five-step process: ① select ingredients; ②) ≥ 30 tons of electric furnace primary molten steel; ③ ladle furnace refining Molten steel: argon blowing intensity 0.4MPa in the early stage, 0.3MPa in the later stage; material addition ≤ 8Kg / ton of steel; two-step aluminum feeding method precipitation deoxidation; add crystalline silicon powder and fluorite (containing calcium fluoride ≥ 98%) to the slag surface ④ Vacuum furnace treatment: vacuum degree ≤ 140Pa, 25min + bottom blowing argon and weak stirring for 15min; ⑤ Liquid steel mold casting under inert atmosphere, this patent is a conventional bearing steel production process, and does not specifically aim at reducing N in GCr15 steel Process measures of content

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of controlling n content in gcr15 bearing steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Converter smelting and tapping volume is about 150t, continuous casting slab section size: 200×200mm;

[0039] Sampling analysis composition before converter tapping: [C]: 0.61%, [P]: 0.013%, [S]: 0.029%, [N]: 0.0032%;

[0040] Temperature measurement before tapping: 1600°C;

[0041] The amount of LF slag in ladle refining is about 1.8t. After heating and arcing, 60Kg of carbon powder is spread on the refining slag with a spade (weight ratio: 3.3%) to form foam slag, and the thickness of the slag is about 450mm; : 1557°C; sampling analysis: [N]: 0.0052%;

[0042] The molten steel is vacuum treated in the RH furnace, the vacuum degree of the system is kept below 67Pa for 12 minutes, and the entire vacuum treatment time is 21 minutes; the soft Ar blowing time: 20 minutes, the Ar gas pressure: 0.26MPa, the flow rate: 125NL / min; sampling analysis: [N]: 0.0036%;

[0043] The long nozzle joint of the continuous casting ladle is sealed by spiral blowing Ar, and the Ar gas pre...

Embodiment 2

[0046] The electric furnace smelting and tapping volume are about 70t, and the cross-sectional size of the continuous casting slab is: 150×150mm;

[0047] Sampling analysis composition before electric furnace tapping: [C]: 0.70%, [P]: 0.007%, [S]: 0.021%, [N]: 0.0054%; temperature measurement before tapping: 1560℃;

[0048] The amount of LF slag in ladle refining is about 1.1t. After heating and arcing, 50Kg of carbon powder is spread on the refining slag with a spade (weight ratio: 4.5%) to form foam slag. The slag thickness is about 390mm; : 1545°C; sampling analysis: [N]: 0.0061%;

[0049] The molten steel is vacuum treated in the RH furnace, the vacuum degree of the system is kept below 67Pa for 20 minutes, and the entire vacuum treatment time is 25 minutes; the time of soft Ar blowing: 30 minutes, Ar gas pressure: 0.20MPa, flow rate: 100NL / min; sampling analysis: [N]: 0.0044%;

[0050] The long nozzle joint of the continuous casting ladle is sealed by spiral blowing Ar,...

Embodiment 3

[0053] Converter smelting and tapping volume is about 250t, continuous casting slab section size: 340×450mm;

[0054] Sampling analysis composition before tapping of converter: [C]: 0.40%, [P]: 0.016%, [S]: 0.024%, [N]: 0.0030%; temperature measurement before tapping: 1610℃;

[0055] The amount of LF slag in ladle refining is about 3.6t. After heating and arcing, spread 216Kg of carbon powder on the refining slag with a spade (weight ratio: 6.0%) to create foam slag with a thickness of about 500mm. Heating molten steel for 15 minutes, the temperature of molten steel : 1562°C; sampling analysis: [N]: 0.0052%;

[0056] The molten steel is vacuum treated in the RH furnace, the vacuum degree of the system is kept below 67Pa for 14 minutes, and the entire vacuum treatment time is 25 minutes; the time of soft Ar blowing: 25 minutes, Ar gas pressure: 0.28MPa, flow rate: 200NL / min; sampling analysis: [N]: 0.0041%;

[0057] The long nozzle joint of the continuous casting ladle is sea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for controlling the N content in GCr15 bearing steel. It adopts the new technology of "high-carbon and low-temperature tapping" in the key link of tapping, and uses a spade to evenly spread carbon powder into the LF furnace during refining to create foamy slag. , the electrode is submerged arc heated, and vacuum treatment and continuous casting are used to protect the casting. The present invention prevents and controls N absorption in each process of GCr15 bearing steel smelting. At the same time, it is simple to operate, saves energy, protects the environment, reduces costs, and improves the product quality. The cost performance and market competitiveness can finally control the N content in GCr15 bearing steel to [N]≤0.0050%.

Description

technical field [0001] The invention relates to the technical field of N content control in bearing steel in the steelmaking production process, and specifically refers to a method for controlling the N content in GCr15 bearing steel. Background technique [0002] The GB / T 18254-2002 standard stipulates that high-carbon chromium bearing steels include: GCr4, GCr15, GCr15SiMn, GCr15SiMo, GCr18Mo and other five steel grades, and the carbon content in the steel [C]: 0.95-1.05%, of which GCr15 is the representative steel It is mainly used to manufacture bearing rolling elements, inner and outer rings. The working conditions of bearings are extremely complicated, and they are subjected to various high alternating stresses, such as tension, pressure, shear and friction. Therefore, the bearing steel The material also puts forward very strict quality requirements. In order to ensure that the bearing steel has high fatigue strength, compressive strength, surface hardness and long ser...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/10C21C7/04C21C7/072
Inventor 陈庆丰陈佳杜方许竹桃李献忠张贤忠陈华强张渊普
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com