Chemical fiber blended yarn

A technology of blended yarn and chemical fiber, which is applied in biochemical fiber treatment, fiber treatment, flame-retardant fiber, etc. It can solve the problems of not meeting customer requirements and single performance of chemical fiber blended yarn, and achieve excellent anti-mildew effect

Inactive Publication Date: 2016-03-09
常熟市明达腈纺有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The performance of the existing chemical fiber blended

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of chemical fiber blended yarn, it is through padding treatment, and this padding treatment comprises the steps:

[0021] 1) Add 1-2 parts by weight of sucrose fatty acid ester, 1.1 parts by weight of hydroxyethyl cellulose, 0.7 parts by weight of sodium diacetate, and 0.3 parts by weight of carnauba wax into 14.2 parts by weight of deionized water, and stir evenly;

[0022] 2) At the same time, slowly add 0.7 parts by weight of zinc borate, 1.2 parts by weight of bamboo acetic acid, 0.5 parts by weight of sodium persulfate, and 1.1 parts by weight of octadecyldimethylhydroxyethyl quaternary ammonium nitrate, and continue stirring until fully mixed and uniform , to prepare the finishing solution;

[0023] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 2

[0025] Chemical fiber blended yarn, which has been subjected to padding treatment, and the padding treatment includes the following steps:

[0026] 1) Put 1 part by weight of sucrose fatty acid ester, 1.1 part by weight of hydroxyethyl cellulose, 0.7 part by weight of sodium diacetate, and 0.3 part by weight of carnauba wax into 14.2 parts by weight of deionized water, and stir evenly;

[0027] 2) At the same time, slowly add 0.7 parts by weight of zinc borate, 1.2 parts by weight of bamboo acetic acid, 0.5 parts by weight of sodium persulfate, and 1.1 parts by weight of octadecyldimethylhydroxyethyl quaternary ammonium nitrate, and continue stirring until fully mixed and uniform , to prepare the finishing liquid;

[0028] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 3

[0030] Chemical fiber blended yarn, which has been subjected to padding treatment, and the padding treatment includes the following steps:

[0031] 1) Put 2 parts by weight of sucrose fatty acid ester, 1.1 parts by weight of hydroxyethyl cellulose, 0.7 parts by weight of sodium diacetate, and 0.3 parts by weight of carnauba wax into 14.2 parts by weight of deionized water, and stir evenly;

[0032] 2) At the same time, slowly add 0.7 parts by weight of zinc borate, 1.2 parts by weight of bamboo acetic acid, 0.5 parts by weight of sodium persulfate, and 1.1 parts by weight of octadecyldimethylhydroxyethyl quaternary ammonium nitrate, and continue stirring until fully mixed and uniform , to prepare the finishing liquid;

[0033] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses chemical fiber blended yarn. The chemical fiber blended yarn is treated in a padding mode, and the padding treatment includes the following steps that firstly, by weight, 1-2 parts of sucrose fatty acid ester, 1.1 parts of hydroxyethyl cellulose, 0.7 part of sodium diacetate and 0.3 part of carnauba wax are thrown into 14.2 parts of deionized water, and the mixture is stirred uniformly; secondly, by weight, 0.7 part of zinc borate, 1.2 parts of bamboo vinegar, 0.5 part of sodium persulfate and 1.1 parts of octadecyl dimethyl ethoxyl ammonium nitrate are added slowly at the same time, and the mixture continues to be stirred to be fully and uniformly mixed to prepare finishing liquid; thirdly, blended yarn is treated in the padding mode in the finishing liquid, taken out and then dried at the constant temperature. The chemical fiber blended yarn has excellent mould-proof, mothproof, antibacterial, flame-retardant and anti-static performance.

Description

technical field [0001] The present invention relates to chemical fiber blended yarn. Background technique [0002] The performance of the existing chemical fiber blended yarn is single, which cannot meet the requirements of customers. Contents of the invention [0003] The purpose of the present invention is to provide a kind of chemical fiber blended yarn, which has excellent mildewproof, mothproof, antibacterial, flame retardant and antistatic properties. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of chemical fiber blended yarn, which is processed through padding, and the padding process includes the following steps: [0005] 1) Add 1-2 parts by weight of sucrose fatty acid ester, 1.1 parts by weight of hydroxyethyl cellulose, 0.7 parts by weight of sodium diacetate, and 0.3 parts by weight of carnauba wax into 14.2 parts by weight of deionized water, and stir evenly; [0006] 2) At the same time, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/224D06M15/09D06M13/188D06M13/02D06M11/82D06M11/50D06M13/463
CPCD06M13/224D06M11/50D06M11/82D06M13/02D06M13/188D06M13/463D06M15/09D06M16/00D06M2200/30
Inventor 缪栋华
Owner 常熟市明达腈纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap