After-finish process of Shu velveteen fabric

A technology of lint-releasing and finishing, which is applied in the field of finishing technology of velveteen fabrics, which can solve the problems of not being soft enough, and achieve the effect of soft hand feeling and excellent anti-mildew effect

Inactive Publication Date: 2016-12-14
常熟市金润针纺织有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The anti-mildew, anti-moth, anti-bacterial, flame-retardant, anti-static, washable, anti-shrinkage, anti-wrinkle, and wear-resistant properties of existing fabrics need to be improved, and the hand feel is not soft enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The post-finishing process of Shu cotton velvet fabric comprises the following steps:

[0026] 1) 1 to 2 parts by weight of nano-titanium dioxide, 0.9 parts by weight of tetraalkylmethyldiethylhydroxyl ammonium bromide, 1.5 parts by weight of sodium lauryl sulfate, 0.7 parts by weight of almond oil amidopropylamine oxide, 2.6 parts by weight Weight part polyethylene glycol distearate drops into 55 weight parts deionized water successively, stirs;

[0027] 2) drop into 4.6 parts by weight of polypropylene glycol, 1.9 parts by weight of polyalkoxy carboxylate, 0.3 parts by weight of sodium hypophosphite, 1.6 parts by weight of dimethylformamide, 2.3 parts by weight of sodium tripolyphosphate, and continue to stir. Until fully mixed evenly, the finishing solution is obtained;

[0028] 3) Then pad the fabric in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 2

[0030] The post-finishing process of Shu cotton velvet fabric comprises the following steps:

[0031] 1) With 1 weight part of nano-titanium dioxide, 0.9 weight part of tetraalkyl-methyl diethylhydroxyl ammonium bromide, 1.5 weight part of sodium lauryl sulfate, 0.7 weight part of almond oleamide propylamine oxide, 2.6 weight part Polyethylene glycol distearate drops into 55 parts by weight of deionized water successively, stirs;

[0032] 2) drop into 4.6 parts by weight of polypropylene glycol, 1.9 parts by weight of polyalkoxy carboxylate, 0.3 parts by weight of sodium hypophosphite, 1.6 parts by weight of dimethylformamide, 2.3 parts by weight of sodium tripolyphosphate, and continue to stir. Until fully mixed evenly, the finishing solution is obtained;

[0033] 3) Then pad the fabric in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 3

[0035] The post-finishing process of Shu cotton velvet fabric comprises the following steps:

[0036] 1) 2 parts by weight of nano-titanium dioxide, 0.9 parts by weight of tetraalkyl-methyl diethylhydroxyl ammonium bromide, 1.5 parts by weight of sodium lauryl sulfate, 0.7 parts by weight of almond oleamide propylamine oxide, 2.6 parts by weight of Polyethylene glycol distearate drops into 55 parts by weight of deionized water successively, stirs;

[0037] 2) drop into 4.6 parts by weight of polypropylene glycol, 1.9 parts by weight of polyalkoxy carboxylate, 0.3 parts by weight of sodium hypophosphite, 1.6 parts by weight of dimethylformamide, 2.3 parts by weight of sodium tripolyphosphate, and continue to stir. Until fully mixed evenly, the finishing solution is obtained;

[0038] 3) Then pad the fabric in the finishing solution, take it out and dry it at a constant temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an after-finish process of Shu velveteen fabric. The after-finish process includes following steps: 1), sequentially putting, by weight, 1-2 parts of nano titanium dioxide, 0.9 part of tetraalkyl methyl diethylhydroxy ammonium bromide, 1.5 parts of lauryl sodium sulfate, 0.7 part of almond oil amide propyl amine oxide and 2.6 parts of polyethylene glycol distearate into 55 parts of deionized water, and well stirring; 2), sequentially putting 4.6 parts of polypropylene glycol, 1.9 parts of polyalkoxy carboxylate, 0.3 part of sodium hypophosphite, 1.6 parts of dimethyl formamide and 2.3 parts of sodium tripolyphosphate, and continuing stirring until mixing is fully performed to obtain finishing liquid; 3), padding fabric in the finishing liquid, taking out the fabric, and drying the fabric at constant temperature. The fabric after being finished by the process is good in performance and soft in hand feel.

Description

technical field [0001] The invention relates to a post-finishing process for cotton wool fabrics. Background technique [0002] The anti-mildew, anti-moth, anti-bacterial, flame-retardant, anti-static, washable, shrink-proof, anti-wrinkle, and wear-resistant properties of the existing fabrics need to be improved, and the hand feeling is not soft enough. Contents of the invention [0003] The object of the present invention is to provide a post-finishing process for cotton velvet fabrics, the finished fabrics have excellent mildew-proof, moth-proof, anti-bacterial, flame-retardant, anti-static, washable, shrink-proof, wrinkle-resistant and wear-resistant properties , and soft to the touch. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of post-finishing process of comfortable cotton velvet fabric, comprising the steps: [0005] 1) 1 to 2 parts by weight of nano-titanium dioxide, 0.9 parts by weight of tet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/53D06M11/46D06M13/463D06M13/262D06M13/402D06M11/70D06M11/72D06M101/06
CPCD06M11/46D06M11/70D06M11/72D06M13/262D06M13/402D06M13/463D06M15/53D06M2101/06
Inventor 张金龙
Owner 常熟市金润针纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com