Biocompatible hemostatic product and preparation method thereof

A biocompatibility and product technology, applied in the field of biocompatible hemostatic products and their preparation, can solve problems such as inconvenience and achieve the effect of preventing irritation

Active Publication Date: 2016-03-23
ENDOCLOT PLUS SUZHOU
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of hemostatic glue is only convenient to use on wounds on the body surface, but this type of hemostatic glue cannot be conveniently applied to bleeding wounds in the internal cavity of the human body (for example, the surface of the lining of the digestive tract)
[0013] There is no report of applying PEO powder particles directly to wounds or other affected areas to stop bleeding or seal wounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biocompatible hemostatic product and preparation method thereof
  • Biocompatible hemostatic product and preparation method thereof
  • Biocompatible hemostatic product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Example 1. Biocompatible Hemostatic Articles of PEO Particles

[0055] This example provides a series of biocompatible hemostatic products #1 to #4 containing polyethylene oxide (PEO) particles with different viscosity-average molecular weights, the physicochemical parameters of the PEO particles contained in these biocompatible hemostatic products and the The particle sizes of the biocompatible hemostatic articles are listed in Table 1 below:

[0056] Table 1

[0057]

[0058] The above-mentioned biocompatible hemostatic products #1 to #4 are prepared through the following steps:

[0059] (a) Polyoxyethylene particles with different viscosity-average molecular weights as raw materials are placed in the granulator,

[0060] (b) adding distilled water to the raw material placed in the granulator of step (a);

[0061] (c) Granulating at 40° C. to 50° C., followed by sieving to obtain a biocompatible hemostatic product with a particle size of 50 μm to 250 μm.

[0...

Embodiment 2

[0068] Example 2. Biocompatible hemostatic articles of PEO particles and carboxymethyl starch (CMS)

[0069] This example provides a series of biocompatible hemostatic products #5 to #8 comprising polyoxyethylene (PEO) particles and carboxymethyl starch (CMS) particles in different mass ratios, wherein the viscosity-average molecular weight of the PEO particles is 2,000,000 D. The particle size is 0.5 μm to 2000 μm, and the water absorption rate is 5 to 15; the viscosity average molecular weight of CMS particles is 3,000D to 200,000D, the particle size is 0.5 μm to 1000 μm, and the water absorption rate is 10 to 30. In this embodiment The mass ratio of PEO particles and CMS particles in biocompatible hemostatic products #5 to #8 is listed in Table 2 below, and the control sample used in this embodiment is Arista TM Hemostatic powder (produced by Medafor Inc., USA); molecular weight: 5,000D to 200,000D; particle size: 10 μm to 350 μm, average particle size: 100 μm, water abso...

Embodiment 3

[0079] Example 3. Biocompatible Hemostatic Articles of PEO Particles and Povidone (PVP) Particles

[0080] This example provides a series of biocompatible hemostatic products #9 to #11 comprising polyoxyethylene (PEO) particles and povidone (PVP) particles in different mass ratios, wherein the viscosity-average molecular weight of the PEO particles is 2,000,000D , the particle size is 0.5 μm to 2000 μm, and the water absorption rate is 5 to 15; the viscosity-average molecular weight of PVP particles is 90,000D, the particle size is 0.5 μm to 1000 μm, and the water absorption rate is 5 to 15. The biocompatibility in this embodiment The mass ratios of PEO particles and PVP particles in hemostatic articles #9 to #11 are listed in Table 3 below:

[0081] table 3

[0082] Sample serial number

Mass ratio of PEO particles to PVP particles

#9

6:1

#10

3:1

#11

1:3

[0083] The above-mentioned biocompatible hemostatic products #9 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a biocompatible hemostatic product and a tissue sealing agent. The biocompatible hemostatic product contains polyoxyethylene particles, the viscosity-average molecular weight of polyoxyethylene ranges from 100,000 daltons to 7,000,000 daltons, the particle size of the polyoxyethylene particles ranges from 0.5 micrometer to 2000 micrometers, and the water absorbency of the polyoxyethylene particles is 1-500, wherein the hemostatic product can form gel capable of sealing a blood wound after absorbing water, and the tissue sealing agent can form gel capable of sealing a wound where tissue fluid oozes after being applied to the wound where the tissue fluid oozes. The invention further provides methods for preparing the biocompatible hemostatic product and the tissue sealing agent and application of the biocompatible hemostatic product and the tissue sealing agent in hemostasis, adhesion prevention, infection prevention, tissue healing promotion and / or wound seal on the blood wounds of the animal body surfaces, the tissue organs and tissue or organs in the body cavity.

Description

technical field [0001] The present invention relates to a biocompatible hemostatic product, a tissue sealant and a preparation method thereof. Specifically, the present invention relates to a biocompatible hemostatic product that can be directly applied to human and For damaged wounds of tissues and organs of other mammals, it is a biocompatible hemostatic product and tissue sealant with high water absorption for the purpose of stopping bleeding, sealing wounds, reducing tissue exudation, promoting tissue repair, protecting wound tissue, and preventing infection and its preparation method. Background technique [0002] Surgical operations and trauma usually cause wound bleeding, resulting in a large amount of blood loss, and it is necessary to take timely measures to stop the bleeding. Moreover, the surgeon needs to seal the wound caused by certain reasons according to the operation situation, to prevent further bleeding, and to protect the wound from infection at the same ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L15/26A61L15/60A61L15/44
CPCA61L15/26A61L15/44A61L2400/04A61L15/46A61L24/0015A61L24/0026A61L24/043A61L24/046A61L26/0076A61P17/02A61L26/0019A61L26/0066A61L2300/418C08L71/02A61L26/0052A61L26/0023A61L26/0014A61L26/009A61L2300/802A61L2300/406A61L2300/41A61K9/14A61L26/0061A61L2300/60
Inventor 纪欣邢程张恒周颖
Owner ENDOCLOT PLUS SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More