A kind of preparation method of platinum-rhenium reforming catalyst and platinum-rhenium reforming catalyst

A technology for reforming catalysts and catalysts, applied in chemical instruments and methods, physical/chemical process catalysts, naphtha catalytic reforming, etc., which can solve problems such as catalyst poisons, extended start-up time, corrosion of reaction equipment, etc., and achieve production process The effect of simplicity, saving start-up time, and low preparation cost

Active Publication Date: 2017-09-22
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, Mao Xuejun et al. (Acta Petroleum Sinica (Petroleum Processing), 2000, Vol. 16, No. 2, P25-32) found that the formation of sulfate radicals on the platinum-rhenium reforming catalyst not only inhibited the acidic and metallic functions of the catalyst, but also accelerated the The inactivation rate of the aromatization activity and selectivity is greatly reduced
[0007] As can be seen from the above, there are following problems in the presulfidation method of reforming catalyst: (1) whether the sulfidation agent added in the sulfide process is H 2 Both S and organic sulfides are likely to cause corrosion of reaction equipment, causing equipment damage and potential safety hazards; (2) special pre-sulfurization equipment needs to be set up on industrial reforming units; Pollution to the environment; (4) higher cost of vulcanizing agent; (5) extended start-up time
For the sulfate radical in the reforming catalyst, it is generally believed that it will damage the performance of the catalyst and is a poison to the catalyst.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of platinum-rhenium reforming catalyst and platinum-rhenium reforming catalyst
  • A kind of preparation method of platinum-rhenium reforming catalyst and platinum-rhenium reforming catalyst
  • A kind of preparation method of platinum-rhenium reforming catalyst and platinum-rhenium reforming catalyst

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The present invention provides a method for preparing a platinum rhenium reforming catalyst. The method includes the following steps:

[0023] (1) The alumina carrier is contacted with the first active component solution, filtered and dried to obtain a dry sample;

[0024] (2) Contacting a sodium alkylxanthate solution with a pH of 7.5-9 with the dried sample, and after filtering, drying and roasting, a catalyst intermediate is obtained;

[0025] (3) Contacting the catalyst intermediate with the second active component solution, and then drying and roasting;

[0026] Wherein, the first active component solution contains a platinum-containing compound and a rhenium-containing compound, and the second active component solution contains a platinum-containing compound, a rhenium-containing compound, and hydrochloric acid;

[0027] The structure of the sodium alkyl xanthate is shown in formula I,

[0028]

[0029] In formula I, R is C 2 -C 4 The straight or branched chain alkyl group. ...

Embodiment approach

[0040] The present invention does not specifically limit the amount of platinum-containing compound and rhenium-containing compound in the first active component solution, as long as the active components, namely, the metal components platinum and rhenium can be introduced into the alumina The carrier is fine. According to an embodiment of the present invention, the amount of the platinum-containing compound in the first active component solution is such that the platinum content can be 0.01-1% by weight, preferably 0.05-0.3% by weight, based on the element; the rhenium-containing compound The amount used is such that the content of rhenium can be 0.05-1% by weight, preferably 0.1-0.7% by weight, based on the element.

[0041] In step (1), the drying conditions can be appropriately selected according to the type of solvent in the solution. For example, the drying temperature can be 95-105°C, and the time can be 2-4 hours.

[0042] In the present invention, the structure of the so...

preparation example 1-4

[0068] Preparation examples 1 to 4 are used to illustrate the first active component solution, sodium alkyl sulfonate solution, and second active component solution of the present invention, that is, the preparation methods of various immersion solutions.

[0069] The first active component solution: add chloroplatinic acid and perrhenic acid to 50 g of ion-free water to dissolve, and prepare an impregnating solution containing platinum and rhenium.

[0070] Sodium alkyl xanthate solution: Add sodium alkyl xanthate to 50 g of non-ionized water to dissolve it, prepare a solution with a certain concentration, and adjust the pH with 23% by weight ammonia water.

[0071] Second active component solution: adding chloroplatinic acid, perrhenic acid, and hydrochloric acid (with a concentration of 36.5% by weight) to 50 g of non-ionized water to dissolve, and prepare an impregnating solution containing elemental platinum, rhenium and chlorine.

[0072] The content of the main components in the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a platinum-rhenium reforming catalyst and the platinum-rhenium reforming catalyst. The method comprises: (1) contacting an alumina carrier with an active component solution containing a platinum compound and a rhenium compound, filtering, After drying, a dry sample is obtained; (2) the sodium alkyl xanthate solution with a pH of 7.5-9 is contacted with the dry sample, and after filtering, drying and roasting, a catalyst intermediate is obtained; (3) the catalyst The intermediate is contacted with a component solution containing a platinum-containing compound, a rhenium-containing compound and hydrochloric acid, and then dried and calcined. The method of the invention integrates the vulcanization process of the catalyst, avoids the catalyst from corroding equipment before use, and has a simple catalyst production process. In addition, the platinum-rhenium reforming catalyst prepared by the method of the present invention does not require a pre-sulfurization process of the catalyst before use, and has better catalytic performance than the sulfate-sulfurized catalyst.

Description

Technical field [0001] The invention relates to a method for preparing a platinum-rhenium reforming catalyst, and a platinum-rhenium reforming catalyst prepared by the preparation method. Background technique [0002] Catalytic reforming is an important process for the production of high-octane gasoline components and aromatics. At the same time, the by-product cheap hydrogen is used for oil hydrorefining, upgrading and cracking. In recent years, as the society’s demand for reformed products continues to rise, the world’s production capacity of catalytic reformers has increased year by year, among which semi-regenerative reformers occupy a very important position. The semi-regenerative reforming catalyst uses platinum rhenium catalyst, which is characterized by good stability and stable operation for a long period of time. [0003] The semi-regenerative reforming catalyst has developed from a single platinum catalyst to a platinum rhenium catalyst, which significantly improves the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/045C10G35/09
Inventor 何烨祁兴维任靖杨若晨张勇肖太顺李顺新李梁善姜艳
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products