Wood preservative

A technology of wood preservative and nano-copper oxide, which is applied in the field of wood preservatives and new wood preservatives, can solve the problems of backward preparation level and efficacy, high preparation cost, unfavorable environmental protection, etc., and achieve reasonable composition configuration and simple preparation process , the effect of good performance

Inactive Publication Date: 2016-03-30
常熟市石林木材有限责任公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the wood preservatives used in the world are mainly CCA preservatives. Because this kind of wood preservatives contain toxic substances such as arsenic and chromium, which are not conducive to environmental protection, and the preparation cost is high, their use has been strictly restri

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] The preferred embodiments of the present invention are described in detail below, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0011] Among the wood preservatives mentioned in the present invention, the main components of the wood preservative and their percentage ratios are: 8%-12% of nano-copper oxide particles, 4%-6% of sodium metabisulfite, 2%- 4%, polyethylene glycol 5%-8%, copper naphthenate 1%-3%, acetic acid 2%-5%, and the rest is deionized water.

[0012] To further illustrate, the main components of the wood preservative and their percentage ratios are: nano-copper oxide particles 10%-12%, sodium metabisulfite 4%-5%, tebuconazole 2%-3%, polyethylene glycol 6%-7%, copper naphthenate 1.5%-2.5%, acetic acid 2%-4%, and the rest is deionized water; among them, the average particle diameter of nano-copper oxide part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a wood preservative. The wood preservative comprises the following main ingredients in percentage by weight: 8-12% of nanometre copper oxide particles, 4-6% of sodium metabisulfite, 2-4% of tebuconazole, 5-8% of polyethylene glycol, 1-3% of copper naphthenate, 2-5% of acetic acid, and the balance deionized water. The invention discloses a wood preservative. The wood preservative is reasonable in ingredient configuration, simple and convenient in preparation process, and moderate in cost; the prepared preservative has good use performance, has no toxic by-products generated during preparation and use processes, meets the environmental protection concept, and can be widely applied to various natural wood, fibre board and shaving board products, and machined parts.

Description

technical field [0001] The invention relates to a wood preservative, in particular to a novel wood preservative with high efficiency, environmental protection and low cost, which belongs to the technical field of wood products. Background technique [0002] Wood is a natural biological material, which is widely used in industrial and civil construction, furniture, decoration and other fields, and it is closely related to people's life. Wood products have obvious biological characteristics, so they are very vulnerable to bacteria, insects and microorganisms, causing discoloration, decay and moth-eaten phenomena, which seriously affect the performance and service life of wood products, increase the consumption of wood, and not only waste resources , It also limits the application field of wood, thus bringing huge economic losses. Therefore, for wood preservation, in addition to strengthening the sanitation management from raw materials to product processing, targeted preserva...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K3/52
CPCB27K3/52
Inventor 石林保
Owner 常熟市石林木材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap