A kind of preparation method of composite polypropylene dielectric film electrode for film capacitor

A technology of composite polypropylene and film capacitors, used in fixed capacitor electrodes, capacitor manufacturing, fixed capacitor dielectrics, etc., can solve the problems of capacitor service life limit and overload resistance breakthrough bottleneck, achieve high density, improve continuity, The effect of increasing the dielectric constant of the medium

Active Publication Date: 2018-08-31
安徽源光电器有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dielectric constant of polypropylene film used in traditional MPP capacitors is 4.2, and its dielectric strength is 420VAC / μm. After evaporation and slitting, its dielectric strength is usually around 70VAC / μm in design. Breakthrough in life limit and anti-overload performance has become a bottleneck

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The method for preparing a composite polypropylene dielectric film electrode for film capacitors provided by the present invention includes: placing the polypropylene film in a vacuum high-temperature environment, melting and vaporizing adhesive ceramic powder on the surface of the polypropylene film, and then applying zinc The aluminum composite metal is vapor-deposited on the surface of the adhesive ceramic layer to obtain a composite polypropylene dielectric film electrode for a film capacitor; the temperature of the vacuum high-temperature environment is 800 DEG C, and the air pressure of the vacuum high-temperature environment is 0.2 Pa.

[0015] The bonded ceramic powder includes 1.2 parts by weight of polyvinyl alcohol with a degree of polymerization of 950 and 23 parts by weight of nano ceramic powder. The nano-ceramic powder includes 85 parts by weight of micro silicon powder, 8 parts of silicon oxide, 25 parts of aluminum silicon carbide, 12 parts of aluminum oxid...

Embodiment 2

[0018] The method for preparing a composite polypropylene dielectric film electrode for film capacitors provided by the present invention includes: placing the polypropylene film in a vacuum high-temperature environment, melting and vaporizing the adhesive ceramic powder on the surface of the polypropylene film, and then applying zinc to the surface of the polypropylene film. The aluminum composite metal is vapor-deposited on the surface of the adhesive ceramic layer to obtain a composite polypropylene dielectric film electrode for a film capacitor; the temperature of the vacuum high temperature environment is 1000° C., and the air pressure of the vacuum high temperature environment is 0.1 Pa.

[0019] The bonded ceramic powder includes 0.8 parts of polyvinyl alcohol with a degree of polymerization of 1050 and 27 parts of nano ceramic powder in parts by weight. Nano-ceramic powder includes 80 parts by weight of micro silicon powder, 11 parts of silicon oxide, 20 parts of aluminum ...

Embodiment 3

[0022] The method for preparing a composite polypropylene dielectric film electrode for film capacitors provided by the present invention includes: placing the polypropylene film in a vacuum high-temperature environment, melting and vaporizing adhesive ceramic powder on the surface of the polypropylene film, and then applying zinc The aluminum composite metal is vapor-deposited on the surface of the adhesive ceramic layer to obtain a composite polypropylene dielectric film electrode for a film capacitor; the temperature of the vacuum high temperature environment is 900° C., and the air pressure of the vacuum high temperature environment is 0.15 Pa.

[0023] The bonded ceramic powder includes 1 part of polyvinyl alcohol with a degree of polymerization of 1000 and 25 parts of nano ceramic powder in parts by weight. Nano-ceramic powder by weight includes: 83 parts of micro silicon powder, 9 parts of silicon oxide, 23 parts of aluminum silicon carbide, 13.5 parts of alumina, 6.5 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a composite polypropylene dielectric thin-film electrode for a thin-film capacitor. The method comprises the following steps: putting a polypropylene thin-film into a vacuum high-temperature environment; melting and evaporating adhesive ceramic powder on the surface of the polypropylene thin-film; and evaporating zinc-aluminum composite metal on the surface of the adhesive ceramic powder to obtain the composite polypropylene dielectric thin-film electrode for the thin-film capacitor, wherein the temperature of the vacuum high-temperature environment is 800-1,000 DEG C; and the air pressure of the vacuum high-temperature environment is 0.099-0.2Pa. According to the composite polypropylene dielectric thin-film electrode for the thin-film capacitor prepared by the method, the dielectric strength of a dielectric medium is improved; the dielectric constant of a dielectric thin-film is improved; the antioxidant activity of the electrode is improved; high rated voltage of the thin-film capacitor is achieved; the thin-film capacitor can be miniaturized in size; and high-end and lightweight requirements of a product are met.

Description

Technical field [0001] The invention relates to the technical field of film capacitors, in particular to a method for preparing a composite polypropylene dielectric film electrode for film capacitors. Background technique [0002] The electrical performance of film capacitors, especially the dielectric in the durability, plays a decisive role. The dielectric constant of polypropylene film used in traditional MPP capacitors is 4.2, and the dielectric strength is 420VAC / μm. After evaporation and slitting, the dielectric strength is often around 70VAC / μm in design. Life limit and anti-overload performance breakthroughs have become bottlenecks. Summary of the invention [0003] Based on the technical problems existing in the background art, the present invention proposes a method for preparing a composite polypropylene dielectric film electrode for film capacitors, which improves the dielectric strength of the dielectric, increases the dielectric constant of the dielectric film, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G4/008H01G4/12H01G13/00
CPCH01G4/008H01G4/12H01G13/00
Inventor 温海波温海清梅丽玲章新宇肖娟孙孝东
Owner 安徽源光电器有限公司