Environment-friendly ceramsite partition boards, bricks, and preparation method thereof

The technology of partition board and ceramsite is applied in the field of brick and its preparation, and environmental protection ceramsite partition board, which can solve the problems that decorative materials are prone to moisture, increase the price of interior wall bricks, and high production costs, and achieve low water and chlorine levels. Ion permeability, eliminate brain fatigue, improve the effect of grade

Inactive Publication Date: 2016-04-13
林谷振
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the production cost of diatomite and medical stone is relatively high, which increases the price of interior wall tiles; and because of the porous structure of natural diatomite and medical stone, it is easy to absorb moisture, which will cause the decoration materials on the interior wall and surface to be easily decomposed. Damp and moldy, not suitable for use in humid southern regions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An environment-friendly ceramsite interior wall brick, which is produced by using the following raw materials in parts by weight: 20-30 parts of Portland cement, 30 parts of ceramsite, 15 parts of fly ash, 0.02 part of water glass, 0.2 part of silica fume, foamed 0.01 parts of agent, 0.02 parts of polypropylene fiber, 0.01 parts of water reducer, 20 parts of tailings sand, 10 parts of tea stem powder, 12 parts of papermaking lime mud, and 60 parts of water.

[0025] The tea stalk powder is prepared by using tea stalks as raw materials, drying to a moisture content of 6-10wt%, and crushing through an 80-mesh sieve.

[0026] The paper-making white mud is the white mud recovered by alkali in paper-making production, dried to a moisture content of 10-15%, and crushed through an 80-mesh sieve.

[0027] A method for preparing the above-mentioned environment-friendly ceramsite interior wall brick, comprising the following steps:

[0028] 1) Mix papermaking lime mud, Portland ...

Embodiment 2

[0033] An environment-friendly ceramsite interior wall panel, which is produced by using the following raw materials in parts by weight: 25 parts of Portland cement, 30 parts of ceramsite, 12 parts of fly ash, 0.02 parts of water glass, 0.15 parts of silicon powder, and 0.01 parts of foaming agent 0.02 parts of polypropylene fiber, 0.02 parts of water reducing agent, 10.78 parts of tailings sand, 12 parts of tea stem powder, 10 parts of papermaking white mud, and 80 parts of water.

[0034] The tea stalk powder is prepared by taking tea stalks as raw materials, drying them to a water content of 6-10 wt%, and crushing them through a 120-mesh sieve.

[0035] The paper-making white mud is the white mud recovered by alkali in paper-making production, dried to a moisture content of 10-15%, and crushed through a 120-mesh sieve.

[0036] A method for preparing the above-mentioned environment-friendly ceramsite interior wall brick, comprising the following steps:

[0037] 1) Mix pape...

Embodiment 3

[0042] An environment-friendly ceramsite interior wall brick, which is produced by using the following raw materials in parts by weight: 30 parts of Portland cement, 30 parts of ceramsite, 15 parts of fly ash, 0.04 parts of water glass, 0.1 part of silica fume, and 0.02 parts of foaming agent 0.01 part of polypropylene fiber, 0.02 part of water reducer, 10 parts of tailings sand, 15 parts of tea stem powder, 8 parts of papermaking white mud, and 100 parts of water.

[0043] The tea stalk powder is prepared by using tea stalks as raw materials, drying to a moisture content of 6-10wt%, and crushing through an 80-mesh sieve.

[0044] The paper-making white mud is the white mud recovered by alkali in paper-making production, dried to a moisture content of 10-15%, and crushed through an 80-mesh sieve.

[0045] A method for preparing the above-mentioned environment-friendly ceramsite interior wall brick, comprising the following steps:

[0046] 1) Mix papermaking lime mud, Portland...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Moisture contentaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of wallboard and brick preparation, and more specifically relates to environment-friendly ceramsite partition boards, bricks, and a preparation method thereof. The interior wall tiles are prepared from, by weight, 20 to 30 parts of Portland cement, 30 to 40 parts of ceramsite, 10 to 15 parts of flyash, 0.02 to 0.04 part of water glass, 0.1 to 0.2 part of silicon powder, 0.01 to 0.02 part of a foaming agent, 0.01 to 0.02 part of polypropylene fiber, 0.01 to 0.02 part of a water reducing agent, 10 to 20 parts of tailing sand, 10 to 15 parts of tea stem powder, 8 to 12 parts of paper white sludge, and 60 to 100 parts of water. According to the invention, tea stem powder and paper white sludge are added into raw materials such as cement and ceramsite, so that air purifying effect, thermal insulation effect, sound insulation effect, and anti-permeability are achieved; and tea stem powder and paper white sludge are wastes, so that wastes are changed into valuables, and economic value is increased.

Description

technical field [0001] The invention belongs to the field of preparation of wall boards and bricks, and in particular relates to an environment-friendly ceramsite partition wall board, bricks and a preparation method thereof. Background technique [0002] In interior decoration, in addition to load-bearing walls, other partition walls are generally used for decoration, and the wall bricks used are generally light wall bricks. Most of the existing wall bricks are made by firing clay or sludge. The bricks have high density and heavy weight, which increases the load on the wall. With the improvement of people's economic level and the consideration of health, higher requirements are put forward for the environmental protection of interior decoration materials. Existing wall tiles generally have no environmental protection features, have a certain degree of adverse effects on the human body, and cannot achieve beneficial effects such as air purification, heat preservation, heat ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/26
CPCC04B28/26C04B2103/302C04B18/08C04B18/023C04B7/02C04B38/02C04B16/0633C04B18/12C04B18/24C04B18/0418C04B14/062
Inventor 林谷振詹晓敏
Owner 林谷振
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com