Rolling heat treatment technology for improving strength and plasticity of 6063 aluminium alloy

An aluminum alloy and plasticity technology, which is applied in the field of rolling heat treatment process to improve the strength and plasticity of 6063 aluminum alloy, can solve the problems of high cost and the need for large and heavy equipment, and achieve the effect of improving strength and plasticity

Active Publication Date: 2016-04-27
BEIJING AOPU KEXING TECH
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The large plastic deformation method is a new technology for obtaining ultra-fine-grained 6063 aluminum alloy. This technology applies severe large plastic strain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Apparently, the described embodiments are only some of the embodiments of the present invention, but not all of them. All other embodiments obtained by persons of ordinary skill in the art based on the embodiments of the present invention belong to the protection scope of the present invention.

[0016] A rolling heat treatment process for improving the strength and plasticity of 6063 aluminum alloy according to the embodiment of the present invention includes the following steps:

[0017] Step 1, annealing the aluminum alloy first, wherein the annealing temperature is kept between 505°C and 515°C, and the annealing time is 1 hour;

[0018] Step 2: In order to prevent aging at room temperature, the annealed aluminum alloy is subjected to water quenching treatment, and after its temperature reaches room temperature, it is immediately placed in a pre-prepared freezer for refrigerated storage, and is used for rolling treatment. The indoor temperature is below -20°C;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rolling heat treatment technology for improving the strength and plasticity of a 6063 aluminium alloy. The rolling heat treatment technology comprises the following steps that the aluminium alloy is subjected to annealing treatment for 1h, with the annealing temperature being kept between 505 degrees and 515 degrees; the aluminium alloy after the annealing treatment is subjected to water quenching treatment, and after the temperature of the aluminium alloy reaches room temperature, the aluminium alloy is immediately put in a ready refrigerating chamber for refrigerating storage; the refrigerated aluminium alloy is subjected to rolling treatment within the temperature range of minus 200 degrees to minus 190 degrees by a ready rolling mill till an aluminium alloy sample of which the thickness is decreased by 80% is obtained, wherein the aluminium alloy is required to be submerged in liquid nitrogen for 10-15 before and after each pass reduction treatment and the pass reduction is 5%; the aluminium alloy sample is subjected to warm rolling treatment within the temperature range of 195 degrees to 205 degrees till the reduction reaches 50%, wherein the pass reduction is 20%, and the aluminium alloy sample is required to be heated to 200 degrees and be subjected to heat preservation for 4-5min before and after each pass warm rolling; and the aluminium alloy after the treatment is subjected to heat preservation at 100 degrees for 60h.

Description

technical field [0001] The invention relates to a rolling heat treatment process, in particular to a rolling heat treatment process for improving the strength and plasticity of 6063 aluminum alloy. Background technique [0002] 6063 aluminum alloy (national standard grade wrought aluminum LD61) is a low-alloyed Al-Mg-Si series high-plasticity alloy. The main alloying elements are magnesium and silicon. It has excellent processing performance, excellent weldability, extrudability and electroplating Good corrosion resistance, toughness, easy polishing, color film, excellent anodizing effect, is a typical extrusion alloy. 6063 aluminum alloy profiles are widely used in building profiles, irrigation pipes, solar photovoltaic panel fixed frames and connections due to their good plasticity, moderate heat treatment strength, good welding performance, and gorgeous surface color after anodizing treatment. Corners, pipes, rods, profiles for vehicles, benches, furniture, lifts, fences...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22F1/047
CPCC22F1/047
Inventor 张代轩薛道荣
Owner BEIJING AOPU KEXING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap