A silver-magnesium-nickel and narrow-band technology, which is applied in the field of alloy material processing, can solve the problems of easy burrs, low production efficiency, and large material waste, and achieve the effects of high production efficiency, improved efficiency, and strong repeatability

Active Publication Date: 2016-05-11
西安诺博尔稀贵金属材料股份有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, narrow silver-magnesium-nickel alloy strips are mainly produced by wide-band shearing. The problems of wide-band shearing are large waste of materials, low production efficiency, poor surface quality, and burrs on the side are easy to cause tip discharge.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Device and method for rolling silver magnesium nickel alloy narrow band
  • Device and method for rolling silver magnesium nickel alloy narrow band
  • Device and method for rolling silver magnesium nickel alloy narrow band

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] combine Figure 1-4 The device for rolling silver-magnesium-nickel alloy narrow strips of the present invention includes a pay-off wheel 1 wound with silver-magnesium-nickel alloy wires, a roller 6 for rolling the silver-magnesium-nickel alloy wires into silver-magnesium-nickel alloy narrow strips And the take-up wheel 9 that is used to wind up the silver-magnesium-nickel alloy narrow strip, the entrance of the roll 6 is provided with a roll guide wheel 4, and the exit of the roll 6 is provided with a straightening mechanism 7, so The entry roller guide wheel 4 is provided with a large guide wheel groove 4-1, and a small guide wheel groove 4-2 is arranged in the described large guide wheel groove 4-1, and the straightening mechanism 7 includes a base 7-1 and a A plurality of guide wheels 7-2 arranged on the base 7-1 are provided with guide wheel grooves on each of the guide wheels 7-2, and the groove widths of the guide wheel grooves on each of the guide wheels 7-2 are ...

Embodiment 2

[0046] The specifications of the silver-magnesium-nickel alloy narrow strip to be rolled in this embodiment are: width B=1.5mm, thickness H=0.1mm. combine Figure 1-4 , the present embodiment utilizes the method for rolling silver-magnesium-nickel alloy narrow strip as described in embodiment 1 and comprises the following steps:

[0047] Step 1. Select the silver-magnesium-nickel alloy wire and determine the rolling pass; according to "the cross-sectional area s of the selected silver-magnesium-nickel alloy wire satisfies: 1.1S≤s≤1.25S, wherein S is the silver to be rolled The cross-sectional area of ​​the magnesium-nickel alloy narrow strip, the units of S and s are mm 2 "Principle, the wire diameter of the silver-magnesium-nickel alloy wire material that the present embodiment selects is 0.48mm, and the determined rolling pass is two passes;

[0048] Step 2, use the roll 6 to carry out the first rolling of the silver-magnesium-nickel alloy wire, and use the compressed air ...

Embodiment 3

[0052] The specifications of the silver-magnesium-nickel alloy narrow strip to be rolled in this embodiment are: width B=2.0mm, thickness H=0.15mm. combine Figure 1-4 , the present embodiment utilizes the method for rolling silver-magnesium-nickel alloy narrow strip as described in embodiment 1 and comprises the following steps:

[0053] Step 1. Select the silver-magnesium-nickel alloy wire and determine the rolling pass; according to "the cross-sectional area s of the selected silver-magnesium-nickel alloy wire satisfies: 1.1S≤s≤1.25S, wherein S is the silver to be rolled The cross-sectional area of ​​the magnesium-nickel alloy narrow strip, the units of S and s are mm 2 "Principle, the wire diameter of the silver-magnesium-nickel alloy wire material selected in the present embodiment is 0.65mm, and the determined rolling passes are two passes;

[0054] Step 2, use the roll 6 to carry out the first rolling of the silver-magnesium-nickel alloy wire, and use the compressed a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention provides a device for rolling a silver magnesium nickel alloy narrow band. The device comprises a paying-off wheel, rollers and a take-up wheel. A roller entrance guide wheel is arranged at inlets of the rollers. A straightening mechanism is arranged at outlets of the rollers. Spray guns utilizing compressed air to purge the surfaces of the rollers are arranged on the portions, above and below the inlets, of the rollers respectively. The invention further provides a method for utilizing the device to roll the silver magnesium nickel alloy narrow band. The method includes the following steps of (1) selecting a silver magnesium nickel alloy wire, and determining rolling passes; (2) carrying out first pass rolling to obtain a semi-finished product narrow band; and (3) carrying out second pass rolling to obtain the silver magnesium nickel alloy narrow band. The problem that the requirement for technology of the product is high can be effectively solved, and the narrow band product meeting the quality requirement can be obtained. The device has the beneficial effects of being simple in machining process, high in production efficiency, simple in structure, high in use reliability, high in repeated operability and the like.

Description

technical field [0001] The invention belongs to the technical field of alloy material processing, and in particular relates to a device and method for rolling a silver-magnesium-nickel alloy narrow strip. Background technique [0002] Silver-magnesium-nickel alloy is a ternary alloy composed of silver as the base and adding a small amount of magnesium and nickel, which belongs to the internal oxidation strengthening material. When the silver-magnesium-nickel alloy is heated in air, oxygen-enriched or oxygen, the magnesium atoms originally present in the solid solution are preferentially oxidized to form submicroscopic MgO dispersion-strengthened particles, which rapidly increase the strength, hardness and elastic properties of the alloy, and maintain Good electrical conductivity, thermal conductivity and electrical contact performance, low creep rate at high temperature, good anti-relaxation performance. Silver-magnesium-nickel alloy combines the properties of electrical co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/16B21B39/16B08B5/02B21D1/02B21B45/02B21B15/00
CPCB08B5/023B21B1/166B21B15/00B21B39/165B21B45/0275B21B2015/0064B21D1/02
Inventor 周龙海余建军韩吉庆赵涛马小龙李永娣郑学军宜楠
Owner 西安诺博尔稀贵金属材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap