Quick-drying paint material composition for metal surface and preparation method of quick-drying paint

A quick-drying paint and metal surface technology, applied in the direction of coating, etc., can solve the problem of long drying time

Inactive Publication Date: 2016-05-25
ANHUI CHUNGU 3D PRINTING INTELLIGENT EQUIP IND TECH RES INST CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the fact that in the prior art, the metal coating often takes a long time to dry in actual use, so it needs to wait for it to dry after applying the coating, which often greatly increases the preparation time and reduces the production efficiency. problem, thereby providing a metal surface quick-drying coating material composition and quick-drying coating preparation method with shorter drying time and greatly improved production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The present invention also provides a method for preparing a metal surface quick-drying paint, wherein the preparation method comprises: silicone rubber, dichromium trioxide, butyl acetate, xylene, dibutyltin dilaurate, Dialkyl sodium sulfate, butyl acrylate, ammonium persulfate and titanium dioxide are mixed to prepare a metal surface quick-drying coating; wherein,

[0018] Relative to 100 parts by weight of the silicone rubber, the amount of dichromium trioxide is 5-15 parts by weight, the amount of butyl acetate is 10-20 parts by weight, and the amount of xylene is 5-20 parts by weight. 10 parts by weight, the consumption of said dibutyl tin dilaurate is 1-5 parts by weight, the consumption of said sodium lauryl sulfate is 1-5 parts by weight, the consumption of said butyl acrylate is 10-20 parts by weight parts by weight, the amount of ammonium persulfate is 10-30 parts by weight, and the amount of titanium dioxide is 20-40 parts by weight.

[0019] In a preferred ...

Embodiment 1

[0025] 100g of silicone rubber, 8g of chromium trioxide, 13g of butyl acetate, 6g of xylene, 2g of dibutyltin dilaurate, 2g of sodium lauryl sulfate, 13g of butyl acrylate, 15g of ammonium persulfate and 25g of titanium The white powder was placed at a temperature of 100°C and mixed at a stirring rate of 100r / min to prepare a metal surface quick-drying coating A1.

Embodiment 2

[0027] 100g of silicone rubber, 12g of chromium trioxide, 17g of butyl acetate, 8g of xylene, 4g of dibutyltin dilaurate, 4g of sodium lauryl sulfate, 17g of butyl acrylate, 25g of ammonium persulfate and 35g of titanium The white powder was placed at a temperature of 160°C and mixed at a stirring rate of 150r / min to prepare a metal surface quick-drying coating A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses quick-drying paint material composition for metal surface and a preparation method of quick-drying paint. The composition comprises organic silicon rubber, chromium(III) oxide, butyl acetate, dimethylbenzene, dibutyltin dilaurate, sodium dodecyl sulfate, butyl acrylate, ammonium persulfate and titanium dioxide, wherein in terms of 100 parts by weight of the organic silicon rubber, the composition comprises 5-15 parts by weight of chromium(III) oxide, 10-20 parts by weight of butyl acetate, 5-10 parts by weight of dimethylbenzene, 1-5 parts by weight of dibutyltin dilaurate, 1-5 parts by weight of sodium dodecyl sulfate, 10-20 parts by weight of butyl acrylate, 10-30 parts by weight of ammonium persulfate and 20-40 parts by weight of titanium dioxide. According to the design, drying time is shorter, and the production efficiency is increased greatly.

Description

technical field [0001] The invention relates to the field of production and preparation of metal surface coatings, in particular to a metal surface quick-drying coating material composition and a preparation method of the quick-drying coating. Background technique [0002] As an important protective layer on the metal surface, the metal surface coating plays an extremely important role. After the preparation of many metal-based equipment, it is necessary to coat the surface with coating, and the metal coating often takes a long time to dry in actual use. , so that it needs to wait for it to dry after applying the paint, which often greatly increases the preparation time and reduces production efficiency. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a metal surface quick-drying coating material composition and a preparation method of the quick-drying coating with a shorter drying time and greatly improved production efficiency. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
CPCC09D4/06C09D7/61C09D7/63
Inventor 章传凡吕月林吕晨黄仲佳郑兰斌吴志华刘俊松
Owner ANHUI CHUNGU 3D PRINTING INTELLIGENT EQUIP IND TECH RES INST CO LTD