A technology for sutures and wires, applied in the field of medical suture materials and preparation, can solve problems such as the limitation of room temperature deformation and processing capacity, and achieve favorable sintering or smelting, good hardness and tensile strength, good corrosion resistance and biophase capacitive effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] A medical suture material, characterized in that, in parts by weight, its components include magnesium: 110-140 parts, zinc: 1-2 parts, calcium: 2-2.5 parts, carbon: 0.1 parts, and niobium: 4- 6 parts, iron: 0.5-1 parts, manganese: 1-2 parts, germanium: 0.5-1 parts, zirconium: 1-2 parts, titanium: 0.05-0.1 parts.
[0014] Preferably, in parts by weight, its components include magnesium: 120-140 parts, zinc: 1-2 parts, calcium: 2-2.5 parts, carbon: 0.1 parts, niobium: 4-5 parts, iron: 0.5-1 Parts, manganese: 1 to 2 parts, germanium: 0.5-1 part, zirconium: 1 part, titanium: 0.05 part.
[0015] Preferably, in parts by weight, its components include magnesium: 120 parts, zinc: 2 parts, calcium: 2.5 parts, carbon: 0.1 parts, niobium: 4 parts, iron: 0.5 parts, manganese: 1 part, germanium: 0.5 Parts, zirconium: 1 part, titanium: 0.05 part.
[0016] The method for preparing a medical suture using the medical suture material is characterized in that it comprises the following steps:...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap