A teaching podium table top ceramic plate

A technology of ceramic plates and podiums, applied in the field of teaching materials, can solve problems such as the influence of teaching effects, easy damage, and waste of class time, and achieve the effects of simple and easy-to-operate preparation methods, mild process conditions, and reduced weight

Active Publication Date: 2018-03-20
臧晓梅
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the wooden desktop is relatively easy to damage, the teacher needs to take the students to a special chemistry or physics experiment table for experiments, and the special chemistry or physics experiment table is generally placed in the laboratory, so the teacher needs to bring the students to the Returning to the classroom to teach after finishing the experiment in the laboratory not only wastes the class time but also affects the teaching effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of teaching platform table top ceramic board, it is prepared from the following raw materials by weight:

[0021] 100 parts of silicon carbide, 30 parts of sepiolite, 20 parts of phenolic resin, 20 parts of quartz sand, 15 parts of water, 15 parts of bentonite, 12 parts of kaolin, 6 parts of glass fiber, 6 parts of polyvinyl alcohol, 3 parts of hydroxyethyl cellulose 3-parts of white graphite, 2 parts of molybdenum disulfide, 2 parts of sodium alginate, 1 part of boron oxide, 1 part of potassium oxide;

[0022] The preparation method of above-mentioned ceramic plate comprises the steps:

[0023] 1) Add glass fiber, polyvinyl alcohol, hydroxyethyl cellulose and white graphite into water in sequence, stir at 200 rpm for 15 minutes, then heat to 50°C, keep warm for 5 minutes, and cool naturally to room temperature to obtain mixture A;

[0024] 2) Add silicon carbide, sepiolite, phenolic resin and quartz sand into the ball milling tank in turn, and ball mill until t...

Embodiment 2

[0029] A kind of teaching platform table top ceramic board, it is prepared from the following raw materials by weight:

[0030] 130 parts of silicon carbide, 50 parts of sepiolite, 30 parts of phenolic resin, 30 parts of quartz sand, 20 parts of water, 20 parts of bentonite, 15 parts of kaolin, 9 parts of glass fiber, 9 parts of polyvinyl alcohol, 5 parts of hydroxyethyl cellulose 5 parts of white graphite, 4 parts of molybdenum disulfide, 4 parts of sodium alginate, 2 parts of boron oxide, and 2 parts of potassium oxide;

[0031] The preparation method of above-mentioned ceramic plate comprises the steps:

[0032] 1) Add glass fiber, polyvinyl alcohol, hydroxyethyl cellulose and white graphite into water in sequence, stir at 200 rpm for 15 minutes, then heat to 50°C, keep warm for 5 minutes, and cool naturally to room temperature to obtain mixture A;

[0033] 2) Add silicon carbide, sepiolite, phenolic resin and quartz sand into the ball milling tank in turn, and ball mill u...

Embodiment 3

[0038] The performance test of ceramic plate of the present invention:

[0039] Water absorption is measured according to GB / T 3299-2011 "Method for Determination of Water Absorption of Ceramics for Daily Use", acid resistance and alkali resistance are measured according to JC / T 2138-2012 "Test Method for Acid and Alkali Corrosion Resistance of Fine Ceramics", bulk density Measured according to Archima's principle. Compressive strength, compressive strength and hardness according to GB / T 4740-1999. The specific test results are shown in Table 1:

[0040] Table 1

[0041] performance

[0042] Conclusion: The ceramic plate prepared by the present invention has high flexural and compressive strength, high hardness, light weight, acid and alkali corrosion resistance, and can be used as a platform table top with broad prospects.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of teaching materials and discloses a teaching platform desktop ceramic plate. The teaching platform desktop ceramic plate is produced from silicon carbide, sepiolite, phenolic resin, quartz sand, water, bentonite, kaolin, glass fibers, polyvinyl alcohol, hydroxyethyl cellulose, white graphite, molybdenum disulfide, sodium alginate, boric oxide and potassium oxide. The teaching platform desktop ceramic plate is applicable to platform desktops and excellent in performance, thereby being promising in application prospect.

Description

technical field [0001] The invention belongs to the field of teaching materials, and in particular relates to a ceramic board for the table top of a teaching platform. Background technique [0002] Existing dais is generally used for teachers to use when giving lectures in the classroom, and its desktop is generally a wooden desktop for teachers to place teaching aids. At present, in order to make the lecture content more vivid and easy for students to understand and absorb, many physics teachers and chemistry teachers usually combine physics experiments and chemical experiments to explain the lecture content in the classroom. However, because the wooden desktop is relatively easy to damage, the teacher needs to take the students to a special chemistry or physics experiment table for experiments, and the special chemistry or physics experiment table is usually placed in the laboratory, so the teacher needs to bring the students to the Returning to the classroom to teach aft...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/565C04B35/622
CPCC04B35/565C04B35/622C04B2235/3201C04B2235/3409C04B2235/3418C04B2235/349C04B2235/36C04B2235/386C04B2235/446C04B2235/449C04B2235/48C04B2235/5216C04B2235/96C04B2235/9692
Inventor 臧晓梅朱利云张海霞
Owner 臧晓梅