Preparation method and application of copper (II) ion imprinting polyurethane

A technology of ion imprinting and polyurethane, applied in chemical instruments and methods, other chemical processes, water/sludge/sewage treatment, etc., to achieve fast adsorption rate and high adsorption selectivity

Active Publication Date: 2016-06-08
HUAIHAI INST OF TECH
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyurethane-based copper (II) ion-imprinted polymer materials have not been reported or disclosed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Example 1 Preparation and properties of copper (II) ion-imprinted polyurethane foam

[0035] Weigh 30 grams of 5-((N-chloride, N-dihydroxyethyl-N-methyl-ammonium) methyl) salicylaldoxime and 12 grams of copper sulfate pentahydrate and dissolve in deionized water, stir at room temperature for 30min, spin Evaporate and concentrate, and after cooling, dark blue crystals are precipitated as bis(5-(((N, N-di(β-hydroxyethyl)-N-methyl-ammonium) methyl) salicylaldoxime) copper(II) The complex is 30.4 g, and the yield is 90.8%.

[0036] 30 grams of bis(5-((N, N-chloride, N-bis(β-hydroxyethyl)-N-methyl-ammonium) methyl) salicylaldoxime) copper(II) complex with a hydroxyl value of 56 mgKOH / g, 42 grams of polyether trihydric alcohol with an average molecular weight of 3000-4000, 13 grams of glycerin and 30 grams of N, N-dimethylformamide, mix well, and then add 0.25 grams of dibutyltin dilaurate, triethylene dilaurate 0.25 grams of amine, 25 grams of pentane and 2.4 grams of dei...

Embodiment 2

[0045] 30 grams of bis(5-((N, N-chloride, N-bis(β-hydroxyethyl)-N-methyl-ammonium) methyl) salicylaldoxime) copper(II) complex with a hydroxyl value of 56 mgKOH / g, 42 grams of polyether trihydric alcohol with an average molecular weight of 3000-4000, 13 grams of glycerin and 130 grams of N, N-dimethylformamide are mixed evenly, and then 0.25 grams of dibutyltin dilaurate and triethylene dilaurate are added. 0.25 g of amine, and fully stirred; finally added 58 g of diphenylmethane diisocyanate, stirred quickly and mixed evenly, polymerized at room temperature for 6 hours, aged at 50°C for 6 hours, and then extruded and granulated in deionized water. Prepare blue copper (II) ion complex polymer resin particles; use ethyl acetate / methanol (volume ratio=1:5) mixed solution to rinse the obtained resin particles for 48 hours, and use 2.0mol / L hydrochloric acid to continue to rinse After 30 minutes, rinse with deionized water until neutral, and dry in vacuum to obtain copper (II) io...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
densityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of a polyurethane base copper (II) ion imprinting polymer with high adsorption capacity, high selectivity and quick adsorption rate. Copper (II) ion imprinting polyurethane serves as a solid phase adsorber, and an effective method is provided for removing copper (II) ions in various water systems and aided detection, separation and enrichment on the copper (II) ions in the various water systems. The copper (II) ion imprinting polyurethane can be formed by foam, diaphragm plate, spun fiber, coating, package or particle processing.

Description

technical field [0001] The invention relates to a copper (II) ion imprinted polymer and its preparation method and application, in particular to a polyurethane-based copper (II) imprinted polymer, which is used for the concentration, enrichment, separation and detection of copper (II), and belongs to The field of functional polymer materials. technical background [0002] Ion-imprinted polymers are a branch of imprinted polymers, and one of the basic raw materials for preparing ion-imprinted polymers is a polymerizable ligand or a chelating ligand. The polymerizable ligand or chelating ligand can form a stable complex with the template (referring to the transition metal ion), and the steric structure is stable through the copolymerization reaction with the crosslinking agent, and the orientation is strong, which is beneficial to the preparation Ion-imprinted polymers with high selectivity and stable imprinting function are the preferred solid-phase selective extraction mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08J9/14C08J9/28B01J20/26C02F1/28C02F101/20
CPCB01J20/262B01J20/265B01J20/268C02F1/285C02F2101/20C08G18/3819C08G18/4829C08G18/6677C08G2101/00C08J9/141C08J9/28C08J2203/14C08J2375/08
Inventor 张田林李京昊张可人岳夏丹
Owner HUAIHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap