Wall-like brick high-molecular hard wall decorative material and preparation method thereof

A decorative material and polymer technology, which is applied in the direction of fireproof coatings, polyester coatings, antifouling/underwater coatings, etc., can solve the problems of destroying the natural environment, wall tiles falling off, and large transportation volume

Inactive Publication Date: 2016-07-20
JIANGYIN HUADONG DECORATIVE MATERIAL
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. High cost: the price of wall tiles per square meter is 100-400 yuan
[0004] 2. Firstly, the firing of wall bricks requires digging waste grain fields, secondly, coal consumption, thirdly, landfill waste and scraps, and fourthly, terminal construction and cutting, all of which will destroy the natural environment and pollute the water and air environment, affecting human health
[0005] 3. The medium and low-grade wall tiles used for the exterior wall will seep water, including poor construction, which will cause the wall to be damp and affect the inner wall wallpaper or paint to mildew and fall off. In severe cases, the exterior wall will also be damaged.
[0006] 4. Long-term exposure to the sun and rain will be weathered and easy to accumulate dust and difficult to clean, dull, affecting the appearance of the wall
[0007] 5. When the decoration takes a long time, severe freezing, and poor construction quality will cause the wall tiles to fall off, resulting in personal injury and unsightly walls
[0008] 6. The transportation volume is large, the construction volume is large, and the terminal construction cost is also high
[0009] 7. The color and pattern have little plasticity, and the appearance is monotonous and unsightly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0152] The present invention relates to a brick imitation polymer rigid wall decoration material, which comprises a base material, a printed mask and a polyester coating, the base material and the printed mask are bonded by hot pressing, and the surface of the printed mask is coated with a net Polyester coating.

[0153] The preparation method of the imitation wall brick polymer hard wall decoration material comprises the following steps:

[0154] Step 1. Prepare the base material

[0155] 1.1. Ingredients

[0156] Using PVC resin, PVC greenhouse film recycling material as the main material, adding PE reinforcing agent, 400 mesh calcium powder, dibutyl ester, base color paste, silver ion agent, NH1197 flame retardant and other plasticizing additives according to the proportion The weight proportion of composition is:

[0157] PVC resin 100 parts

[0158] PVC greenhouse film recycling material 80 copies

[0159] 85 parts of 400 mesh calcium powder

[0160] PE enhancer 11 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a wall-like brick high-molecular hard wall decorative material, comprising a base material, a printing mask and a polyester coating layer, wherein the base material and the printing mask are laminated together by hot pressing, and the polyester coating layer is coated as a net on the surface of the printing mask. A preparation method of the wall-like brick high-molecular hard wall decorative material comprises the following steps: 1, preparing the base material; 2, preparing the printing mask; 3, printing a mask; 4, performing hot-pressing lamination; 5, performing net coating of polyester; 6, curing; and 7, performing mould pressing cutting. The wall-like brick high-molecular hard wall decorative material provided by the invention has the advantages of avoiding mildew, having fire resistance, and being high in strength, hardness, degree of finish, brightness, and simulation view; and the preparation method has the advantages of being low in production cost, high in quality of products, and high in assembly line output.

Description

technical field [0001] The invention relates to a wall brick imitation polymer hard wall decoration material and a preparation method thereof. Background technique [0002] The walls of modern buildings attach great importance to decoration. For indoor and outdoor wall decoration materials, wall bricks are mainly used in my country. And wall tiles have the following disadvantages: [0003] 1. High cost: the price of wall tiles per square meter is 100-400 yuan. [0004] 2. Firstly, the firing of wall bricks requires digging waste grain fields, secondly, coal consumption, thirdly, landfill waste and scraps, and fourthly, terminal construction and cutting, all of which will destroy the natural environment and pollute the water and air environment, affecting human health. [0005] 3. The medium and low-grade wall tiles used for the exterior wall will seep water, including poor construction, which will cause the wall to be damp and affect the inner wall wallpaper or paint to mi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/06C08K13/02C08K3/26C08K5/10C09D167/00C09D5/18C09D5/14E04F13/075
CPCC08L27/06C08J5/18C08J2327/06C08K5/10C08K13/02C08L2201/02C08L2203/16C08L2205/025C08L2205/03C08L2207/20C09D5/14C09D5/18C09D167/00E04F13/18E04F2290/046C08L23/06C08K2003/265
Inventor 朱广和赵霞王燕李向华徐文亚赵丽芳
Owner JIANGYIN HUADONG DECORATIVE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products