External drying assisting agent matched with polyurethane foam caulking agent and preparing method and application thereof

A polyurethane foam and desiccant technology, applied in the direction of polyurea/polyurethane adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the dry time of about 4-6 hours in season, and it needs to be around zero in winter It takes 24 hours or more to fully dry, long-term secondary corrections, time-consuming and labor-intensive problems, to achieve the effects of avoiding catalyst hydrolysis, accelerating dissolution speed, and rapid catalytic action

Active Publication Date: 2016-07-27
SHIJIAZHUANG DONGXIANG CHEM CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface drying time of polyurethane foam at a room temperature of 20°C is generally within 10 minutes; the full drying time varies with the ambient temperature and humidity. Generally, the full drying time in summer is about 4-6 hours, and it takes about 24 hours in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] The preparation method of the aerosol drying aid includes the following steps:

[0025] A. Weigh the preservatives, catalysts and water in proportion, add them to the reactor in the order of preservatives, water, and catalysts, and mix them. Heat up to no more than 30°C (preferably 20-25°C), and stir thoroughly until the solution Clear

[0026] B. Pour the drying aid solution prepared in step A into an aerosol tank, press the valve, and flush the propellant gas to obtain an external drying aid aerosol.

[0027] An application of external drying aid with polyurethane foam caulking agent refers to the use of external drying aid with one-component polyurethane foam caulking agent.

[0028] There are two ways to use the external drying aid and polyurethane foam jointing agent together:

[0029] (1) Mix the external drying aid into the foam produced by the polyurethane foam sealant, and then extrude the foam. An external drying aid extruding device can be installed on the glue gun, ...

Example Embodiment

[0033] Example 1

[0034] (1) An external drying aid aerosol with polyurethane foam sealant, including the following components:

[0035] Drying aid: Kasone preservative (5-chloro-2-methyl-4-isothiazolin-3-one) 7.5g, triethylenediamine catalyst 37.5g, distilled water 205g;

[0036] Projection gas: 30g propane butane (the mass ratio of propane to butane is 1:2).

[0037] (2) The preparation method of the aerosol drying aid is:

[0038] A. Weigh the preservatives, catalysts and distilled water, add them to the reactor in the order of preservatives, water, and catalysts and mix them. The temperature is raised to 20~25°C, and the mixture is fully stirred until the solution is clear;

[0039] B. Use a 400 ml tinplate aerosol can as a container, pour the drying aid solution in step A; press the valve and flush with the propellant gas propane butane to obtain the external drying aid aerosol.

[0040] (3) Application of the external drying aid

[0041] The external drying aid aerosol is used in co...

Example Embodiment

[0046] Example 2

[0047] (1) An external drying aid aerosol with polyurethane foam sealant, including the following components:

[0048] Drying aid: Kasone preservative (5-chloro-2-methyl-4-isothiazolin-3-one) 15.6g, triethylenediamine catalyst 26g, distilled water 218.4g;

[0049] Projection gas: 20g of propane and butane (the mass ratio of propane to butane is 1:4).

[0050] (2) The preparation method of the aerosol drying aid is:

[0051] A. Weigh the preservatives, catalysts and distilled water, add them to the reactor in the order of preservatives, water, and catalysts and mix them, control the temperature at 25±2℃, and stir well until the solution is clear;

[0052] B. Use a 400 ml tinplate aerosol can as a container, pour the drying aid solution in step A; press the valve and flush with the propellant gas propane butane to obtain the external drying aid aerosol.

[0053] (3) Application of the external drying aid

[0054] The external drying aid aerosol is used in combination with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an external drying assisting agent matched with a polyurethane foam caulking agent and a preparing method and application thereof.The external drying assisting agent comprises, by mass, 3%-6% of preservative, 10%-20% of catalyst and the balance water; the external drying assisting agent is an aerosol, and further comprises casting gas, and the weight ratio of the drying assisting agent to the casting gas is 25:3.The preparing method includes the steps that A, the preservative, the catalyst and the water are weighed in proportion, and are fully dissolved to be clear; B, the drying assisting agent is poured into an aerosol can, a valve is pressed, and the casting gas is inflated.The external drying assisting agent is used in cooperation with the polyurethane foam caulking agent, and is not limited by environment conditions, polyurethane foam can be fully dried within 15 minutes, correction can be carried out while gluing, and efficiency is greatly improved; under catalyzing of the external drying assisting agent, the produced polyurethane foam is even, stable, free of treaded foam and cavities and good in sealing effect.

Description

technical field [0001] The invention relates to an external drying aid combined with a polyurethane foam caulking agent, a preparation method and application thereof, and belongs to the technical field of building materials. Background technique [0002] Polyurethane foam caulking agent, commonly known as foaming agent, PU caulking agent, is a moisture-curing, multi-purpose polyurethane foam filling elastic sealing material, which is filled with polyurethane prepolymer, foaming agent, catalyst and other components. Special polyurethane product in pressure-resistant aerosol cans. During construction, the aerosol colloid is sprayed to the site to be constructed through a matching sizing gun or a manual nozzle. The foamy polyurethane material expands rapidly and reacts with the air or the moisture in the substrate to form a foam, and the molding is completed in a short period of time. , Foaming, bonding and sealing process. Its cured foam elastomer has excellent properties su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K5/47C08K5/17C08G18/48C08L75/08C09J11/04C09J175/08
CPCC08G18/4808C08K5/17C08K5/47C08L75/08C09J11/04C09J175/08
Inventor 步帅步贺
Owner SHIJIAZHUANG DONGXIANG CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka