Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Thermal-deformation-resisting polyethylene foam plastic and preparation method thereof

A technology of polyethylene foaming and low-density polyethylene, which is applied in the field of polyethylene foaming plastics and can solve problems such as pipe separation

Active Publication Date: 2016-08-10
芜湖格川新材料科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main purpose of the present invention is to provide a heat-resistant deformation polyethylene foamed plastic and its preparation method, so as to solve the phenomenon that the polyethylene foamed plastic in the prior art is separated from the pipe when it is used at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal-deformation-resisting polyethylene foam plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Provide a kind of polyethylene foam plastics, prepare through the following steps:

[0015] (1) Weigh each raw material according to mass percentage: bisphenol A type epoxy resin 4%, polyvinyl butyral 0.8%, diethylene triamine 0.9%, epoxy modified silicone resin 3%, potassium acetate 0.5% , Azodicarbonamide 6%, and the balance is low-density polyethylene;

[0016] (2) Add bisphenol A type epoxy resin, polyvinyl butyral, diethylene triamine, epoxy modified silicone resin, potassium acetate and low density polyethylene into the closed rubber mixing machine, at 140 ~ 150 Mix evenly at ℃, then add azodicarbonamide, mix evenly at 155-160℃, and discharge to obtain the mixed material;

[0017] (3) Put the mixed material into a mould, and then send it into a flat vulcanizer for cross-linking and foaming. The temperature is 160-175° C., the pressure is 10-12 MPa, and the holding time is 15-20 minutes;

[0018] (4) After the pressure holding is completed, the pressure drops sud...

Embodiment 2

[0020] Provide a kind of polyethylene foam plastics, prepare through the following steps:

[0021] (1) Weigh each raw material according to mass percentage: bisphenol A type epoxy resin 4.8%, polyvinyl butyral 0.6%, diethylene triamine 0.7%, epoxy modified silicone resin 3.2%, potassium acetate 0.2% , 7% of azodicarbonamide, and the balance is low-density polyethylene;

[0022] (2) Add bisphenol A type epoxy resin, polyvinyl butyral, diethylene triamine, epoxy modified silicone resin, potassium acetate and low density polyethylene into the closed rubber mixing machine, at 140 ~ 150 Mix evenly at ℃, then add azodicarbonamide, mix evenly at 155-160℃, and discharge to obtain the mixed material;

[0023] (3) Put the mixed material into a mould, and then send it into a flat vulcanizer for cross-linking and foaming. The temperature is 160-175° C., the pressure is 10-12 MPa, and the holding time is 15-20 minutes;

[0024] (4) After the pressure holding is completed, the pressure dr...

Embodiment 3

[0026] Provide a kind of polyethylene foam plastics, prepare through the following steps:

[0027] (1) Weigh each raw material according to mass percentage: bisphenol A type epoxy resin 5%, polyvinyl butyral 1.0%, diethylenetriamine 0.6%, epoxy modified silicone resin 4%, potassium acetate 0.4% , Azodicarbonamide 8%, the balance is low density polyethylene;

[0028] (2) Add bisphenol A type epoxy resin, polyvinyl butyral, diethylene triamine, epoxy modified silicone resin, potassium acetate and low density polyethylene into the closed rubber mixing machine, at 140 ~ 150 Mix evenly at ℃, then add azodicarbonamide, mix evenly at 155-160℃, and discharge to obtain the mixed material;

[0029] (3) Put the mixed material into a mould, and then send it into a flat vulcanizer for cross-linking and foaming. The temperature is 160-175° C., the pressure is 10-12 MPa, and the holding time is 15-20 minutes;

[0030] (4) After the pressure holding is completed, the pressure drops suddenly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a thermal-deformation-resisting polyethylene foam plastic and a preparation method thereof .The polyethylene foam plastic is prepared from bisphenol-A epoxy resin 4, polyvinyl butyral, diethylenetriamine, epoxy-modified organosilicon resin, potassium acetate, azodicarbonamide and low-density polyethylene in a molding foaming mode.

Description

technical field [0001] The invention relates to polyethylene foamed plastics, in particular to a heat-resistant deformation polyethylene foamed plastics and a preparation method thereof. Background technique [0002] As a thermal insulation material, polyethylene foam has many advantages: light weight, low density, and a bulk density of about 20-40kg / m 3 ; The thermal conductivity is small, generally between 0.017 and 0.027 (w / m·k); the water absorption is low, and it has strong water resistance. Because polyethylene foam plastic has the above advantages, it is more suitable for the insulation of air-conditioning systems, especially for air-conditioning systems that require high cleanliness. Moderate polyethylene foam is a good substitute. [0003] However, polyethylene foamed plastics are not suitable for use at high temperatures. When the temperature exceeds 70°C, polyethylene foamed plastic sleeves will melt and shrink, resulting in a phenomenon of being separated from ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L63/00C08L29/14C08L83/04C08K5/098C08J9/10C08G59/50
CPCC08G59/502C08J3/246C08J9/0023C08J9/0061C08J9/103C08J2203/04C08J2323/06C08J2463/00C08L23/06C08L2201/08C08L2203/14C08L2205/035C08L2205/08C08L2207/066C08L63/00C08L29/14C08L83/04C08K5/098
Inventor 魏亮
Owner 芜湖格川新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More