Thermally-insulated nano paint for transparent glass and preparation method of paint

A technology of transparent glass and nano heat insulation, applied in the field of coatings, can solve the problems of low light transmittance, complex process, poor heat insulation effect, etc., and achieve the effect of high visibility, excellent acid resistance, and remarkable heat insulation effect.

Inactive Publication Date: 2016-08-31
WUXI IMPRINT NANO TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, products such as sticking film, heat insulating paper, and metal-coated heat insulating glass are usually used to realize the heat insulation problem of glass windows, but these products usually have problems such as low light transmittance, poor heat insulation effect, and complicated process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The invention provides a nano heat-insulating transparent glass coating, which comprises the following raw materials in parts by weight:

[0024] 80-120 parts of epoxy resin; 10-25 parts of nano-ATO; 5-15 parts of nano-silica; 50-80 parts of curing agent; 20-40 parts of solvent; 0.1-0.5 parts of dispersant; 0.1-0.5 part of defoamer.

[0025] Among them, the curing agent is polyamide 650, the solvent is acetone, the dispersant is BYK, the leveling agent is acrylic resin, and the defoaming agent is silicone.

Embodiment 2

[0027] The invention provides a nano heat-insulating transparent glass coating, which comprises the following raw materials in parts by weight:

[0028] 90-110 parts of epoxy resin; 15-20 parts of nano-ATO; 8-12 parts of nano-silica; 60-70 parts of curing agent; 25-35 parts of solvent; 0.2-0.4 parts of dispersant; 0.2-0.4 part of defoamer.

[0029] Among them, the curing agent is polyamide 650, the solvent is acetone, the dispersant is BYK, the leveling agent is acrylic resin, and the defoaming agent is silicone.

Embodiment 3

[0031] The invention provides a nano heat-insulating transparent glass coating, which comprises the following raw materials in parts by weight:

[0032] 90 parts of epoxy resin; 15 parts of nano-ATO; 8 parts of nano-silica; 60 parts of curing agent; 25 parts of solvent; 0.2 parts of dispersant;

[0033] Among them, the curing agent is polyamide 650, the solvent is acetone, the dispersant is BYK, the leveling agent is acrylic resin, and the defoaming agent is silicone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thermally-insulated nano paint for transparent glass and a preparation method of the paint. The thermally-insulated nano paint for transparent glass is prepared from, by weight, 80-120 parts of epoxy resin, 10-25 parts of nano ATO, 5-15 parts of nano silicon dioxide, 50-80 parts of curing agent, 20-40 parts of solvent, 0.1-0.5 part of dispersing agent, 0.1-0.5 part of leveling agent, and 0.1-0.5 part of defoaming agent. The preparation method of the thermally-insulated nano paint for transparent glass is simple; the paint is stable in performance, high in light transmittance and excellent in heat-insulating performance.

Description

technical field [0001] The invention relates to a coating, in particular to a nano heat-insulating transparent glass coating and a preparation method thereof. Background technique [0002] At present, the thermal effect of the global environment is intensifying, and energy conservation and emission reduction are common problems faced by the world's construction industry. Building energy saving is to reduce the energy consumption of buildings for heating and cooling under the condition of ensuring comfortable room temperature. Glass is widely used in buildings as a transparent material. Studies have shown that the heat transfer coefficient of ordinary glass is 3.2 times that of walls and 5 times that of roofs. In addition, due to the transparency of ordinary glass, light can pass directly from one side of the glass to the other, causing the space inside the glass to be heated by sunlight. It can be seen that improving the heat insulation effect of glass windows is an import...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12
CPCC09D163/00C08K2201/011C08L2205/03C09D7/61
Inventor 王晶
Owner WUXI IMPRINT NANO TECH