Technology for pretreating complex and difficult-to-treat gold concentrate through utilizing industrial microware

A technology of refractory gold and industrial microwave, which is applied in the field of industrial microwave pretreatment of complex and refractory gold concentrate and gold smelting to achieve the effects of promoting decomposition and oxidation, reducing activation energy and shortening the process flow.

Inactive Publication Date: 2016-09-14
托里县招金北疆矿业有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to propose a kind of process technology of complex refractory gold concentrate with industrial microwave pretreatment in view of the existing problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology for pretreating complex and difficult-to-treat gold concentrate through utilizing industrial microware
  • Technology for pretreating complex and difficult-to-treat gold concentrate through utilizing industrial microware
  • Technology for pretreating complex and difficult-to-treat gold concentrate through utilizing industrial microware

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: A kind of process technology of complex refractory gold concentrate with industrial microwave pretreatment, described technical process is carried out according to the following steps: the first step puts complex refractory gold concentrate into continuous horizontal belt type industrial microwave oven shop The thickness of the ore layer is 25-100mm. Turn on the fan of the microwave oven and let in the air. In the second step, start the microwave heating device to dry and roast the complex and refractory gold concentrate obtained in the first step. The microwave frequency in the drying section is controlled. The microwave source is 915MHz, the power level of the single tube of the microwave source is 3kW, 5kW, the temperature of the drying section is controlled at 120°C ~ 140°C, and the drying time is 5 ~ 10 minutes; the microwave frequency of the roasting section is controlled at 915MHz, and the power of the single tube of the microwave source is The stage...

Embodiment 2

[0020] Embodiment 2: A kind of process technology of complex refractory gold concentrate with industrial microwave pretreatment, described technical process is carried out according to the following steps: the first step puts complex refractory gold concentrate into continuous horizontal belt-type industrial microwave oven shop The thickness of the ore layer is 25-100mm. Turn on the fan of the microwave oven and let in the air. In the second step, start the microwave heating device to dry and roast the complex and refractory gold concentrate obtained in the first step. The microwave frequency in the drying section is controlled. The microwave source is 915MHz, the single-tube power level of the microwave source is 5kW, 10kW, the temperature of the drying section is controlled at 140°C-160°C, and the drying time is 10-15 minutes; the microwave frequency of the roasting section is controlled at 915MHz, and the power level of the single-tube microwave source is The grades are 20kW...

Embodiment 3

[0022] Embodiment 3: A kind of process technology of complex refractory gold concentrate with industrial microwave pretreatment, described technical process is carried out according to the following steps: the first step puts complex refractory gold concentrate into continuous horizontal belt-type industrial microwave oven shop The thickness of the ore layer is 25-100mm. Turn on the fan of the microwave oven and let in the air. In the second step, start the microwave heating device to dry and roast the complex and refractory gold concentrate obtained in the first step. The microwave frequency in the drying section is controlled. The microwave source is 2450MHz, the single-tube power level of the microwave source is 1kW, 5kW, the temperature of the drying section is controlled at 160°C-200°C, and the drying time is 15-20 minutes; The stage is 50kW, the temperature of the roasting section is controlled at 550°C-600°C, the roasting volatilization time is 20-25 minutes, and the pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a technology for pretreating complex and difficult-to-treat gold concentrate through utilizing industrial microware. The technology comprises the steps of putting the complex and difficult-to-treat gold concentrate in an industrial microwave oven, and paving the complex and difficult-to-treat gold concentrate; starting a microwave oven fan, and introducing air; starting a microwave heating device to sequentially dry and bake the complex and difficult-to-treat gold concentrate; sending obtained flue gas into a recycling system to recycle As2O3 and SO2, so as to prepare arsenic and arsenic; and sending obtained hot gold concentrate to a cyanide leaching system to recycle valuable metals such as gold and silver. According to the technology, the leaching rate of gold can be greatly increased, the operation is easy, the technological process is short, the reaction temperature is decreased, the reaction time is shortened, and the production efficiency is improved.

Description

technical field [0001] The invention relates to a technology for pretreating complex and refractory gold concentrates with industrial microwaves, and belongs to the field of gold smelting industry. Background technique [0002] With the development of the gold industry, domestic easy-to-handle gold mines have basically been exhausted, and the scope of development has rapidly developed from single, easy-to-handle gold resources to high-arsenic, high-carbon, low-sulfur, and polymetallic-containing refractory gold resources In the field, the occurrence state of gold in ores is mainly gold in dispersed state, colloidal gold, lattice gold or solid solution gold in gold-bearing minerals. Arsenopyrite (FeAsS) and pyrite (FeS 2 ) is the main gold-bearing mineral, and gold is usually wrapped in it or impregnated in crystals in fine grains or microscopic state. Using the conventional cyanidation gold extraction method, the direct gold leaching rate is generally below 80%, and some e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/02C22B11/08C01B17/50C01G28/00
CPCC01B17/50C01G28/005C22B1/02C22B11/08
Inventor 杨悦增刘洪晓宋裕华冷启龙张敬闯
Owner 托里县招金北疆矿业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com