A method for improving the initial adhesion of nylon 66 dipped cord fabric

A technology of dipped cord fabric and adhesive force, which is applied in the field of tire manufacturing, can solve the problems of glue line detachment, low initial adhesion of nylon 66 dipped cord fabric, and exposed cords, so as to reduce decomposition and avoid glue lines Detachment, quality-enhancing effects

Active Publication Date: 2017-05-10
PINGDINGSHAN SHENMA TIRE CORD FABRIC DEV CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a production method for improving the initial adhesion of nylon 66 dipped cord fabric in order to solve the problems of low initial adhesive force of nylon 66 dipped cord fabric, glue line detachment and exposed cord during calendering, etc. , specifically including a dipping solution for nylon 66 cord fabric and a production method for improving the initial adhesion of nylon 66 dipped cord fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for improving the initial adhesion of nylon 66 dipped cord fabric
  • A method for improving the initial adhesion of nylon 66 dipped cord fabric
  • A method for improving the initial adhesion of nylon 66 dipped cord fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of dipping solution of nylon 66 cord fabric, in parts by weight, consists of 0.9 parts of resorcinol, 1.4 parts of formaldehyde, 0.1 part of caustic soda, 2.9 parts of natural rubber latex, 15.3 parts of butylpyridine latex, 1.3 parts of ammonia, 28.9 parts of low Pure water is prepared by mixing for 9 hours at a temperature of 5-10°C.

Embodiment 2

[0020] A kind of dipping solution of nylon 66 cord fabric, in parts by weight, consists of 1.8 parts of resorcinol, 1.4 parts of formaldehyde, 0.1 part of caustic soda, 15 parts of natural rubber latex, 51.5 parts of butylpyridine latex, 3.9 parts of ammonia, 79.2 parts of low Pure water is prepared by mixing for 5 hours at a temperature of 31-35°C.

Embodiment 3

[0022] A kind of dipping solution of nylon 66 cord fabric, in parts by weight, by 1.5 parts of resorcinol, 3.5 parts of formaldehyde, 0.1 part of caustic soda, 25.7 parts of natural latex, 28 parts of butylpyridine latex, 1.8 parts of ammonia, 35.6 parts of low Pure water, made by mixing for 6 hours at a temperature of 20-22°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for improving the initial adhesive force of nylon 66 dipped tyre cord fabric. The method includes the steps of: 1) passing a non-dipped nylon 66 cord fabric through a dip solution at a speed of 50-120m / min; and 2) passing the dipped nylon 66 cord fabric through a drying area 1A, a drying area 1B, a drafting area and a shaping area in order at a speed of 50-120m / min, and then conducting packaging and storage. The dip solution is prepared by mixing 0.9-2.8 parts of resorcinol, 1.4-4.1 parts of formaldehyde, 0.1 part of caustic soda, 2.9-25.7 parts of natural latex, 8.6-51.5 parts of butadiene vinyl-pyridine rubber latex, 1.3-3.9 parts of ammonia water, and 28.9-79.2 parts of low purity water at 5-35DEG C for 5-9h. According to the invention, the dip solution greatly increases the natural latex content, the initial adhesive force of the prepared nylon 66 dipped tyre cord fabric finished product is increased to 500-1000g / 5 threads, and the production cost is low, therefore the method is easy for industrialization.

Description

technical field [0001] The invention belongs to the field of tire manufacturing, in particular to a production method for improving the initial adhesive force of nylon 66 dipped cord fabric. Background technique [0002] Nylon 66 dipped cord fabric is an important skeleton material of the tire. The dipped cord fabric and rubber must have good bonding performance, and the bonding force directly affects the performance and service life of the tire. [0003] With the development of the tire industry, the formula of tire rubber is constantly changing, and the requirements for adhesion are constantly improving. Some customers require particularly good initial adhesion. Under the current technical conditions, the dipped cord fabric produced by using the traditional latex system formula and dipping process, when cutting after calendering in some high-end tire companies, defects such as edge glue line detachment and cord exposure occur. Phenomenon, indicating that the initial adhes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/693D06M13/152D06M13/127D06M11/38D06M11/60B05C3/12B05C11/10B05C13/02D06M101/34
CPCB05C3/12B05C11/10B05C13/02D06M11/38D06M11/60D06M13/127D06M13/152D06M15/693D06M2101/34
Inventor 仵晓李新谷慧平袁书亮闫永强刘晓光郑红莉王圣德寇万宏英克军付宏乐康伟峰张会云邹炳乾张瑞
Owner PINGDINGSHAN SHENMA TIRE CORD FABRIC DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products