Low-smoke, zero-halogen and environment-friendly flame-retardant PVC (polyvinyl chloride) composite

A flame-retardant composite material and environmental protection technology, which is applied in the field of low-smoke halogen-free environmental protection PVC flame-retardant composite materials, can solve the problems of PVC wire and cable pollution, human health hazards, heavy smoke, etc., and achieves good flame retardant function.

Inactive Publication Date: 2016-09-28
陈旭
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there is still a considerable share of domestic wire and cable PVC insulation products. Conventional PVC wires and cables are quite polluted, and a large amount of harmful substances such as dioxin and lead will be pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) Preparation of modified hydromagnesite powder and orthorhombite powder

[0019] Add aluminate modifier F3 to 1250 mesh ultra-fine hydromagnesite powder and orthorhombite powder for dry modification, the modification temperature is 115 ° C ~ 120 ° C, the mass ratio of hydromagnesite powder and orthorhombite powder The ratio is 3:1, and the amount of F3 is 1% of the weight of hydromagnesite powder and orthorhombite powder.

[0020] (2) Raw material formula

[0021] PVC 100 parts;

[0022] DOP 45 copies;

[0023] 35 parts of calcium carbonate;

[0024] 75 parts of modified hydromagnesite powder and orthorhombite powder;

[0025] 5 parts of antimony trioxide;

[0026] FWR-XC (Jingjiang Xuguang Plastic Co., Ltd.) 6 copies;

[0027] 1.4 parts of paraffin;

[0028] IRGANOX MD-1024 0.4 parts.

Embodiment 2

[0030] (1) Preparation of modified hydromagnesite powder and orthorhombite powder

[0031] Add aluminate modifier F-1 to 2500-mesh ultrafine hydromagnesite powder and orthorhombite powder for dry modification. The modification temperature is 115°C to 120°C. The mass ratio is 2:1, and the amount of F-1 is 1.5% of the weight of modified hydromagnesite powder and orthorhombite powder.

[0032] (2) Raw material formula

[0033] PVC 100 parts;

[0034] DOP 55 copies;

[0035] Calcium carbonate 25 parts;

[0036] 85 parts of modified hydromagnesite powder and orthorhombite powder;

[0037] 3 parts of antimony trioxide;

[0038] FWR-J (Jingjiang Xuguang Plastic Co., Ltd.) 8 copies;

[0039] 0.5 parts of stearic acid;

[0040] 1.0 parts of paraffin;

[0041] Naugard XL-I 0.6 parts.

Embodiment 3

[0043] Raw material formula:

[0044] PVC 100 parts;

[0045] DOP 50 copies;

[0046] 30 parts of calcium carbonate;

[0047] 64 parts of hydromagnesite powder;

[0048] 16 parts of orthoclase powder;

[0049] 4 parts of antimony trioxide;

[0050] 7 parts of calcium-zinc composite stabilizer;

[0051] 0.8 parts of stearic acid;

[0052] 0.6 parts of paraffin;

[0053] CL-09-367 0.5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-smoke, zero-halogen and environment-friendly flame-retardant PVC (polyvinyl chloride) composite. The composite is prepared from components of raw materials in parts by weight as follows: 100 parts of PVC, 45-55 parts of DOP (dioctyl phthalate), 25-35 parts of calcium carbonate, 75-85 parts of hydromagnesite powder and huntite powder, 3-5 parts of antimonous oxide, 6-8 parts of a heat stabilizer, 1.4-1.8 parts of a lubricant and 0.4-0.6 parts of a metal deactivator. The prepared low-smoke, zero-halogen and environment-friendly flame-retardant PVC composite has an excellent flame retardant function and cannot affect the mechanical strength of plastics.

Description

technical field [0001] The invention belongs to the technical field of PVC materials, and in particular relates to a low-smoke, halogen-free and environment-friendly PVC flame-retardant composite material. Background technique [0002] At present, domestic wire and cable PVC insulation products still have a considerable share. Conventional PVC wires and cables are quite polluted, and a large amount of harmful substances such as dioxin and lead will be produced during manufacture, use and disposal. When PVC material is burned, it will produce a lot of smoke and harmful HCl gas, which will cause certain harm to human health. After burning and burying, it will cause soil and water pollution. Therefore, how to design flame-retardant wire and cable products that meet low smoke, low toxicity, and low corrosion has become an urgent task for the whole society. Contents of the invention [0003] The purpose of the present invention is to solve the defects and deficiencies in the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L91/06C08K13/06C08K9/04C08K3/26C08K3/22
CPCC08L27/06C08K3/2279C08K3/26C08K9/04C08K13/06C08K2003/265C08K2003/267C08K2201/014C08L2201/02C08L2201/22C08L91/06
Inventor 陈旭
Owner 陈旭
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap