Chestnut shell plant fiber synthetic resin and preparation process thereof

A plant fiber and synthetic resin technology is applied in the field of chestnut shell plant fiber synthetic resin and its preparation technology, which can solve the problems of unfavorable degradation, damage to soil water permeability, and high cost, so as to alleviate resource shortage, increase farmers' income, and reduce production costs. Effect

Inactive Publication Date: 2016-09-28
安徽科邦树脂科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing tableware, furniture, kitchen utensils and other daily necessities on the market are all made of wood, bamboo, ordinary plastics and other products. Pollution" destroys the water permeability of the soil, while wood and bamboo products require deforestation and waste water pollution during the manufacturing process, so they are not very good environmental protection materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of chestnut shell plant fiber synthetic resin, comprising the following raw materials in parts by weight: 30 parts of chestnut shell powder, 5 parts of carboxyethyl cellulose, 15 parts of Arabic resin, 3 parts of adipic acid, 15 parts of cornstarch, 3 parts of diethylene glycol 3 parts of gum powder, 5 parts of polyhydroxybutyrate, 10 parts of polylactic acid fiber;

[0021] Its preparation process comprises the following steps:

[0022] (1), chestnut shells are subjected to ultra-fine grinding processing to obtain fine particle chestnut shell powder;

[0023] (2), put diethylene glycol and adipic acid into the high-speed mixer, add carboxyethyl cellulose and stir evenly to obtain the initial mixed material;

[0024] (3) Put the chestnut shell powder in step (1) into a high-speed mixer and mix it with the primary mixing material in step (2), and add cornstarch at the same time and stir evenly, then cool to room temperature, and pulverize after solidifying into a...

Embodiment 2

[0031] A kind of chestnut shell plant fiber synthetic resin, comprising the following raw materials in parts by weight: 60 parts of chestnut shell powder, 10 parts of carboxyethyl cellulose, 40 parts of Arabic resin, 8 parts of adipic acid, 40 parts of cornstarch, 8 parts of diethylene glycol 8 parts of gum powder, 10 parts of polyhydroxybutyrate, 20 parts of polylactic acid fiber;

[0032] Its preparation process comprises the following steps:

[0033] (1), chestnut shells are subjected to ultra-fine grinding processing to obtain fine particle chestnut shell powder;

[0034] (2), put diethylene glycol and adipic acid into the high-speed mixer, add carboxyethyl cellulose and stir evenly to obtain the initial mixed material;

[0035] (3) Put the chestnut shell powder in step (1) into a high-speed mixer and mix it with the primary mixing material in step (2), and add cornstarch at the same time and stir evenly, then cool to room temperature, and pulverize after solidifying into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of chemical materials, in particular to chestnut shell plant fiber synthetic resin and a preparation process thereof. The resin is prepared from chestnut shell powder, carboxyethyl cellulose, Arabia gum, adipic acid, corn starch, diethylene glycol, balsam powder, polyhydroxybutyrate and polylactic acid fiber. The preparation process comprises the following steps that 1, fine particle chestnut shell powder is prepared; 2, a primary mixed material is prepared; 3, chestnut shell fiber powder is prepared; 4, a mixed additive material is prepared; 5, the mixed additive material and the polylactic acid fiber are stirred to be uniform, blended, extruded and molded in an injection mode to obtain the chestnut shell plant fiber synthetic resin. Crop waste and other resources are prevented from being waste and are sufficiently utilized, and therefore environmental pollution is reduced. The production cost is low, the application range is quite wide, country resource advantages can be exploited to the full, and an effective method and approach is provided for reasonable utilization of waste crops.

Description

technical field [0001] The invention relates to the field of chemical materials, in particular to a chestnut shell plant fiber synthetic resin and a preparation process thereof. Background technique [0002] As a large agricultural country, with the continuous harvest of agriculture, the output of crop straws and other wastes has also increased significantly, of which the output of bare straws is about 650 million t / year. Except for the development and utilization of feed and fertilizer, most of them are burned, which not only wastes resources, but also seriously endangers the natural ecological environment. Therefore, the comprehensive utilization of abandoned crops is of great significance. While human beings create modern civilization, it also brings negative impacts - white pollution. Disposable tableware, disposable plastic products, and agricultural mulch are difficult to recycle, and their treatment methods are mainly incineration and landfill. Incineration will pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L93/00C08L3/02C08L67/04C08K5/092C08K5/06
CPCC08L97/02C08L2201/06C08L2201/08C08L2205/035C08L2205/16
Inventor 袁振洲
Owner 安徽科邦树脂科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com