Preparation method and application of leveling agent for high-temperature and high-pressure dyeing of polyester fibers by disperse dyes

A high-temperature and high-pressure dyeing and polyester fiber technology, applied in the field of textile dyeing and finishing, can solve the problems of unsatisfactory solution of production technical problems, no discovery of new dyeing technology, poor practicability, etc., and achieves reduction of uneven dyeing, Simple process flow and easy-to-achieve effects

Inactive Publication Date: 2016-09-28
XI'AN POLYTECHNIC UNIVERSITY
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the lack of practicability of this research result and many technical problems in production, it has not been satisfactorily resolved, so far there has been no report of its application in actual production.
[0007] To sum up, for disperse dyeing, a feasible new dyeing technology with deep water saving and emission reduction has not been found at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of leveling agent for high-temperature and high-pressure dyeing of polyester fibers by disperse dyes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] The preparation method of the leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers with disperse dyes is specifically implemented according to the following steps:

[0063] Take the following raw materials respectively according to mass percentage:

[0064] Fatty alcohol polyoxyethylene ether 3%, sodium alkylsulfonate 4%, sodium alkyl sulfate 6%, fatty amine polyoxyethylene ether 5%, urea 20%, purified water 62%, the total content of the above components is 100%;

[0065] Heat the clean water to 25°C; add the weighed fatty alcohol polyoxyethylene ether, sodium alkyl sulfonate, sodium alkyl sulfate, fatty amine polyoxyethylene ether and urea into the pure water at 25°C, stir After homogenization, the high-temperature and high-pressure dyeing leveling agent XDR for polyester fiber with disperse dyes is obtained;

[0066] The method for dyeing polyester fiber and its blended products by using disperse dye polyester fiber high-temperature a...

Embodiment 2

[0070] The preparation method of the leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers with disperse dyes is specifically implemented according to the following steps:

[0071] Take the following raw materials respectively according to mass percentage:

[0072] 4% of fatty alcohol polyoxyethylene ether, 3% of sodium alkylsulfonate, 5% of sodium alkyl sulfate, 2% of fatty amine polyoxyethylene ether, 25% of urea, and 61% of purified water. The total content of the above components is 100%;

[0073] Heat the clean water to 30°C; add the weighed fatty alcohol polyoxyethylene ether, sodium alkyl sulfonate, sodium alkyl sulfate, fatty amine polyoxyethylene ether and urea into the purified water at 30°C, stir After homogenization, the high-temperature and high-pressure dyeing leveling agent XDR for polyester fiber with disperse dyes is obtained;

[0074] The method for dyeing polyester fiber and its blended products by using disperse dye polyeste...

Embodiment 3

[0078] The preparation method of the leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers with disperse dyes is specifically implemented according to the following steps:

[0079] Take the following raw materials respectively according to mass percentage:

[0080] 4.5% fatty alcohol polyoxyethylene ether, 3.5% sodium alkylsulfonate, 4.5% sodium alkyl sulfate, 1.5% fatty amine polyoxyethylene ether, 30% urea, 56% pure water, the total content of the above components is 100%;

[0081] Heat the clean water to 28°C; add the weighed fatty alcohol polyoxyethylene ether, sodium alkyl sulfonate, sodium alkyl sulfate, fatty amine polyoxyethylene ether and urea into the purified water at 28°C, stir After homogenization, the high-temperature and high-pressure dyeing leveling agent XDR for polyester fiber with disperse dyes is obtained;

[0082] The method for dyeing polyester fiber and its blended products by using disperse dye polyester fiber high-tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and application of a leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers by disperse dyes. The preparation method is mainly characterized in that fatty alcohol-polyoxyethylene ether, alkyl sodium sulfonate, alkyl sulfate sodium, fatty amine polyoxyethylene ether, urea and purified water are uniformly mixed to obtain the leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers by disperse dyes. The invention also discloses a method for dyeing polyester fibers and polyester fiber blended products by use of the leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers by disperse dyes. After adoption of the prepared leveling agent XDR for high-temperature and high-pressure dyeing of polyester fibers by disperse dyes, the oriented adsorption density of surfactant molecules on the surfaces of disperse dyes particles is remarkably improved, the interfacial tension between the dye particles and water and the average grain diameters of the dyes particles are obviously reduced, the solubility of the dyes and the dyeing percentage of the dyes to the fibers are remarkably improved, and agglomeration of the dyes and nonuniform dyeing can be dramatically reduced.

Description

technical field [0001] The invention belongs to the technical field of textile dyeing and finishing, and specifically relates to a preparation method of a high-temperature and high-pressure dyeing leveling agent XDR for polyester fibers with disperse dyes. And its application in the dyeing process of blended products. Background technique [0002] When disperse dyes are used to dye polyester fibers and their blended products, there are usually problems of poor level dyeing and relatively low dyeing percentage of the fibers, and these problems often easily lead to unqualified dyeing quality and low dye utilization rate. Not high and dyeing wastewater CODcr higher consequences. [0003] In the production process of commercial disperse dyes, in order to ensure fine and uniform dye particles and dispersion stability under high temperature conditions in the dye bath, dispersants with anionic surfactants as the main body are often added. [0004] In the dyeing process, in order ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/16D06P1/649D06P1/607D06P1/613D06P1/62D06P3/54D06P3/82
CPCD06P1/16D06P1/6076D06P1/6131D06P1/623D06P1/6497D06P3/004D06P3/54D06P3/82
Inventor 邢建伟徐成书沈兰萍曹贻儒欧阳磊苏广召赵航周梦宇刘刚中李世朋王培王志刚
Owner XI'AN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More