Transfer Coated Inkjet Printing High Gloss Photo Paper

An inkjet printing, high-gloss technology, applied in coating, printing, papermaking, etc., can solve the problems of photo paper performance to be improved, low production efficiency, environmental protection burden, etc., to reduce fixed costs, increase production speed, Environmentally friendly and good effect

Active Publication Date: 2017-07-07
ZHEJIANG JUNMA DIGITAL TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since the advent of inkjet printing photo technology, the photo paper for inkjet printing has been produced by the traditional casting coating method. When using the traditional casting coating technology to produce high-gloss photo paper, the casting coating machine can only be produced at a slow speed due to the limitation of the casting coating method. In addition, during the production process, part of the wastewater with paint is discharged, the production efficiency is low, the production cost is high, and the wastewater discharge also poses a burden on environmental protection
[0003] CN103129202B (2014-4-16) discloses a kind of polyvinyl alcohol image photographic paper, yet the performance of this photographic paper still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transfer Coated Inkjet Printing High Gloss Photo Paper
  • Transfer Coated Inkjet Printing High Gloss Photo Paper
  • Transfer Coated Inkjet Printing High Gloss Photo Paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] 1. When preparing the primer coating, add light calcium carbonate at a ratio of 25% to 75% deionized water to start the dispersing machine. During the dispersion process, add 0.6% polycarboxylate sodium salt dispersant, and then add in order after dispersing for 20 minutes. Add 6% polyvinyl acetate emulsion adhesive, 8% polyvinyl alcohol glue, and 0.3% color fixing agent Y. After adding all of them, continue stirring for 15 minutes to complete the preparation.

[0057] 2. The preparation of the top coating is to use water-based silica sol as the main body, add 12% of polyvinyl alcohol glue with a solid content of 10%, and 0.2% of color-fixing agent Y, stir well and set aside.

[0058] 3. Preparation of back-coating paint Add 3% polyvinyl alcohol to 95% deionized water, stir and disperse fully, then turn on steam and heat to gelatinize under continuous stirring state, heat gelatinization time for 30 minutes, the colloid is colorless and transparent. OK, cool to room temp...

Embodiment 2

[0063] The primer coating includes light calcium carbonate, polycarboxylate sodium salt dispersant, polyvinyl acetate emulsion adhesive, polyvinyl alcohol glue and color fixing agent;

[0064] Topcoat coatings include water-based silica sol and polyvinyl alcohol glue;

[0065] Backcoat paints include polyvinyl alcohol.

[0066] The formula of primer coating comprises by following parts by weight: 26 parts of light calcium carbonate, 73 parts of deionized water, 0.5 part of polycarboxylate sodium salt type dispersant, 5 parts of polyvinyl acetate emulsion adhesive, polyvinyl alcohol glue 8 parts, 0.5 parts of color fixing agent.

[0067] The preparation method of the primer coating is: adding light calcium carbonate to deionized water according to the above weight parts, adding polycarboxylate sodium salt type dispersant during the dispersion process of starting the disperser, and adding polyvinyl acetate in sequence after dispersing for 20 minutes The emulsion adhesive, poly...

Embodiment 3

[0072] The primer coating includes light calcium carbonate, polycarboxylate sodium salt dispersant, polyvinyl acetate emulsion adhesive, polyvinyl alcohol glue and color fixing agent;

[0073] Topcoat coatings include water-based silica sol and polyvinyl alcohol glue;

[0074] Backcoat paints include polyvinyl alcohol.

[0075] The formula of primer coating comprises by following parts by weight: 28 parts of light calcium carbonate, 72 parts of deionized water, 0.9 part of polycarboxylate sodium salt type dispersant, 8 parts of polyvinyl acetate emulsion adhesive, polyvinyl alcohol glue 11 parts, 0.6 parts of color fixing agent.

[0076] The preparation method of the primer coating is: adding light calcium carbonate to deionized water according to the weight part, adding polycarboxylate sodium salt type dispersant during the dispersion process of starting the disperser, and then adding polyvinyl acetate emulsion in turn after dispersing for 25 minutes Adhesive, 11 parts of p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a paper and especially relates to a transfer coating ink-jet printing high-gloss photographic paper. The paper comprises a surface coating, a base coating, a raw paper layer and a back coating. The surface coating is an ink absorption water-resistant gloss coating. The base coating is an ink absorption fixation coating. The back coating is a water-resistant coating for balancing two surface tensions of a photographic paper. The base coating comprises light calcium carbonate, a sodium polycarboxylate dispersant, a polyvinyl acetate emulsion adhesive, a polyvinyl alcohol glue solution and a fixer. The surface coating comprises aqueous silica sol and a polyvinyl alcohol glue solution. The back coating comprises polyvinyl alcohol. The photographic paper surface is a high-gloss mirror surface, images obtained by color ink-jet printing have plump colors and realizes real restoration and ink absorption and fixing performances are good.

Description

technical field [0001] The invention relates to a paper, in particular to a high-gloss photographic printing paper for transfer coating and inkjet printing. Background technique [0002] Since the advent of inkjet printing photo technology, the photo paper for inkjet printing has been produced by the traditional casting coating method. When using the traditional casting coating technology to produce high-gloss photo paper, the casting coating machine can only be produced at a slow speed due to the limitation of the casting coating method. In addition, during the production process, part of the wastewater with paint is discharged, the production efficiency is low, the production cost is high, and the wastewater discharge also poses a burden on environmental protection. [0003] CN103129202B (2014-4-16) discloses a polyvinyl alcohol imaging paper, but the performance of the paper still needs to be improved. Contents of the invention [0004] The object of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H19/14D21H19/20D21H19/26D21H21/16B41M5/52
CPCB41M5/5254B41M5/5263D21H19/14D21H19/20D21H19/26D21H21/16
Inventor 夏建国
Owner ZHEJIANG JUNMA DIGITAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com