Liquid dhydrophilic glass film, hydrophilic glass, and preparation method of liquid hydrophilic glass and hydrophilic glass
A glass membrane, hydrophilic technology, applied in chemical instruments and methods, coatings, inorganic chemistry, etc., can solve the problems of poor glass substrate bonding, short duration, high cost, low cost, lasting and stable effect, and long life. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example 1
[0026] (1) Add 0.5 mL of trimethoxy mercaptopropyl silane to 5 mL of ethyl orthosilicate and stir for 5 hours, then add 50 mL of ethanol and stir for 2 days to obtain a uniform and transparent solution;
[0027] (2) Add 5 mL of water to the solution in step (1) and stir for 5 days to obtain SiO containing sulfhydryl groups 2 Sol, that is, liquid hydrophilic glass film;
[0028] (3) Spray the above-mentioned liquid hydrophilic glass film on the glass surface, and obtain hydrophilic glass after drying. The glass film on the surface of the hydrophilic glass is uniform, transparent, and flat without cracks.
Example Embodiment
[0029] Example 2
[0030] (1) Add 0.25 mL of trimethoxymercaptopropyl silane to 5 mL of methyl orthosilicate and stir for 5 hours, then add 50 mL of ethanol and stir for 2 days to obtain a uniform and transparent solution;
[0031] (2) Add 5.5 mL of water to the solution in step (1) and stir for 5 days to obtain SiO containing sulfhydryl groups 2 Sol, that is, liquid hydrophilic glass film;
[0032] (3) Spin coating the above liquid hydrophilic glass film on the glass surface, and obtain hydrophilic glass after drying. The glass film on the surface of the hydrophilic glass is uniform, transparent, and flat without cracks.
Example Embodiment
[0033] Example 3
[0034] (1) Add 0.75 mL of trimethoxy mercaptopropyl silane to 5 mL of propyl orthosilicate and stir for 5 hours, then add 50 mL of ethanol and stir for 2 days to obtain a uniform and transparent solution;
[0035] (2) Add 4 mL of water to the solution in step (1) and stir for 5 days to obtain SiO containing sulfhydryl groups 2 Sol, that is, liquid hydrophilic glass film;
[0036] (3) Spray the above-mentioned liquid hydrophilic glass film on the glass surface, and obtain hydrophilic glass after drying. The glass film on the surface of the hydrophilic glass is uniform, transparent, and flat without cracks.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology