Medical-fabric special treating liquid

A technology for treating liquids and fabrics, applied in fiber treatment, anionic surface active compounds, cationic surface active compounds, etc. It can solve the problems that the treatment liquid cannot meet the market demand, and achieve strong oxidation resistance, low volatility, and enhanced bonding sexual effect

Inactive Publication Date: 2016-10-12
广德毅维纺织有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current treatment flu...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A special treatment solution for medical fabrics, comprising the following raw materials in parts by weight: 45 parts of glycerin, 15 parts of white vinegar, 11 parts of nano-activated carbon, 11 parts of nano-titanium dioxide, 2 parts of imidazoline laurate, 7 parts of behenic acid, and aloe leaves 7 parts of extract, 2 parts of hyperbranched quaternary ammonium salt, 2 parts of isopropyl palmitate, 12 parts of modified preparation;

[0015] The modified preparation is made of the following raw materials in parts by weight: 6 parts of ψ-glucosterol, 6 parts of p-cymephyllin, 6 parts of orientin, 0.4 part of Prunella vulgaris polysaccharide, kaempferol-7 0.4 parts of -glucose-3-glucogalactoside, 12 parts of tea polyphenols, 1 part of N-isobutyltetradecenamide, and 12 parts of methyl eugenol; the preparation method is to mix and grind each raw material after drying Crush into fine powder.

[0016] A method for preparing a special treatment liquid for medical fabrics, co...

Embodiment 2

[0021] A special treatment solution for medical fabrics, comprising the following raw materials in parts by weight: 42 parts of glycerin, 12 parts of white vinegar, 8 parts of nano-activated carbon, 8 parts of nano-titanium dioxide, 1 part of imidazoline laurate, 5 parts of behenic acid, and aloe leaves 5 parts of extract, 1 part of hyperbranched quaternary ammonium salt, 1 part of isopropyl palmitate, 9 parts of modified preparation;

[0022] The modified preparation is made of the following raw materials in parts by weight: 4 parts of ψ-glucosterol, 4 parts of p-cymephyllin, 4 parts of orientin, 0.3 part of Prunella vulgaris polysaccharide, kaempferol-7 0.3 parts of -glucose-3-glucogalactoside, 10 parts of tea polyphenols, 1 part of N-isobutyltetradecenamide, and 10 parts of methyl eugenol; the preparation method is to mix and grind each raw material after drying Crush into fine powder.

[0023] A method for preparing a special treatment liquid for medical fabrics, comprisi...

Embodiment 3

[0028] A special treatment liquid for medical fabrics, comprising the following raw materials in parts by weight: 48 parts of glycerin, 17 parts of white vinegar, 14 parts of nano-activated carbon, 14 parts of nano-titanium dioxide, 3 parts of imidazoline laurate, 9 parts of behenic acid, and aloe leaves 9 parts of extract, 3 parts of hyperbranched quaternary ammonium salt, 3 parts of isopropyl palmitate, 14 parts of modified preparation;

[0029] The modified preparation is made of the following raw materials in parts by weight: 8 parts of ψ-glucosterol, 8 parts of p-cymenol, 8 parts of orientin, 0.6 part of Prunella vulgaris polysaccharide, kaempferol-7 0.6 parts of -glucose-3-glucogalactoside, 15 parts of tea polyphenols, 2 parts of N-isobutyltetradecenamide, and 15 parts of methyl eugenol; the preparation method is to mix and grind each raw material after drying Crush into fine powder.

[0030] A method for preparing a special treatment liquid for medical fabrics, compris...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a medical-fabric special treating liquid. The medical-fabric special treating liquid is prepared from, by weight, 42-48 parts of glycerol, 12-17 parts of white vinegar, 8-14 parts of nanometer active carbon, 8-14 parts of nanometer titanium dioxide, 1-3 parts of lauric acid imidazoline, 5-9 parts of hexacosanoic acid, 5-9 parts of aloe leaf extracting liquid, 1-3 parts of hyperbranched quaternary ammonium salt, 1-3 parts of isopropyl palmitate and 9-14 parts of modified preparation. According to the medical-fabric special treating liquid, the stability is good, the volatilization rate is low, mildew is not bred, the oxidation resistance is high, the bonding performance of fabric fibers can be enhanced, the treating liquid is free of performance changing at the high temperature, is free of reaction under irradiation of ultraviolet rays, and can also serve as cleaning liquid of medical fabric, germs can be completely killed, and decoloring of the fabric is avoided.

Description

technical field [0001] The invention relates to the technical field of textile fabric treatment, in particular to a special treatment liquid for medical fabrics. Background technique [0002] Hospital curtains, curtains, surgical gowns, carpets and many other places need to use fabrics. The fabrics used in hospitals must meet medical grades, such as anti-mold and anti-bacteria requirements. After the medical fabric is woven, it generally needs to be soaked in a special treatment solution to make the fabric meet the medical grade. However, the current treatment fluid is difficult to meet the market demand. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a special treatment liquid for medical fabrics. The treatment liquid has good stability, low volatility, no mold growth, strong oxidation resistance, and can enhance the cohesiveness of fabric fibers. Invariant, does not react under strong ultraviolet radiation, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/148D06M13/188D06M11/74D06M11/46D06M13/352D06M13/00D06M13/46D06M13/224C11D1/94C11D3/48C11D3/60C11D3/382
CPCD06M13/148C11D1/04C11D1/62C11D1/667C11D1/88C11D1/94C11D3/12C11D3/1213C11D3/187C11D3/2027C11D3/2065C11D3/2068C11D3/2079C11D3/2096C11D3/221C11D3/222C11D3/32C11D3/382C11D3/48D06M11/46D06M11/74D06M13/00D06M13/188D06M13/224D06M13/352D06M13/46
Inventor 王建谊
Owner 广德毅维纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap