Antistatic flame-retardant PE pipe and preparation method thereof

An antistatic and antistatic agent technology, applied in the field of antistatic flame retardant PE pipe and its preparation, can solve the problems of low pressure resistance and impact resistance, flammability, etc., achieve small conveying resistance, improve conveying capacity, and save corrosion and descaling costs

Inactive Publication Date: 2016-10-26
SANTEH PIPE & FITTINGNANTONG CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, plastic pipes are very prone to static electricity, and the accumulation of static electricity may lead to static spark discharge, which may become an ignition source for underground coal dust or gas explosions; plastic pipes also have the disadvantages of flammability, low pressure resistance and low impact resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1: Decabromodiphenyl ether (DBDPO): 5%, red phosphorus-MgO: 1%, conductive carbon black: 5%, PE base material: 89%.

Embodiment 2

[0020] Example 2: Decabromodiphenyl ether (DBDPO): 4.5%, red phosphorus-MgO: 0.5%, conductive carbon black: 4%, PE base material: 91%.

Embodiment 3

[0021] Example 3: Decabromodiphenyl ether (DBDPO): 6%, red phosphorus-MgO: 1%, conductive carbon black 6%, PE base material 87%.

[0022] Concentrate the auxiliary components in the formula first to make a double-antibody masterbatch, then mix the masterbatch and resin in proportion, and then extrude and granulate through a twin-screw extruder; the granulation processing temperature (°C) as shown in the table below:

[0023] District I

[0024] Melt pressure: 0.15MPa, host speed: 40HZ; feeding speed: 18HZ;

[0025] The extrusion process temperature (°C) is shown in the table below:

[0026]

[0027] The antistatic and flame retardant properties of the present invention are in line with national standards, and are suitable for underground flammable and explosive specific places. They are light in weight, easy to install, and have low pipe density. / 3, so the polyethylene pipes used in coal mines are convenient to transport and install, and can greatly redu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antistatic flame-retardant PE pipe and a preparation method thereof. The PE pipe is prepared from 4-6% of fire retardant, 0.5-1.5% of auxiliary flame retardant, 4-6% of antistatic agent and 86-91% of PE base material. The auxiliary components in the formula are concentrated first to prepare dual-resistance master batch, then the master batch is mixed with body resin in proportion, and then the materials are extruded and granulated through a twin-screw extruder. The PE pipe has the advantages of being good in ageing resistance and not prone to embrittlement, having good toughness and impact energy absorption, and being good in rapid crack resistance and corrosion resistance, free of scaling, smooth in inner wall and capable of improving the conveying capacity by 30%.

Description

technical field [0001] The invention relates to a pipe material, in particular to an antistatic flame retardant PE pipe and a preparation method thereof. Background technique [0002] At present, traditional mining pipes mainly use steel pipes, cast iron pipes, plastic pipes and glass steel pipes. Due to material problems, steel pipes and cast iron pipes are likely to collide underground and generate sparks, causing the risk of gas explosions; glass steel pipes are easily damaged by impact; plastic pipes are acid-resistant, alkali-resistant, oil-resistant, corrosion-resistant, light in weight, low in cost, and service The advantages of long service life (about 2.5 times that of steel) are unmatched by steel pipes. However, plastic pipes are extremely prone to static electricity, and the accumulation of static electricity may lead to static spark discharge, which may become an ignition source for underground coal dust or gas explosions; plastic pipes also have the disadvanta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K13/02C08K5/06C08K3/02C08K3/22C08K3/04
CPCC08K13/02C08K3/02C08K3/04C08K3/22C08K5/06C08K2003/026C08K2003/222C08K2201/001C08K2201/017C08L2201/02C08L2201/04C08L2203/18C08L23/06
Inventor 汪柯柯王杰
Owner SANTEH PIPE & FITTINGNANTONG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap