Precious metal glazed artistic ceramics and manufacturing method thereof

A technique for artistic ceramics and a production method, applied in the field of ceramic manufacturing, can solve the problems of high production cost and single glaze effect, and achieve the effects of long-lasting luster, safe use and good stability

Active Publication Date: 2018-10-30
QUANZHOU SUNSHINE CREATIVE CERAMICS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the glaze surface of this imitation metal ceramic art glaze has a mirror effect, its color can only reflect golden yellow, while precious metals also have silver, white gold, purple gold, copper red and other colors in addition to golden yellow. Artistic glaze has a single glaze effect and high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0024] The glaze composition of precious metal glazed artistic ceramics is as follows: 49 parts of lead-free frit, 6 parts of calcite, 6 parts of kaolin, 7 parts of quartz, 9 parts of iron yellow, MnO 2 6 parts, NiO 2 parts, Al 2 o 3 3 parts, CrO 3 1 part, ZrSiO 4 2 copies, V 2 o 5 5 parts, CuO 1 part, TiO 2 2.5 copies, CMC 0.5 copies;

[0025] The composition of the lead-free frit is as follows: 42 parts of potassium feldspar, 18 parts of zinc oxide, 6 parts of quartz, 7 parts of calcite, 6 parts of barium carbonate, Al 2 o 3 5 copies, WO 3 6 copies, K 2 O 3 parts, Na 2 O 2 parts, Li 2 O 5 copies.

[0026] The base color of the fired precious metal glazed artistic ceramics in this embodiment is golden yellow, the glazed surface has a strong metallic luster, the glazed surface is smooth, mirror-reflected, the luster is long-lasting, and has good stability. The precious metal glaze art ceramic glaze does not contain lead and chromium, so it is safe to use. ...

specific Embodiment 2

[0027] The glaze composition of precious metal glazed artistic ceramics is as follows: 53 parts of lead-free frit, 5 parts of calcite, 8 parts of kaolin, 6 parts of quartz, 5 parts of iron yellow, MnO 2 5 parts, NiO 1 part, Al 2 o 3 3 parts, CrO 3 4 parts, ZrSiO 4 2 copies, V 2 o 5 1 part, CuO 5 parts, TiO 2 1 copy, 1 copy of CMC;

[0028] The composition of the lead-free frit is as follows: 36 parts of potassium feldspar, 16 parts of zinc oxide, 7 parts of quartz, 8 parts of calcite, 8 parts of barium carbonate, Al 2 o 3 8 copies, WO 3 7 copies, K 2 O 3 parts, Na 2 O 2 parts, Li 2 O 5 copies.

[0029] The base color of the precious metal glazed art ceramic fired in this embodiment is gold and silver, the glaze effect has a strong metallic luster, the glaze is smooth, mirror reflection, the luster is long-lasting, and has good stability. The precious metal glaze art ceramic glaze does not contain lead and chromium, so it is safe to use.

specific Embodiment 3

[0030] The glaze composition of precious metal glazed artistic ceramics is as follows: 62 parts of lead-free frit, 5 parts of calcite, 5 parts of kaolin, 5 parts of quartz, 8 parts of iron yellow, MnO 2 5 parts, NiO 2 parts, Al 2 o 3 2 parts, CrO 3 1 part, ZrSiO 4 1 copy, V 2 o 5 1 part, CuO 1 part, TiO 2 1 copy, 1 copy of CMC;

[0031] The composition of the lead-free frit is as follows: 40 parts of potassium feldspar, 16 parts of zinc oxide, 8 parts of quartz, 7 parts of calcite, 4 parts of barium carbonate, Al 2 o 3 9 copies, WO 3 7 copies, K 2 O 3 parts, Na 2 O 3 parts, Li 2 O 3 parts.

[0032] The base color of the fired precious metal glazed artistic ceramics in this embodiment is grayish black, the glazed surface has a strong metallic luster, the glazed surface is smooth, mirror-reflected, the luster is long-lasting, and has good stability. The precious metal glaze art ceramic glaze does not contain lead and chromium, so it is safe to use.

[0033]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the technical field of ceramic manufacturing, and relates to a precious metal glaze artistic ceramic and manufacturing method thereof. The precious metal glaze artistic ceramic uses glazes of lead-free frit, calcite, kaolin, quartz, goethite, MnO2, NiO, Al2O3, CrO3, ZrSiO4, V2O5, CuO, TiO2 and CMC. Through the unique production and firing processes, the produced precious metal glaze artistic ceramic has strong metallic luster glaze effect; the formula can be adjusted to make the glaze in metal colors such as gold, silver and grey black; the glaze is smooth, has specular reflection, lasting gloss and good stability. In addition, the precious metal artistic ceramic does not contain lead or chromium, and is safe to use.

Description

technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to a precious metal glazed artistic ceramic and a manufacturing method thereof. Background technique [0002] Precious metals such as gold, silver, titanium and other precious metals are polished to a bright mirror surface. The combination of this mirror effect and ceramic materials has a unique artistic effect. The existing precious metal mirrors on ceramic surfaces are usually obtained by electroplating. However, the effect of electroplating is too bright and deviates from the standard gold / silver color, which is far behind the real precious metal mirror. In addition, the cost of ceramic electroplating is high, and the products obtained after electroplating have high heavy metal content, which cannot be used as daily-use ceramics. [0003] In order to solve the above problems, the application publication number is CN 104496555 A cermet-like art glaze and its preparat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/20C03C8/04C04B41/86
CPCC03C8/04C03C8/20C04B41/5022C04B41/86
Inventor 毛录贵郑金鼎
Owner QUANZHOU SUNSHINE CREATIVE CERAMICS CO LTD