A kind of silk fiber and flax fiber blended woven fabric

A silk fiber, flax fiber technology, applied in textile, fiber processing, plant fiber and other directions, can solve the problems of poor flax feel, poor silk moisture absorption and air permeability, etc., and achieve the effect of novel appearance and high wearing performance.

Active Publication Date: 2018-01-26
JIANGSU HUAXIN LINEN TEXTILE
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The problem to be solved by the present invention is to propose an innovative solution for the above-mentioned shortcomings in the prior art, especially a solution that can effectively solve the problems of flax with poor hand feeling and silk with poor moisture absorption and air permeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: a kind of silk fiber and flax fiber blended woven fabric, the weight content of described flax fiber is 40-85%, the rest is silk fiber, and its preparation comprises the following steps:

[0027] Step 1, pretreatment: loosely stack the flax fibers and silk fibers separately, mix the cotton and linen finishing agent with water and spray evenly on the flax fibers, use the pretreatment agent to evenly spray on the silk fibers, and seal the piles separately set;

[0028] Step 2, flax high-count yarn: the flax fiber and water-soluble vinylon roving are fed together on a wet-spinning frame to achieve mixing to obtain flax / water-soluble vinylon blended yarn; the blended yarn is boiled in aqueous solution A, Dissolve and remove vinylon fiber to obtain flax high-count yarn;

[0029] Step 3, degumming: immerse the high-count flax yarn obtained in step 2 in the compound enzyme solution, keep the temperature of the compound enzyme solution at 45-55 degrees Celsius, t...

Embodiment 2

[0038] Embodiment 2: a kind of silk fiber and flax fiber blended woven cloth, the weight content of described flax fiber is 65%, and the rest is silk fiber, and its preparation comprises the following steps:

[0039] Step 1, pretreatment: loosely stack the flax fibers and silk fibers separately, mix the cotton and linen finishing agent with water and spray evenly on the flax fibers, use the pretreatment agent to evenly spray on the silk fibers, and seal the piles separately set;

[0040] Step 2, flax high-count yarn: the flax fiber and water-soluble vinylon roving are fed together on a wet-spinning frame to achieve mixing to obtain flax / water-soluble vinylon blended yarn; the blended yarn is boiled in aqueous solution A, Dissolve and remove vinylon fiber to obtain flax high-count yarn;

[0041] Step 3, degumming: immerse the high-count flax yarn obtained in step 2 in the compound enzyme solution, keep the temperature of the compound enzyme solution at 45-55 degrees Celsius, t...

Embodiment 3

[0050] Embodiment 3: a kind of silk fiber and flax fiber blended woven cloth, the weight content of described flax fiber is 40-85%, the rest is silk fiber, and its preparation comprises the following steps:

[0051] Step 1, pretreatment: loosely stack the flax fibers and silk fibers separately, mix the cotton and linen finishing agent with water and spray evenly on the flax fibers, use the pretreatment agent to evenly spray on the silk fibers, and seal the piles separately set;

[0052] Step 2, flax high-count yarn: the flax fiber and water-soluble vinylon roving are fed together on a wet-spinning frame to achieve mixing to obtain flax / water-soluble vinylon blended yarn; the blended yarn is boiled in aqueous solution A, Dissolve and remove vinylon fiber to obtain flax high-count yarn;

[0053] Step 3, degumming: immerse the high-count flax yarn obtained in step 2 in the compound enzyme solution, keep the temperature of the compound enzyme solution at 50 degrees Celsius, take ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a blended woven fabric of silk fiber and flax fiber. The weight content of the flax fiber is 40-85%, and the rest is silk fiber. The preparation includes: pretreatment, flax high-count yarn, degummed silk fiber high-count yarn , roving, bleaching, pickling, washing, spinning and weaving. The wet spinning process provided by the present invention can prepare silk fiber and flax fiber blended woven fabric with excellent performance, and the silk fiber and flax fiber blended woven fabric woven by the method of the present invention has the advantages of both silk fiber and flax fiber, and has excellent wearability. high. The silk fiber and flax fiber blended woven fabric woven by the method of the invention has the characteristics of softness, comfort, ventilation, sweat absorption, antibacterial, etc., and has a novel and fashionable appearance.

Description

technical field [0001] The invention relates to the textile field, in particular to a silk fiber and flax fiber blended woven fabric. Background technique [0002] The main components of hemp are cellulose, lignin, hemicellulose, pectin and so on. The biggest difference between hemp products and other natural cellulose textiles is that degumming is required. The degumming process has a great impact on the quality of hemp, and it is also one of the research topics that the hemp industry has devoted itself to in recent years. The traditional degumming process is mainly based on chemical degumming, that is, the chemical reagents that can dissolve pectin are used to boil the hemp fiber for a long time to remove the gum. The treatment of large volumes of degumming wastewater puts great pressure on the environment and costs. Taking Hubei as an example, Hubei Province has an annual output of more than 4,000 tons of flax and dry hemp. There are 5 degumming production enterprises, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D02G3/04D06B3/04D06L4/13D06M11/56D06M11/71D06M16/00D06M101/04D06M101/10D03D15/217D03D15/233D03D15/47D03D15/50
CPCD02G3/042D03D15/00D06B3/04D06M11/56D06M11/71D06M16/003D06M2101/10D06M2101/04D10B2211/04D10B2201/04D03D15/47
Inventor 王雅琴薛茂深
Owner JIANGSU HUAXIN LINEN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More