Frost-resistant concrete

A technology of concrete and antifreeze, applied in the field of concrete, can solve the problems of difficulty in ensuring building quality, difficulty in construction, delay in construction period, etc., and achieve the effects of abundant raw materials, good durability and low cost

Inactive Publication Date: 2016-11-16
许偏奎
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In winter in alpine areas, in order to ensure the quality of building materials and construction quality, it is generally difficult to carry out building construction in w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of frost-resistant concrete, its composition by mass is as follows: 100 parts of cement, 50 parts of fine aggregate sand, 50 parts of coarse aggregate sand, 10 parts of glass fiber, 1 part of dispersible latex powder, 12 parts of nano silicon dioxide powder, 5 parts of calcium lignosulfonate, 3.6 parts of basic magnesium sulfate whiskers, 5.4 parts of sodium carboxymethylcellulose, 8 parts of antifreeze, 2.8 parts of water reducing agent, 3.6 parts of concrete modifier, 3.6 parts of air-entraining agent .

[0021] Among them, the composition of the antifreeze agent is as follows: 10 parts of sodium sulfate, 1.8 parts of sodium water reducer, 2.4 parts of sodium citrate, 3.8 parts of sodium chloride, and 10 parts of seaweed colloid A2.

[0022] Among them, the water reducer is a mixture of sodium lignosulfonate and sodium naphthalenesulfonate, and the mass ratio is 1:1.1.

[0023] Among them, the concrete modifier is a mixture of carbon nanotubes and acrylic emul...

Embodiment 2

[0026] A kind of antifreeze concrete, its mass parts composition is as follows: 120 parts of cement, 60 parts of fine aggregate sand, 60 parts of coarse aggregate sand, 20 parts of glass fiber, 12 parts of dispersible latex powder, 15 parts of nano silicon dioxide powder, 7 parts of calcium lignosulfonate, 6 parts of basic magnesium sulfate whiskers, 6.4 parts of sodium carboxymethyl cellulose, 9 parts of antifreeze, 3.2 parts of water reducing agent, 4 parts of concrete modifier, 4 parts of air-entraining agent .

[0027] Among them, the composition of the antifreeze agent is as follows: 12 parts of sodium sulfate, 2.4 parts of sodium water reducer, 3 parts of sodium citrate, 4.2 parts of sodium chloride, and 12 parts of seaweed colloid A2.

[0028] Among them, the water reducer is a mixture of sodium lignosulfonate and sodium naphthalenesulfonate, and its mass ratio is 1:1.2.

[0029] Among them, the concrete modifier is a mixture of carbon nanotubes and acrylic emulsion, a...

Embodiment 3

[0032] A kind of antifreeze concrete, its mass parts composition is as follows: 150 parts of cement, 80 parts of fine aggregate sand, 80 parts of coarse aggregate sand, 35 parts of glass fiber, 20 parts of dispersible latex powder, 18 parts of nano silicon dioxide powder, 8 parts of calcium lignosulfonate, 6.8 parts of basic magnesium sulfate whiskers, 8 parts of sodium carboxymethyl cellulose, 12 parts of antifreeze, 4.5 parts of water reducing agent, 5.8 parts of concrete modifier, 6.2 parts of air-entraining agent .

[0033] Wherein, the antifreezing agent is composed in parts by mass as follows: 15 parts of sodium sulfate, 3.6 parts of sodium water reducer, 4.2 parts of sodium citrate, 6.2 parts of sodium chloride, and 15 parts of seaweed colloid A2.

[0034] Among them, the water reducing agent is a mixture of sodium lignosulfonate and sodium naphthalenesulfonate, and its mass ratio is 1:1.3.

[0035] Among them, the concrete modifier is a mixture of carbon nanotubes and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of concrete, especially a kind of antifreeze concrete; its composition by mass is as follows: 100-200 parts of cement, 50-100 parts of fine aggregate sand, 50-100 parts of coarse aggregate sand, 10-60 parts of glass fiber 10-30 parts of dispersible latex powder, 12-25 parts of nano-silica powder, 5-12 parts of calcium lignosulfonate, 3.6-10 parts of basic magnesium sulfate whiskers, 5.4-10 parts of sodium carboxymethyl cellulose 10.8 parts, 8-16 parts of antifreeze agent, 2.8-6.4 parts of water reducing agent, 3.6-8 parts of concrete modifier, 3.6-9 parts of air-entraining agent; the antifreeze concrete of the present invention has abundant raw materials, low price, low cost In addition, it has the characteristics of good frost resistance, high compressive strength, good durability, and a wide range of strength grades. The concrete of the invention can be widely used in shipbuilding industry, machinery industry, ocean development, geothermal engineering and the like.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to frost-resistant concrete. Background technique [0002] Concrete has also become the material of choice for roads, dams, and bridges, as industrial development and urbanization accelerate. [0003] In winter in alpine regions, in order to ensure the quality of building materials and construction quality, it is generally difficult to carry out building construction in winter, which not only delays the construction period, but also makes it difficult to ensure the quality of the building even if the construction is forced, causing safety hazards. Contents of the invention [0004] The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art and provide a frost-resistant concrete with good anti-freeze effect and low use cost. [0005] In order to solve the problems of the technologies described above, the technical scheme adopted i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B111/20
CPCC04B28/00C04B2111/29
Inventor 许偏奎
Owner 许偏奎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap