Waterproof antibacterial coating fabric and preparation technology thereof

A preparation process and technology of coating cloth, applied in textiles and papermaking, etc., can solve the problems of poor softness and mechanical properties of coated cloth, limited adhesion firmness, and cannot be used for a long time, and achieve good softness and mechanical properties. , The effect of good adhesion and long service life

Active Publication Date: 2016-12-07
ZHEJIANG HUIFENG NEW MATERIALS
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the prior art, there are very few coated cloths that simultaneously realize waterproof and antibacterial effects, and the addition of waterproof and antibacterial materials often makes the softness and mechanical properties of the coated cloth worse, affecting the normal use of the coated cloth, and , the general waterproof and antibacterial materials have limited adhesion on the base fabric and cannot be used for a long time
In addition, how to achieve uniform coating of waterproof materials and antibacterial materials is also a big problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A waterproof bacteriostatic coated cloth, comprising a base cloth and a waterproof bacteriostatic layer coated on its surface in sequence, the waterproof bacteriostatic layer is made of the following components: 50kg of bamboo fiber, 15kg of wasabi, 15kg of wax gourd kernels, poly Vinylidene chloride emulsion 40kg, compound emulsion of acrylate copolymer and paraffin (weight ratio 1:1) 35kg, sodium carboxymethyl cellulose 10kg.

[0027] The preparation process of above-mentioned a kind of waterproof bacteriostatic coating cloth, comprises steps:

[0028] (1) After drying the wax gourd kernels and wasabi, crush and grind them to 100 mesh to obtain a mixed powder for later use;

[0029] (2) Add sodium carboxymethyl cellulose to 100 times the weight of water at 70°C under stirring, and continue stirring for 20 minutes to obtain a suspension;

[0030] (3) Add the mixed powder obtained in step (1) to the suspension obtained in step (2), and stir for 1 hour;

[0031] (4) Co...

Embodiment 2

[0034] A waterproof and antibacterial coated cloth, comprising a base cloth and a waterproof and antibacterial layer coated on its surface in sequence, the waterproof and antibacterial layer is made of the following components: 65kg of bamboo fiber, 25kg of wasabi, 30kg of wax gourd kernels, poly Vinylidene chloride emulsion 55kg, compound emulsion of acrylate copolymer and paraffin (weight ratio 1:1) 45kg, sodium carboxymethyl cellulose 15kg.

[0035] The preparation process of above-mentioned a kind of waterproof bacteriostatic coating cloth, comprises steps:

[0036] (1) After drying the wax gourd kernels and wasabi, crush and grind them to 200 mesh to obtain a mixed powder for later use;

[0037] (2) Add sodium carboxymethyl cellulose to 120 times the weight of 80°C water under stirring, and continue stirring for 30 minutes to obtain a suspension;

[0038] (3) Add the mixed powder obtained in step (1) to the suspension obtained in step (2), and stir for 2 hours;

[0039]...

Embodiment 3

[0042] A waterproof and antibacterial coated cloth, comprising a base cloth and a waterproof and antibacterial layer coated on its surface in sequence, the waterproof and antibacterial layer is made of the following components: 55kg of bamboo fiber, 18kg of wasabi, 17kg of wax gourd kernels, poly Vinylidene chloride emulsion 42kg, compound emulsion of acrylate copolymer and paraffin (weight ratio 1:1) 38kg, sodium carboxymethyl cellulose 11kg.

[0043] The preparation process of above-mentioned a kind of waterproof bacteriostatic coating cloth, comprises steps:

[0044] (1) After drying the wax gourd kernels and wasabi, crush and grind them to 100 mesh to obtain a mixed powder for later use;

[0045] (2) Add carboxymethylcellulose sodium to 120 times the weight of 70°C water under stirring, and continue stirring for 30 minutes to obtain a suspension;

[0046] (3) Add the mixed powder obtained in step (1) to the suspension obtained in step (2), and stir for 1 hour;

[0047] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof antibacterial coating fabric and a preparation technology thereof. The coating fabric comprises a base fabric and a waterproof antibacterial layer sequentially coating the surface of the base fabric. The waterproof antibacterial layer is prepared from, by weight, 50-65 parts of bamboo fiber, 15-25 parts of wasabi, 15-30 parts of wax gourd, 40-55 parts of a polyvinylidene chloride emulsion, 35-45 parts of acrylate copolymer and paraffin compound emulsion, and 10-15 parts of sodium carboxymethylcellulose. The coating fabric achieves the waterproof and antibacterial performance at the same time, the flexibility and mechanical property of the coating fabric are good, the waterproof antibacterial layer uniformly coats the base fabric, the attaching firmness is good, the coating fabric can be still well attached after being used for a long time, and the coating fabric has the long service life.

Description

technical field [0001] The invention relates to a coated cloth, in particular to a waterproof and antibacterial coated cloth and a preparation process thereof. It belongs to the technical field of textile materials. Background technique [0002] Coated cloth is mainly coated with a layer of material with special functions on the basis of cloth, which adds special functions to the cloth. Coated cloth is widely used in tents, clothing, bags, national defense, transportation and many other fields. Coated cloth will inevitably come into contact with a high humidity environment during use or storage. At this time, waterproof and antibacterial properties are particularly important. [0003] Under normal circumstances, the method of coating with waterproof materials can be used to achieve waterproofing, and the method of adding antibacterial materials can achieve better antibacterial effect. However, in the prior art, there are very few coated cloths that simultaneously realize w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/00
CPCD06N3/00D06N3/0056D06N3/0061
Inventor 苏跃锋张伟忠沈金凌建丰陆慧斌
Owner ZHEJIANG HUIFENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com