Method for preparing wula sedge blended fasciated yarn

A technology of Ulagrass and wrapping yarn, which is applied in the direction of yarn, textiles and papermaking, etc. It can solve the problems that Ulagrass products have not yet been researched, and achieve the effects of excellent appearance and mechanical quality, less hairiness, and low strength.

Active Publication Date: 2016-12-21
TIANJIN POLYTECHNIC UNIV
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, research has not yet been carried out on the preparation of higher-grade ulagrass products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Preparation of ulagrass fiber

[0024] ①Boil in water, immerse the Uralia stalks in tap water and boil for 1 hour;

[0025] ②Carding, using a comb of 15 needles / cm to comb the Ulagrass stalks into filaments;

[0026] ③ The first alkali boiling, the bath ratio is 1:10, sodium hydroxide with 10% of the mass of Uralia ulata, and urea with 0.5% of the mass of Uralia ulata, treated at 80°C for 2 hours, and then washed with warm water until neutral;

[0027] ④ The second alkali boiling, the bath ratio is 1:10, sodium hydroxide with 4% of the mass of Uralia, hydrogen peroxide with 4% of the mass of Uralia, JFC penetrant with 0.5% of the mass of Uralia, and treated at 70°C for 2 hours , then wash with warm water until neutral;

[0028] ⑤ The third alkali boiling, the bath ratio is 1:10, sodium hydroxide of 2% of the mass of Uralia ulata, urea of ​​0.5% of the mass of Uralia ulata, treated at 80°C for 2 hours, and washed with warm water until neutral;

[0029] ⑥Softening ...

Embodiment 2

[0038] (1) Preparation of ulagrass fiber

[0039] ①Boil in water, immerse the Uralia stalks in tap water and boil for 2 hours;

[0040] ②Carding, using a comb of 17 needles / cm to comb the Ulagrass stalks into filaments;

[0041] ③ The first alkali boiling, the bath ratio is 1:10, sodium hydroxide of 12% of the mass of Uralia ulata, urea of ​​1% of the mass of Uralia ulata, treated at 90°C for 1 hour, and then washed with warm water until neutral;

[0042] ④ The second alkali boiling, the bath ratio is 1:10, sodium hydroxide with 6% of the mass of Uralia, hydrogen peroxide with 6% of the mass of Uralia, JFC penetrant with 1% of the mass of Uralia, and treated at 80°C for 1 hour , then wash with warm water until neutral;

[0043] ⑤ The third alkali boiling, the bath ratio is 1:10, sodium hydroxide of 4% of the mass of Uralia ulata, urea of ​​1% of the mass of Uralia ulata, treated at 90°C for 1 hour, and washed with warm water until neutral;

[0044] ⑥Softening treatment, usi...

Embodiment 3

[0053] (1) Preparation of ulagrass fiber

[0054] ①Boil in water, immerse the Uralia stalks in tap water and boil for 3 hours;

[0055] ②Carding, using a comb of 19 needles / cm to comb the Ulagrass stalks into filaments;

[0056] ③ The first alkali boiling, the bath ratio is 1:20, sodium hydroxide with 12% of the mass of Uralia ulata, urea with 2% of the mass of Uralia ulata, treated at 95°C for 1 hour, and then washed with warm water until neutral;

[0057] ④ The second alkali boiling, the bath ratio is 1:20, sodium hydroxide with 8% of the mass of Uralia, hydrogen peroxide with 8% of the mass of Uralia, JFC penetrant with 2% of the mass of Uralia, and treated at 90°C for 1 hour , then wash with warm water until neutral;

[0058] ⑤ Soda boiling for the third time, the bath ratio is 1:20, sodium hydroxide with 6% of Uralia mass, urea with 2% of Uralia mass, treated at 95°C for 1 hour, and washed with warm water until neutral;

[0059] ⑥Softening treatment, using softener wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of ulagrass blended wrapping yarn. First, "boiling + carding + three times of alkali boiling + softening treatment" is used to obtain ulagrass fiber; then the ulagrass fiber cut to 45-50 mm and cotton are mixed and opened at a mass ratio of 70/30-10/90, Carding, drawing, and rotor spinning into core yarn materials, in which a roller carding machine is used for carding, and repeated opening and carding are used to improve the uniformity of subsequent yarns; Cotton blended core yarn is used for wrapping, and two or several pieces of pure cotton yarn, modal yarn, wool yarn, etc. are combined and wound on a bobbin in parallel as outer wrapping yarn. The speed ratio of hollow spindle speed and output roller is 500-900. The preparation of ulagrass blended wrapped yarn will broaden the application field of ulagrass fiber with thermal insulation and antibacterial properties.

Description

technical field [0001] The invention belongs to the field of textiles, and in particular relates to a preparation method of ulagrass blended wrapping yarn. Background technique [0002] Ulagrass, as a material with thermal and antibacterial properties, has been gradually developed and utilized by people and used in the textile field. [0003] At present, the extraction of ulagrass fiber mainly refers to the extraction process of hemp fiber, mainly by chemical method, and the basic properties of ulagrass fiber can be compared with some hemp fibers, but the further in-depth research of ulagrass fiber is still at the stage. preliminary research stage. Wang Junyou, Wang Chunhong and others only mixed ulagrass fiber with other fibers, and prepared nonwoven fabrics through opening, carding, acupuncture and other processes, which were applied to mat products. However, no research has been carried out on the preparation of higher-grade Ulagrass products. In order to bring out the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/36
Inventor 王春红岳鑫敏曹文静
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap