Air-purifying ceramic ink with dermatoglyphs effect and preparation method thereof

A technology for purifying air and ceramic ink, applied in the field of ceramics

Inactive Publication Date: 2017-01-11
FOSHAN GAOMING HAIDI CERAMIC RAW MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports about functional dermatoglyph effect ceramic inks at present, so the technology needs to be improved, and there is an urgent need to develop

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Air-purifying ceramic ink with dermatoglyphs effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] An air-purifying ceramic ink with skin texture effect and a preparation method thereof, the preparation method comprising the following steps:

[0040] Step A. Preparation of skin texture glaze: Mix and sand 40% SiO2, 8% Al2O3, 1% (K2O+Na2O), 10% (CaO+MgO), 9% B2O3, 10% ZrO2, 13% V2O5; add 1% antibacterial compound and sanded evenly; then add 8% negative ion compound, sanded evenly to obtain a mixture; spread the mixture into a refractory sagger, and melt at a high temperature of 1400°C to obtain a molten slurry material; the slurry is water-quenched and cooled, and broken into granules to obtain a skin-grain glaze;

[0041] Step B. Weigh 20% skin texture glaze, 8% Solsperse 24000, 5% Span-80, 0.3% BYK052, 3% polystyrene resin, 1% deodorant and 62.7% environmentally friendly hydrocarbon solvent, and add them to the high-speed mixer Disperse for 60 minutes; put the dispersed mixed solution into a sand mill, and sand for 10 hours to obtain a semi-finished ink with a part...

Embodiment 2

[0054] An air-purifying ceramic ink with skin texture effect and a preparation method thereof, the preparation method comprising the following steps:

[0055] Step A. Preparation of skin texture glaze: Mix and sand 38%SiO2, 9%Al2O3, 2% (K2O+Na2O), 10% (CaO+MgO), 8%B2O3, 13%ZrO2, 12%V2O5; add 3% antibacterial compound and sanded evenly; then add 5% negative ion compound, sanded evenly to obtain a mixture; spread the mixture into a refractory sagger, and melt at 1400°C to obtain a molten slurry material; the slurry is water-quenched and cooled, and broken into granules to obtain a skin-grain glaze;

[0056] Step B. Weigh 30% skin texture glaze, 5% Solsperse 24000, 3% Span-80, 0.5% BYK052, 2% polystyrene resin, 3% deodorant and 56.5% environmentally friendly hydrocarbon solvent, and add them to the high-speed mixer Disperse for 60 minutes; put the dispersed mixed solution into a sand mill, and sand for 10 hours to obtain a semi-finished ink with a particle size distribution betw...

Embodiment 3

[0069] An air-purifying ceramic ink with skin texture effect and a preparation method thereof, the preparation method comprising the following steps:

[0070] Step A. Preparation of skin texture glaze: Mix and sand 35%SiO2, 10%Al2O3, 3% (K2O+Na2O), 10% (CaO+MgO), 8%B2O3, 15%ZrO2, 12%V2O5; add 5% antibacterial compound and sanded evenly; then add 2% negative ion compound, sanded evenly to obtain a mixture; spread the mixture into a refractory sagger, and melt it at 1400°C to obtain a molten slurry material; the slurry is water-quenched and cooled, and broken into granules to obtain a skin-grain glaze;

[0071] Step B. Weigh 35% skin texture glaze, 3% Solsperse 24000, 2% Span-80, 0.8% BYK052, 1% polystyrene resin, 5% deodorant and 53.2% environmentally friendly hydrocarbon solvent, and add them to the high-speed mixer Disperse for 60 minutes; put the dispersed mixed solution into a sand mill, and sand for 10 hours to obtain a semi-finished ink with a particle size distribution ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Viscosityaaaaaaaaaa
Surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention discloses an air-purifying ceramic ink with dermatoglyphs effect and preparation method thereof. The preparation method includes the following steps: step A. preparing dermatoglyph glaze ; step B. weighing by proportion dermatoglyph glaze, dispersant, surface additive, defoamer, bonding agent, the rest is solvent, grinding to obtain the ink semi-product; step C. filtering to obtain the ink finished product. Compared with current ceramic ink with dermatoglyphs effect, the present invention has scientific ingredients, reasonable preparation, and good stable quality. Used in connection with the color ink of ceramic ink-jet printing, the vivid concave-convex lines are more fully visualized and revealed for dermatoglyph ceramics. The 3-D effect is strong, further enhancing the decorative effect of ceramics. The present invention can also be widely applied in such fields as tiles and archaized brick, meanwhile through reasonably combining negative ion compound with deodorant and antibacterial compound material, the ceramic ink has superior antibacterial, antifouling, air-purifying function, further broadening the application scope of sinkable ceramic ink.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to an air-purifying ceramic ink with skin texture effect and a preparation method thereof. Background technique [0002] Bacteria and mold, as pathogenic bacteria, are very harmful to humans, animals and plants, affecting people's health and even life-threatening, and bringing significant economic losses. Therefore, the research on antibacterial materials and their products has attracted people's attention day by day, and the demand for antibacterial products will constitute a huge market. [0003] For environmental protection, negative air ions can eliminate indoor odors and various harmful gases. The irritating gases such as benzene, formaldehyde, ketone, ammonia volatilized from the decoration materials used in the interior decoration process, as well as the sour smell of leftovers in daily life, cigarettes and other harmful odors to the human body, use materials rich in negati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/30C09D11/38
CPCC09D11/30C09D11/38
Inventor 于庆九邱杰华
Owner FOSHAN GAOMING HAIDI CERAMIC RAW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap