A primer and two-component technology, applied in coatings, polyester coatings, etc., can solve the problems of poor wear and scratch resistance and insufficient hardness of the coating, and achieve good wear and scratch resistance and high hardness. Effect
Inactive Publication Date: 2017-01-11
广东花王涂料有限公司
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] However, the currently used mid-coating primer, considering its application on outdoor woodware, has insufficient coating hardness and poor wear and scratch resistance. Therefore, it is necessary to improve and optimize
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0040] Acrylic resin 78.7%
[0041] Dispers610s dispersant 0.05%
[0042] Glide100 leveling agent 0.3%
[0043] EFKA-3600 leveling agent 0.11%
[0044] BYK-066N defoamer 0.3%
[0045] Xylene 3%
[0046] Methyl isobutyl ketone 3%
[0047] 20% Cellulose Acetate 12%
[0048] n-Butyl acetate 2%.
Embodiment 2
[0050] Acrylic resin 89.25%
[0051] Dispers610s dispersant 0.05%
[0052] Glide100 leveling agent 0.05%
[0053] EFKA-3600 leveling agent 0.05%
[0054] BYK-066N defoamer 0.1%
[0055] Xylene 1%
[0056] Methyl isobutyl ketone 1%
[0057] 20% Cellulose Acetate 8%
[0058] n-Butyl acetate 0.5%.
Embodiment 3
[0060] Acrylic resin 83.5%
[0061] Dispers610s dispersant 0.2%
[0062] Glide100 leveling agent 0.3%
[0063] EFKA-3600 leveling agent 0.5%
[0064] BYK-066N defoamer 0.2%
[0065] Xylene 2%
[0066] Methyl isobutyl ketone 2%
[0067] 20% Cellulose Acetate 10%
[0068] n-Butyl acetate 1.3%.
[0069] Primer coat:
[0070] A kind of two-component intermediate coating primer of the present invention, according to mass ratio, comprises following composition:
[0071] Saturated polyester resin 44%~66.25%
[0072] Synthetic fatty acid resin 15%~25%
[0073] 10% bentonite slurry 4% ~ 6%
[0074] Dispersant 0.5%~2%
[0075] Leveling agent 0.15%~0.5%
[0076] Defoamer 0.1%~0.3%
[0077] Xylene 1%~3%
[0078] Zinc stearate 2%~3.5%
[0079] n-Butyl acetate 0.5%
[0080] 20% cellulose acetate 8% ~ 12%
[0081] Light stabilizer 1%~2%
[0082] n-Butyl acetate 1.5%~3%
[0083] After the above ingredients are mixed, they are uniformly dispersed until the fineness is ≤35um,...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a two-component middle coating primer. The two-component middle coating primer is prepared from, by mass, 44%-66.25% of saturated polyester resin, 15%-25% of synthetic fatty acid resin, 4%-6% of bentonite slurry of 10%, 0.5%-2% of a dispersing agent, 0.15%-0.5% of a flatting agent, 0.1%-0.3% of an antifoaming agent, 1%-3% of xylene, 2%-3.5% of zinc stearate, 0.5% of n-butyl acetate, 8%-12% of cellulose acetate of 20%, 1%-2% of a light stabilizer and 1.5%-3% of n-butyl acetate; all the ingredients are mixed and dispersed to be even till the fineness is smaller than or equal to 35 microns, and the viscosity is 2,500 mpa.s/25 DEG C to 3,500 mpa.s/25 DEG C. The two-component middle coating primer has the advantages of being high in hardness, good in wear resistance and scratching resistance and capable of well meeting outdoor woodware.
Description
technical field [0001] The invention relates to a two-component intermediate coating primer. Background technique [0002] Wood varnishes for outdoor use are composed of three layers, namely, sealing primer, intermediate coating primer and top coat. The sealing primer has the characteristics of strong permeability and excellent sealing performance. The primer is used to strengthen the adhesion of the topcoat, making the topcoat more plump, delicate and smooth, and also has an anti-corrosion effect. The topcoat is the final coating of painting, and the paint effect presented after decoration or painting Rendered by topcoat. [0003] However, the currently used mid-coating primer is considered to be applied to outdoor woodware, and its coating hardness is not high enough, and its wear resistance and scratch resistance are relatively poor. Therefore, it is necessary to improve and optimize. Contents of the invention [0004] In order to overcome the deficiencies of the abov...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more