A multi-layer radar absorbing coating
A wave-absorbing coating and radar technology, applied in the direction of radiation-absorbing coatings, electrical components, antennas, etc., can solve the problems of unacceptable stability and wave-absorbing effect, unsolved powder nanomaterial dispersion process, etc. The effect of absorption effect, widening frequency band, good temperature resistance and environmental stability
Active Publication Date: 2012-09-12
SOUTHWEST JIAOTONG UNIV
View PDF5 Cites 11 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
From the perspective of practical application, there are also two problems: one is that the dispersion process of powdered nanomaterials has not been solved, and the other is that the stability and absorbing effect have not yet been accepted.
But its material thickness is more than 3.5mm
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
Embodiment 2
Embodiment 3
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
length | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Login to view more
Abstract
The invention provides a multi-layer radar wave-absorbing coating and a preparation method thereof. The wave-absorbing coating comprises alternately laminated dielectric loss composite coating layers and magnetic loss composite coating layers; the dielectric loss coating mainly includes tetrapod-shaped zinc oxide Whiskers, conductive carbon black; magnetic loss composite coating mainly includes ferric oxide and nano-iron powder; it is applied to aluminum flat materials by spraying or brushing, and the spraying sequence from the bottom layer to the surface layer is: magnetic layer-dielectric Layer-magnetic layer-dielectric layer..., the coating is cured at constant temperature to obtain a wave-absorbing coating. The total thickness of the coating is 1.5±0.1mm, and the thickness of each layer is evenly distributed. The reflectance of the radar wave absorbing stealth paint in the 4-8GHz band reaches -4-6dB, and the reflectivity in the 8-18GHz band reaches -5--8dB. The surface density of the coating is about 1.6±0.2kg/m2, the adhesion reaches more than 13.5MPa, the impact strength reaches 50kg.cm, and it has good temperature resistance and environmental stability.
Description
A multi-layer radar absorbing coating technical field The invention relates to a wave-absorbing stealth material (RAM), in particular to a multi-layer radar wave-absorbing coating and a preparation method thereof. Background technique The development and application of stealth materials are considered to be a major breakthrough in the field of military high-tech. Modern stealth technology mainly includes the design and application of stealth structures and stealth materials. Advanced stealth materials play a pivotal role in the engineering application of stealth targets. They can be used not only to suppress specular waves, but also to suppress traveling waves, creeping waves, and edge-launched echoes. The radar wave absorption performance of materials is an important and key indicator of stealth materials and stealth technology; radar wave absorption performance refers to the ability of materials to attenuate the target echo intensity through the interaction with radar wa...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01Q17/00C09D5/32
Inventor 周祚万胡书春陈晓浪
Owner SOUTHWEST JIAOTONG UNIV
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap