Preparation method of metal filament with high porosity
A technology of metal filaments and high porosity, applied in metal material coating technology, manufacturing tools, heat treatment equipment, etc., can solve the problems of low tear strength of metal filaments, low porosity of porous materials, large pores, etc., to achieve High marketing value and economic benefits, improved porosity and through-porosity, good surface finish
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0031] Example one
[0032] A method for preparing high-porosity metal filaments, after three times of drawing and three times of annealing,
[0033] It includes the following steps:
[0034] The first step is to choose 3.5mm metal wire as raw material;
[0035] In the second step, the raw metal wire is fed into the coarse wire drawing machine to be drawn to a diameter of 2.0mm;
[0036] In the third step, the wire is soaked in a 3% sodium carbonate solution for 30 minutes and then drained;
[0037] In the fourth step, the drained metal wire is sent to the first annealing furnace for annealing; the furnace temperature of the first annealing furnace is 800°C, and the speed is 5 meters per second;
[0038] In the fifth step, the metal wire after the first annealing is sent to the wire drawing machine for drawing;
[0039] The sixth step is to soak the wire in a 10% sodium carbonate solution for 20 minutes and then drain it for the second time;
[0040] In the seventh step, the metal wire drai...
Example Embodiment
[0043] Example two
[0044] A method for preparing high-porosity metal filaments, after three times of drawing and three times of annealing,
[0045] It includes the following steps:
[0046] The first step is to choose 4.0mm metal wire as raw material;
[0047] In the second step, the raw metal wire is fed into the coarse wire drawing machine to be drawn to a diameter of 2.0mm;
[0048] In the third step, the wire is soaked in a 20% sodium carbonate solution for 30-60 minutes and then drained;
[0049] In the fourth step, the drained metal wire is sent to the first annealing furnace for annealing; the furnace temperature of the first annealing furnace is 950℃, and the speed is 5 meters per second;
[0050] In the fifth step, the metal wire after the first annealing is sent to the wire drawing machine for drawing;
[0051] The sixth step is to soak the wire in a sodium carbonate solution with a concentration of 20% for 30 minutes and then drain it for the second time;
[0052] In the sevent...
Example Embodiment
[0055] Example three
[0056] A method for preparing high-porosity metal filaments, after three times of drawing and three times of annealing,
[0057] It includes the following steps:
[0058] The first step is to choose 3.5mm metal wire as raw material;
[0059] In the second step, the raw metal wire is fed into the coarse wire drawing machine to be drawn to a diameter of 2.0mm;
[0060] In the third step, the wire is soaked in a 3% sodium carbonate solution for 60 minutes and then drained;
[0061] In the fourth step, the drained metal wire is sent to the first annealing furnace for annealing; the furnace temperature of the first annealing furnace is 950℃, and the speed is 5 meters per second;
[0062] In the fifth step, the metal wire after the first annealing is sent to the wire drawing machine for drawing;
[0063] In the sixth step, the metal wire is soaked in a 10% sodium carbonate solution for 30 minutes and then drained for the second time;
[0064] In the seventh step, the metal ...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Aperture | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap