Antistatic anti-flaming PC/ABS compound material and preparation method thereof

A composite material, antistatic technology, applied in the field of antistatic flame retardant PC/ABS composite material, can solve the problems of limited practical application, decreased thermal stability of PC, high price of antistatic agent, etc., to achieve excellent antistatic properties, reduce Influence, little effect on mechanical properties

Inactive Publication Date: 2017-01-25
SHANGHAI KINGFA SCI & TECH +2
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In EP1290106B1, the quaternary ammonium salt of perfluoroalkane sulfonic acid is used as an antistatic agent in plastics, but the price of the antistatic agent is high, and the thermal stability of PC decreases, which seriously limits the practical application of the invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic anti-flaming PC/ABS compound material and preparation method thereof
  • Antistatic anti-flaming PC/ABS compound material and preparation method thereof
  • Antistatic anti-flaming PC/ABS compound material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5 and comparative example 1～4

[0040] According to Table 1, formula PC resin, ABS resin, flame retardant, toughening agent, antistatic agent, antioxidant and other additives are put into the mixer and blended until uniform, and the obtained premix is ​​put into the twin screw extruder Melt mixing and extrusion granulation are performed to obtain the antistatic and flame-retardant PC / ABS composite material of the present invention. Among them, the screw length-diameter ratio of the twin-screw extruder is 40:1, the barrel temperature is 260-280°C, and the screw speed is 400-500rpm.

[0041] The antistatic property, flame retardancy and notched cantilever beam impact strength of the prepared PC / ABS composite material were tested. The reference standards or methods for the test are as follows:

[0042] (1) Antistatic property: The surface resistivity is used to characterize the antistatic properties of the material. A 2mm thick molded square plate is adjusted for 24 hours at 23°C and 50% humidity, and the surface re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Surface resistivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antistatic and flame-resistant PC / ABS composite material and a preparation method thereof. The composite material comprises 60-80 parts of PC resin; 8-15 parts of ABS resin; 8-12 parts of flame retardant; toughening agent 1-5 parts; antistatic agent 8-25 parts; antioxidant 0.01-2 parts; other additives 0.4-0.8 parts. The present invention selects the preferred antistatic agent, which minimizes the impact on PC performance, and the use of the antistatic agent in conjunction with the emulsion method ABS is beneficial to the antistatic effect of the antistatic agent and can last.

Description

Technical field [0001] The invention relates to the field of PC / ABS composite materials, in particular to an antistatic and flame-retardant PC / ABS composite material. Background technique [0002] PC / ABS resin is an alloy material with excellent properties. It has excellent physical and mechanical properties, surface hardness, high strength and fluidity, and has a certain degree of heat resistance. It has been widely used in electrical and electronic equipment materials, computers , Mobile phones, printers, housing materials, automotive materials and other industrial parts manufacturing materials. However, the disadvantage of PC / ABS resin is that it has poor flame retardancy and high electrical insulation. Therefore, various modifiers should be added to PC / ABS alloy to improve its performance. Flame retardant PC / ABS alloy is one of them. An important modification direction. [0003] In the semiconductor and automotive industries, the accumulation of static charges can cause perma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L55/02C08L77/12C08K13/02C08K5/523C08K5/134
CPCC08L69/00C08L2201/02C08L2201/04C08L2201/08C08L2205/035
Inventor 田征雨王琦玲董相茂刘贤文岑茵艾军伟佟伟
Owner SHANGHAI KINGFA SCI & TECH