Metal nanoparticle structure array and preparation method thereof

A technology of metal nanoparticles and arrays, applied in the direction of nanostructure manufacturing, nanotechnology, nanotechnology, etc., can solve the problems of difficulty in realizing nanogap control, low preparation efficiency, and high equipment requirements, and achieve low cost, good compatibility, and adaptability broad effect

Active Publication Date: 2017-02-01
NAT UNIV OF DEFENSE TECH
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing process has high equipment requirements, high cost, complex process, and low production efficiency; a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal nanoparticle structure array and preparation method thereof
  • Metal nanoparticle structure array and preparation method thereof
  • Metal nanoparticle structure array and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A metal nanoparticle structure array of the present invention, specifically a gold nanoparticle structure array, comprising a two-layer two-dimensional gold nanoparticle structure array and a layer of aluminum oxide film, and the aluminum oxide film is located between the two-layer two-dimensional gold nanoparticle structure array between. The two-dimensional gold nanoparticle structure array is a two-dimensional hexagonal array structure composed of gold nanoparticles periodically arranged, and the gold nanoparticles in the second layer two-dimensional gold nanoparticle structure array are located in the first layer two-dimensional gold nanoparticle structure array in the depressions formed between adjacent gold nanoparticles. The diameter of the gold nanoparticles in the first layer of the two-dimensional gold nanoparticle structure array is 200nm, and the diameter of the gold nanoparticles in the second layer of the two-dimensional gold nanoparticle structure array i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a metal nanoparticle structure array and a preparation method thereof. The preparation method comprises the following steps: (1) preparing an ordered polystyrene nano spherical dense arrangement; (2) depositing a metal film; and (3) preparing a single-layer ordered metal nanoparticle structure array. The invention further discloses a method for preparing a double-layer or a multi-layer ordered metal nanoparticle structure array. An alumina film is arranged between every two adjacent layers of the ordered metal nanoparticle structure array of the metal nanoparticle structure array disclosed by the invention. The preparation method disclosed by the invention is simple in process, economical and efficient, controllable in nano size gaps and good in repeatability, and the metal nanoparticle structure array has the advantages of being large in area, high in density, controllable in nano size gaps, and the like.

Description

technical field [0001] The invention belongs to the field of metal nanostructures, and in particular relates to a metal nanoparticle structure array and a preparation method thereof. Background technique [0002] Surface-enhanced Raman spectroscopy (SERS) is an emerging biomolecular detection technology, which has high detection sensitivity, can achieve single-molecular-weight detection, and can provide rich molecular structure information. The key to developing SERS into an analytical technique with practical application significance is to prepare SERS active substrates with high sensitivity, high stability, good reproducibility and high selectivity. In recent years, periodic metal nanostructure arrays (especially noble metal nanostructure arrays, such as gold, silver, platinum, copper, etc.) have attracted extensive attention due to their great enhancement effect on SERS. [0003] The size of the nanogap of metal nanostructures directly affects the sensitivity and other p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B82B3/00B82B1/00B82Y30/00B82Y40/00
Inventor 吴学忠董培涛孟选辉王朝光陈剑曾学盛
Owner NAT UNIV OF DEFENSE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap