Thermal transfer ribbon for near-edge printing and preparation method thereof

A thermal transfer ribbon, emulsion technology, applied in printing, ink ribbon, inking device, etc., can solve the problem of different viscosity of release layer and adhesive layer without control, single-layer coating is difficult to meet the release temperature, low imprint pattern Strength and other issues, to achieve the effect of fast printing speed, strong adhesion, and clear imprinting

Active Publication Date: 2018-10-30
HANGZHOU TODAYTEC DIGITAL
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, although the ribbons used for edge-pressure printers also use water-based systems, most of the ribbons are not fully transferred after printing, and the imprint is not clear. The effect is poor under the fast printing of variable pressure printers. The reason for this is mainly at present. Most of the variable pressure ribbons used are single-layer coated, and single-layer coating is difficult to meet the requirements of low release temperature and high imprint pattern strength after printing; a few use double-layer coated ribbons, but there is no controlled release layer and The viscosity of the adhesive layer is different, because the viscosity difference between the release layer and the adhesive layer is too small, the release layer and the ink layer are mixed together during the heating process, the pattern transfer is incomplete, and the imprinting effect is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Mix and stir 20 parts of water-based wax emulsion, 1 part of water-based silica gel emulsion, 1 part of dispersant and 78 parts of deionized water, and disperse evenly to obtain a release layer coating liquid; set the drying tunnel of the gravure coating machine The temperature is 80°C, and the release layer coating solution is passed through the coating machine at a rate of 1g / m 2 The coating amount is coated on a polyester film with a heat-resistant back coating thickness of 4.5 μm to obtain a substrate with a release layer.

[0027] 12 parts of water-based EVA emulsion, 2 parts of water-based EEA emulsion, 3 parts of water-based rosin emulsion, 5 parts of water-based wax emulsion, 6 parts of carbon black, 0.7 parts of dispersant, 1 part of leveling agent, 0.3 parts Mix and stir the defoamer and 70 parts of deionized water, disperse evenly, and grind to a fineness below 5 μm; set the oven temperature of the gravure coating machine to 75 ° C, and pass the release layer...

Embodiment 2

[0029] Mix and stir 20 parts of water-based wax emulsion, 1 part of water-based silica gel emulsion, 1 part of dispersant and 78 parts of deionized water, and disperse evenly to obtain a release layer coating liquid; set the drying tunnel of the gravure coating machine The temperature is 80°C, and the release layer coating solution is passed through the coating machine at a rate of 1g / m 2 The coating amount is coated on a polyester film with a heat-resistant back coating thickness of 4.5 μm to obtain a substrate with a release layer.

[0030] With 10 parts of water-based EVA emulsion, 2 parts of water-based EEA emulsion, 2 parts of water-based polyester emulsion, 2 parts of water-based polyurethane emulsion, 6 parts of water-based wax emulsion, 6 parts of carbon black, 0.7 parts of dispersant, 1 1 part of leveling agent, 0.3 part of defoamer and 70 parts of deionized water are mixed and stirred, dispersed evenly, and ground to a fineness below 5 μm; set the temperature of the ...

Embodiment 3

[0032] Mix and stir 20 parts of water-based wax emulsion, 1 part of water-based silica gel emulsion, 1 part of dispersant and 78 parts of deionized water, and disperse evenly to obtain a release layer coating liquid; set the drying tunnel of the gravure coating machine The temperature is 80°C, and the release layer coating solution is passed through the coating machine at a rate of 1g / m 2 The coating amount is coated on a polyester film with a heat-resistant back coating thickness of 4.5 μm to obtain a substrate with a release layer.

[0033] 10 parts of water-based EVA emulsion, 2 parts of water-based EEA emulsion, 2 parts of water-based acrylic emulsion, 2 parts of water-based polyurethane emulsion, 6 parts of water-based wax emulsion, 6 parts of carbon black, 0.7 parts of dispersant, 1 part Mix and stir the leveling agent, 0.3 parts of defoamer and 70 parts of deionized water, disperse evenly, and grind to a fineness below 5 μm; set the drying tunnel temperature of the grav...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thermal transfer ribbon used for proximal margin printing and a production method thereof. The thermal transfer ribbon comprises a releasing layer, an adhesive coating and a matrix layer; the releasing layer comprises an aqueous wax emulsion, an auxiliary agent and deionized water, the adhesive coating comprises an aqueous resin emulsion, the aqueous wax emulsion, inorganic pigment, an auxiliary agent and deionized water; the emulsions used in the releasing layer and the adhesive coating are aqueous emulsions, an organic solvent is not added; viscosity of the releasing layer and the adhesive coating are different, and cannot be mutually penetrated while transfer printing. The thermal transfer ribbon can realize rapid printing for a proximal margin printer, the printed characters and images are clear, and the wear resistant and scratch resistant effects are good.

Description

technical field [0001] The invention relates to the field of thermal transfer printing, in particular to a water-based thermal transfer ribbon for near-edge printing. Background technique [0002] Thermal transfer printers are divided into flat-press printers and side-press printers. Compared with flat-press printing, the side-press printing speed is fast and saves ribbons. The printing speed of the side-press printers can reach 600mm / s, while the flat-press printers The speed can only reach 300mm / s. Because the printing speed is relatively doubled, edge-press printers are widely used in various large-scale manufacturing factories. [0003] Printing ribbons for edge-press printers and flat-press printers are not universal. At present, most of the ribbons used for edge-press printers are solvent systems. Solvent systems use a large amount of toluene, xylene, and methyl ethyl ketone during use. , methyl isobutyl ketone and ethers and other organic solvents, during the coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D191/06C09D123/08C09D167/00C09D183/04C09D175/04C09D133/00C09D193/04C09D7/61B41J31/00
CPCB41J31/00C08L2205/02C08L2205/035C09D123/0853C09D191/06C08L83/04C08L23/0869C08L93/04C08L91/06C08K3/04C08L67/00C08L75/04C08L33/00
Inventor 颜晨曦孙段冰曹伟鹏
Owner HANGZHOU TODAYTEC DIGITAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com