A special skeleton composite new material yarn and a preparation method therefor

A new material and skeleton technology, which is applied in the direction of yarn, fiber type, textile and paper making, can solve the problems such as poor coating of skeleton composite materials, and achieve the effect of good appearance, high strength and improved strength

Active Publication Date: 2017-02-15
潍坊四棉纺织有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] 4. The present invention adopts the most suitable feeding tension; it can well solve quality p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A special skeleton composite new material yarn and a preparation method therefor
  • A special skeleton composite new material yarn and a preparation method therefor
  • A special skeleton composite new material yarn and a preparation method therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Example 1 A special skeleton composite new material yarn and its preparation method

[0043] Include the following steps:

[0044] Step 1 raw material selection

[0045] (1) Yarn outsourcing fiber raw materials

[0046] The outsourcing fiber raw material is cotton fiber;

[0047] The cotton fiber: high-quality Xinjiang long-staple cotton, grade 1, length 37.00mm, micronaire value 4.15, single fiber breaking strength 48.52cN / tex, uniformity 87.81%, short fiber 10.3%, moisture regain 6.93%, containing impurities 3.7%;

[0048] (2) Yarn core fiber raw material

[0049] The core fiber is a polyester filament fiber;

[0050] The polyester filament fiber: linear density 100dtex, root number 48F, dry breaking strength 3.88cN / tex, dry elongation at break 29.3%;

[0051] Among the outsourcing fiber raw materials and the core fiber raw materials, the quality of the outsourcing fibers accounts for 45% of the total raw material mass, and the core fiber accounts for 55% of the...

Embodiment 2

[0078] Example 2 A special skeleton composite new material yarn and its preparation method

[0079] Include the following steps:

[0080] Step 1 raw material selection

[0081] (1) yarn outsourcing fiber

[0082] The outsourcing fiber raw material includes cotton fiber and modal fiber;

[0083] The cotton fiber: high-quality Xinjiang long-staple cotton, grade 1, length 37.00mm, micronaire value 4.15, single fiber breaking strength 48.52cN / tex, uniformity 87.81%, short fiber 10.3%, moisture regain 6.93%, containing impurities 3.7%;

[0084] The modal fiber: the modal specification is 1.3dtex*39mm, the dry breaking strength is 3.5cN / dtex, and the moisture regain is 9.98%.

[0085] (2) Yarn core fiber

[0086] The core fiber raw material adopts nylon filament fiber;

[0087] The nylon filament fiber has a linear density of 100dtex, a root number of 48F, a dry breaking strength of 5.18cN / tex, and a dry breaking elongation of 20.5%.

[0088] Among the outsourcing fiber and c...

Embodiment 3

[0114] Example 3 A special skeleton composite new material yarn and its preparation method

[0115] Include the following steps:

[0116] Step 1 raw material selection

[0117] (1) yarn outsourcing fiber

[0118] The outsourcing fiber raw material comprises bamboo cellulose fiber and fine denier polyester fiber;

[0119] The bamboo cellulose fiber: the specification is 1.33dtex*38mm, the dry breaking strength is 2.52cN / dtex, and the moisture regain is 11.2%.

[0120] The fine-denier polyester fiber: the specification of the fine-denier polyester is 0.89dtex*38mm, the dry breaking strength is 6.22cN / dtex, and the moisture regain is 0.36%.

[0121] (2) Yarn core fiber

[0122] The yarn core fiber raw material is polyester filament fiber;

[0123] The polyester filament fiber: linear density 100dtex, root number 48F, dry breaking strength 3.88cN / tex, dry elongation at break 29.3%.

[0124] Among the outsourcing fiber and core fiber raw materials, bamboo cellulose fiber acco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Linear densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a special skeleton composite new material yarn and a preparation method therefor. The yarn comprises outer wrapping fibers and core yarn fibers. The yarn is characterized in that the yarn evenness CV is 8.1-9.6%, the number of thin segments in one thousand meters is 0-1, the number of nubs in one thousand meters is 3-6, and the number of neps in one thousand meters is 16-25. The invention also provides a preparation method for the special skeleton composite new material yarn. The method comprises an outer wrapping fiber raw material pretreatment step of performing spraying pretreatment on outer wrapping fiber raw materials by using a composite oil agent. The composite oil agent comprises, in weight percentage, 4-6% of silica sol, 3-5% of glycerinum, 18-20% of an antistatic agent, 15-17% of peregal, and 51-57% of water, wherein the temperature of water is 45-50 DEG C. The prepared skeleton composite new material yarn is characterized by constant wrapping tension maintenance and favorable wrapping, and is free of such quality problems as naked threads, hollow yarns and thread loop noses.

Description

technical field [0001] The invention relates to a special skeleton composite new material yarn and a production method thereof, belonging to the technical field of ring spinning. Background technique [0002] With the replacement of functional fibers, protective clothing continues to develop in the direction of multi-functionality, compounding and comfort. Although the market's requirements for protective clothing are increasingly demanding, it is difficult to meet the requirements of protective clothing due to the uniqueness of various fibers. The development of core-spun technology has brought development opportunities to occupational protective clothing, but the quality stability of core-spun products is poor at present, and the depth and breadth of product applications are far from enough. Therefore, the development of functional core-spun products and the quality of core-spun products This problem has become a new research topic. This invention is entrusted by the Chin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/36D02G3/04D06M11/79D06M13/148
CPCD02G3/04D02G3/36D06M11/79D06M13/148D06M2101/06D06M2101/32D06M2101/34D10B2201/02D10B2201/10D10B2201/22D10B2321/06D10B2331/02D10B2331/04
Inventor 罗秀丽王晓明刘呈刚逯常青曹茂春
Owner 潍坊四棉纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap