Low temperature multiplying power type lithium ion battery

A lithium-ion battery and rate technology, applied in battery electrodes, secondary batteries, circuits, etc., can solve problems such as premature discharge voltage, failure to discharge electricity, and lower discharge platform

Active Publication Date: 2017-02-22
江苏海四达电源有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When an ordinary battery is used under high-current discharge in a low-temperature environment, the polarization of the battery increases, the discharge platform decreases, and the discharge voltage is reached prematurely, resulting in too little discharge capacity of the battery or no discharge directly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low temperature multiplying power type lithium ion battery
  • Low temperature multiplying power type lithium ion battery
  • Low temperature multiplying power type lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Low-temperature rate lithium-ion battery A1 with a rated capacity of 5Ah: composed of positive electrode, negative electrode, separator and electrolyte. Among them, the positive electrode contains (calculated by weight percentage of solid): 98.2% LiCoO 2 (D 50 5.2um), 0.8% binder PVDF, 1% conductive agent CNT; the negative electrode contains (calculated by weight percentage of solid): 74% artificial graphite, 20% hard carbon, 1.5% conductive agent KS-6, 1.5% Conductive agent SP, 3% binder PVDF, 0.25% oxalic acid; polyethylene ceramic film is used as diaphragm; low-temperature electrolyte containing vinylene carbonate and fluoroethylene carbonate is selected.

Embodiment 2

[0025] Low-temperature rate lithium-ion battery A2 with a rated capacity of 5Ah: composed of positive electrode, negative electrode, separator and electrolyte. Among them, the positive electrode contains (calculated by weight percentage of solid): 96% LiCoO 2 (D 50 7.2um), 2% binder PVDF, 2% conductive agent CNT; the negative electrode contains (calculated by weight percentage of solid): 78% artificial graphite, 15% hard carbon, 3% conductive agent SP, 4% bond Agent PVDF, 0.15% oxalic acid; use polyethylene ceramic film as the diaphragm; use low-temperature electrolyte containing vinylene carbonate and fluoroethylene carbonate.

Embodiment 3

[0027] According to the method of Example 1, the low-temperature rate lithium-ion battery A3 with a rated capacity of 5Ah is obtained, the difference is that the LiCoO in the positive electrode 2 Change to LiNi 0.4 co 0.1 mn 0.5 o 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low temperature multiplying power type lithium ion battery which comprises an anode, a cathode, a diaphragm and an electrolyte, wherein an active substance, a binder and a conductive agent are contained in the anode; synthetic graphite, hard carbon, a conductive agent, a binder and oxalic acid are contained in the cathode; and the active substance is lithium cobalt oxide LiCoO2 or nickel cobalt lithium manganese oxide LiNixCoyMn1-x-yO2. The low temperature multiplying power type lithium ion battery has an excellent discharging property under a low temperature environment.

Description

technical field [0001] The invention relates to a lithium ion battery, in particular to a low-temperature rate lithium ion battery. Background technique [0002] Lithium-ion batteries have attracted much attention because of their high energy density, high voltage platform, excellent cycle performance, portability, safety and environmental protection, and are widely used in various products. With the advancement of science and technology and the development of society, portable products are developing toward miniaturization, intelligence, and multi-functionality. The complexity of product use environments increases, requiring batteries as energy sources to have better environmental applicability. The low-temperature performance (low temperature generally refers to below -10°C) is particularly important as an important indicator for considering the environmental applicability of the battery. When an ordinary battery is used under high-current discharge in a low-temperature e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M10/0525H01M4/505H01M4/525
CPCH01M4/505H01M4/525H01M10/0525Y02E60/10
Inventor 沈晓彦王进沙永香葛汤铭
Owner 江苏海四达电源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com