A kind of all-aqueous plastic flexographic printing ink and preparation method thereof

An all-water-based, flexographic technology, applied in the field of printing inks, to achieve good printability, eliminate generation and discharge of pollution, and improve safety and health effects

Active Publication Date: 2020-01-10
中国印刷科学技术研究院有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] The problem to be solved by the present invention is to provide a fully water-based plastic flexographic ink under the premise of ensuring the printing suitability of the ink and the quality of the printed matter. During its preparation and use, no organic solvent is added at all, and only deionized water or As a single solvent, tap water fundamentally eliminates the generation and volatilization of VOC in ink products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment 1 A kind of full water-based plastic flexographic yellow printing ink

[0047] (1) Preparation of water-based yellow color paste: Weigh 42kg of ink resin, 40kg of yellow pigment, 1.8kg of wetting and dispersing agent, 1kg of defoamer and 28kg of deionized water, mix the weighed raw materials into a sand mill, grind and disperse , the rotation speed is 2000 rpm, the grinding time is 120 minutes, and the water-based yellow color paste with a fineness of 5-10 μm is prepared;

[0048] The ink resin is acrylic resin solution (JONCRYL HPD 96, BASF Chemicals); the yellow pigment is benzidine yellow PY12 (DIC pigment); the wetting and dispersing agent is non-ionic acrylic polymer (Digo 760) and Ceno The polycarboxylate ammonium salt dispersant SN-5029 of Puke Co., Ltd. is a mixture with a weight ratio of 2:1; the defoamer is a polyether siloxane copolymer (Digo 810); the deionized water is self-made in the laboratory.

[0049] (2) Preparation of water-based binder: ...

Embodiment 2

[0054] Embodiment 2 A kind of full water-based plastic flexographic yellow printing ink

[0055] (1) Preparation of water-based yellow color paste: Weigh 50kg of ink resin, 42kg of yellow pigment, 6kg of wetting and dispersing agent, 5kg of defoamer and 40kg of deionized water, mix the weighed raw materials into a sand mill for grinding and dispersing, The rotation speed is 2000 rpm, the grinding time is 120 minutes, and the water-based yellow color paste with a fineness of 5-10 μm is prepared;

[0056] The ink resin is acrylic resin solution (JONCRYL HPD 96, BASF Chemicals); the yellow pigment is benzidine yellow PY12 (DIC pigment); the wetting and dispersing agent is non-ionic acrylic polymer (Digo 760) and Ceno The polycarboxylate ammonium salt dispersant SN-5029 of Puke Co., Ltd. is a mixture with a weight ratio of 2:1; the defoamer is polyether-modified trisiloxane; deionized water is self-made in the laboratory.

[0057] (2) Prepare water-based binder: Put 65kg of ink b...

Embodiment 3

[0061] Embodiment 3 A kind of fully water-based plastic flexo cyan ink

[0062] (1) Preparation of water-based cyan color paste: Weigh 33kg of ink resin, 34kg of cyan pigment, 1.5kg of wetting and dispersing agent, 1kg of defoamer and 28kg of deionized water, mix the weighed raw materials into a sand mill for grinding and dispersing , the rotation speed is 2000 rpm, the grinding time is 120 minutes, and the water-based cyan color paste with a fineness of 5-10 μm is prepared;

[0063] The ink resin is acrylic resin solution (JONCRYL HPD 96, BASF chemical industry); the cyan pigment is phthalocyanine blue (BASF pigment); the wetting and dispersing agent is non-ionic acrylic polymer (Digo 760) The mixture of polycarboxylate ammonium salt dispersant SN-5029 of Keke Co., Ltd. with a weight ratio of 2:1; the defoamer is polydimethylsiloxane; deionized water is made in the laboratory.

[0064] (2) Prepare water-based binder: Put 45kg of ink binder and 2kg of wax emulsion into the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
Login to View More

Abstract

The invention provides full water-based plastic flexible printing ink. The full water-based plastic flexible printing ink is prepared by the following raw materials by weight: 35-70 parts of printing ink connection materials, 25-50 parts of color paste, 1-10 parts of a flatting agent, 1-10 parts of a defoamer, 1-8 parts of wax emulsion, and 5-20 parts of deionized water. The color paste is prepared by mixing the following raw materials by weight: 20-55 parts of printing ink resin, 20-50 parts of organic pigments, 1-8 parts of a wetting dispersant, 1-6 parts of the defoamer, and 20-40 parts of the deionized water. The full water-based printing ink has abroad application range, and has environment-friendly feature compared with the normal water-based printing ink, and is capable of greatly reducing the pollutant residue and volatility gases on the surface of a printed matter, and realizing the zero release of VOC in the printing ink products. The full water-based printing ink has the characteristics of good adhesive force, rub resistance, scratch resistance, weather resistance, water resistance, chemical resistance, resistance and so on, and the high-speed flexible printing is more than 150 m / min.

Description

technical field [0001] The invention belongs to the technical field of printing inks, and in particular relates to a fully water-based plastic flexographic ink and a preparation method thereof. Background technique [0002] Due to its wide adaptability and economy, flexographic printing has become the fastest growing printing method at home and abroad in recent years, and because of the wide use of water-based ink in flexographic printing, water-based flexographic printing is recognized as one of the best , the most promising printing method. Since the 1970s, water-based inks have been greatly developed and have been widely used on absorbent materials such as paper and cardboard. However, flexographic water-based inks applied to non-absorbent materials such as plastic films still have problems such as slow drying speed and poor adhesion. In order to solve these technical problems, many water-based inks still add some alcohols or ethers during production or use. Such as org...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/107C09D11/03C09D11/033C09D11/037
CPCC09D11/03C09D11/033C09D11/037C09D11/107
Inventor 刘亚男王晓芳孙志勇欧阳芸刘晓丽高雪来燕张竞
Owner 中国印刷科学技术研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com