A technology of propylene polymer and polar monomer, applied in the field of propylene polymer grafting polar monomer, can solve the problems of many kinds of raw materials, limited polymer performance, complicated process, etc., so as to reduce costs and improve grafting. efficiency, the effect of simplifying the process

Inactive Publication Date: 2017-03-29
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN101492517B has introduced a kind of grafting monomer that utilizes the porosity of polypropylene to absorb oil solubility, uses peroxide as initiator, reacts in water phase, obtains the graft product that grafting efficiency is higher, but does not involve polypropylene characteristics, its examples are limited to propylene hom

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for grafting propylene polymer with polar monomer
  • Method for grafting propylene polymer with polar monomer
  • Method for grafting propylene polymer with polar monomer

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0052] Example 1

[0053] A propylene / ethylene random copolymer is used as the polypropylene matrix, wherein the ethylene content is 2.2 wt%, the melt mass flow rate is 3.6 g / 10 min, and 300 g particles with a particle size between 1 mm and 2 mm are taken after sieving.

[0054] Put it into a 2L glass kettle with a condensing device with mechanical stirring, airtightly vacuumize and remove oxygen. An acetone solution containing 0.384 g of benzoyl peroxide was added, and after stirring and mixing for 15 minutes, the acetone was removed by vacuum. Then add 15g GMA and 100ml deionized deionized water, airtightly stir for 30min, so that GMA can fully infiltrate the base material. Then add 100ml deionized water, heat to 90°C, and react for 4 hours. After the reaction, the product was filtered, cooled, washed with deionized water 3 times, and fluidized and dried.

[0055] Take 2g sample, dissolve it with 100ml xylene at 140℃ for 1 hour, then pour it into 250ml acetone while it is hot, a...

Example Embodiment

[0056] Example 2

[0057] The polypropylene matrix was changed to a propylene / ethylene random copolymer with an ethylene content of 2.5 wt%. Other conditions were the same as in Example 1. The experimental results of A1730 / A2722 before and after purification are listed in Table 1.

Example Embodiment

[0058] Example 3

[0059] The polypropylene matrix was changed to a propylene / ethylene random copolymer with an ethylene content of 2.8 wt%. The other conditions were the same as in Example 1. The experimental results of A1730 / A2722 before and after purification are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for grafting a propylene polymer with a polar monomer. The method comprises a, mixing a propylene polymer, an initiator and an organic solvent to obtain a mixture, b, removing the organic solvent in the mixture obtained by the step a and adding a polar monomer into the mixture for swelling, c, adding water into the swollen material obtained by the step b and heating the solution for a reaction, and d, washing and drying the reaction product obtained by the step c to obtain a propylene polymer grafted with the polar monomer. The method can utilizes an aqueous phase suspension grafting method for the propylene polymer, can observably improve polar monomer grafting efficiency and ratio and is conducive to wide application of the grafting-modified polypropylene.

Description

technical field [0001] The invention relates to a method for grafting and modifying polymers, in particular to a method for grafting propylene polymers with polar monomers. Background technique [0002] As a general-purpose plastic, polypropylene is widely used in many fields such as daily necessities, electrical accessories, and packaging. However, due to the lack of polar functional groups in polypropylene, it has the disadvantages of poor dyeability, adhesion, antistatic and hydrophilic properties, and poor compatibility with reinforcing materials and inorganic fillers. In order to expand the application range of polypropylene, it needs to be modified, such as grafting, blending, filling and composite reinforcement modification. [0003] Among them, graft modification has been widely used in the fields of polypropylene and nylon blend modification, glass fiber and inorganic particle filled polypropylene. The commonly used grafting methods mainly include solution graftin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F255/04C08F255/02C08F220/32C08F2/18
Inventor 宋文波邵清毕福勇张京春张晓萌邹发生胡慧杰刘振杰
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap