Ice-cold polyester functional fabric and production method thereof

A production method and cool technology, applied in textile, yarn, fabric and other directions, can solve the problems of difficult weaving, large shrinkage, complex process design, etc., and achieve the effect of reducing yarn hairiness, increasing weft strength, and simple process

Inactive Publication Date: 2017-04-19
JIHUA 3509 TEXTILE
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its disadvantages are large shrinkage, difficult weaving, and complicated process design.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1) Warping process

[0027] Warp the blended yarn of cool polyester fiber and Tencel fiber (the blending ratio is 50:50), the warping speed is controlled at 440-460 m / min, and the average weight of the tension disc is 3.2-3.6g. Carry out arc segmentation in the front, middle and back;

[0028] 2) Sizing process

[0029] Sizing the blended yarn of cool polyester fiber and LF tencel fiber at a sizing speed of 40-45 m / min.

[0030] The slurry used includes the following raw materials in parts by weight: 45.0 parts of phosphate starch, 14.5 parts of liquid propylene, 20.0 parts of composite starch, 35.0 parts of rubber powder, 2.5 parts of antistatic agent, 1.0 part of penetrating agent, slurry The solid content is 11.4±1%, and the sizing is performed with a single size tank.

[0031] 3) Denting

[0032] According to the design requirements of the upper machine diagram, the warp stopper, heald, and reed are sequentially passed through. When drawing in the warp, it is th...

Embodiment 2

[0037] 1) Warping process

[0038] Warp the blended yarn of cool polyester fiber and Tencel fiber (the blending ratio is 45:55). The warping speed is controlled at 440-460 m / min. Carry out arc segmentation in the front, middle and back;

[0039] 2) Sizing process

[0040] Sizing the blended yarn of cool polyester fiber and tencel fiber at a sizing speed of 40-45 m / min.

[0041] The slurry used in step 2) includes each raw material of following parts by weight: the phosphate starch of 50.0 parts, the liquid propylene of 15 parts, the TH-100 of 25 parts, the rubber powder of 37.5 parts, the antistatic agent of 4 parts, 1 parts of penetrating agent, the solid content of the slurry is 11.4±1%.

[0042] 3) Denting

[0043] According to the design requirements of the upper machine diagram, the warp dropper, the heddle and the reed are sequentially passed through, and when the warp is drawn in, it is threaded strictly according to the arrangement ratio of the two warp yarns.

[...

Embodiment 3

[0049] 1) Warping process

[0050] Warp the blended yarn of cool polyester fiber and Tencel fiber (the blending ratio is 55:45), the warping speed is controlled at 440-460 m / min, the average weight of the tension disc is 3.2-3.6g, and the upper, middle and lower Carry out arc segmentation in the front, middle and back;

[0051] 2) Sizing process

[0052] Sizing the blended yarn of cool polyester fiber and tencel fiber at a sizing speed of 40-45 m / min.

[0053] The slurry used in step 2) includes each raw material of following parts by weight: 55.0 parts of phosphate starch, 15.5 parts of liquid propylene, 30.0 parts of composite starch, 40.0 parts of rubber powder, 4.5 parts of antistatic agent, 1.5 parts of permeable agent, and the solid content of the slurry is 11.4±1%.

[0054] 3) Denting

[0055] According to the design requirements of the upper machine diagram, the warp dropper, the heddle and the reed are sequentially passed through, and when the warp is drawn in, it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Heightaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of textile production and specifically relates to ice-cold polyester functional fabric and a production method thereof. The fabric is satin fabric which is formed by warp yarn and weft yarn, wherein the wrap yarn is blended yarn formed by ice-cold polyester fiber and tencel fiber and the weft yarn is doubling yarn formed by doubled bamboo fiber. The production method comprises following steps: 1) beam-warping process; 2) sizing process; 3) denting; 4) weaving process. The yarn strength is increased by adopting blended yarn; the yarn feather is reduced so as to facilitate later sizing and weaving; the blended yarn is processed with sizing agent, which can effectively reduce the shrinkage of ice-cold polyester fiber and is convenient for weaving; doubled bamboo fiber is used as weft yarn; the cross sectional area of the weft yarn is doubled so that the weft direction strength is increased so as to facilitate the later high speed weaving; the production method is simple and efficient. The ice-cold polyester functional fabric has smooth hand feel, high strength and good anti-static-electricity performance and color fastness performance; the fabric is quick in cooling and heat dissipating.

Description

technical field [0001] The invention belongs to the technical field of textile production, and in particular relates to a cool polyester functional fabric and a production method thereof. Background technique [0002] With the development of the economy, the application field of textiles continues to expand, especially in the application of industrial textiles. How to endow textiles with more functionality, bring more convenience to people's production and life, and improve the core of products? Competitiveness has important practical significance. A kind of cool polyester functional fabric is added with mineral element thin-layer mica during the drawing process, so the temperature is about 1-2 degrees lower than cotton or other fiber fabrics. It can quickly absorb moisture and perspiration, and the natural non-toxic effect is permanent and effective. It is needed in summer and is more and more popular among people. However, its disadvantages are large shrinkage, high diff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D03D13/00D02G3/04D02G3/22D06M15/11D06M13/03D03D15/217D03D15/225D03D15/283D03D15/47D03D15/50
CPCD02G3/045D02G3/22D03D13/00D03D13/008D06M13/03D06M15/11D10B2401/16D10B2401/063D10B2201/24D10B2201/10D10B2331/04D03D15/47
Inventor 熊原刘渊明张一村余胜许鹤陈小谭
Owner JIHUA 3509 TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com