A color masterbatch and toner technology, applied in new color masterbatch and manufacturing fields, can solve the problems of uneven dispersion of toner particles, obvious color difference, unevenness, etc., achieve the best dispersion uniformity, wide application, and improve The effect of product quality
Inactive Publication Date: 2017-05-10
李勇军
View PDF1 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, the manufacturing method of color masterbatch in domestic enterprises is the blending and granulation of resin powder and toner. The color masterbatch produced by this method has two shortcomings. Unevenness causes uneven dispersion, and it is easy to produce crystal points and have obvious color difference when producing plastic films; 2. When using powder resin to produce products, the color masterbatch cannot be blended evenly with powder resin, so it can only be used when producing products with powder resin The color masterbatch cannot be used in color powder; the color masterbatch of the present invention has a particle size of 1-3 microns, is uniformly dispersed, has no crystal points, has a small amount of use, has good gloss, no color difference, and has wide applicability
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0058] Embodiment 1: the color masterbatch of the present invention is made of deionized water, polyvinyl butyral, ethanol, defoamer, stabilizer, plasticizer, dispersant, polyethylene wax, ethylene oxide wax, leveling agent , coupling agent, plastic toner, anti-ultraviolet agent, anti-aging agent;
[0059] 17 parts of said polyvinyl butyral;
[0060] 17 parts of described deionized water;
[0061] 35 parts of ethanol;
[0062] 1 part of the defoamer;
[0063] 0.5 parts of the stabilizer;
[0064] 2.8 parts of said plasticizer;
[0065] 1 part of the dispersant;
[0066] 0.2 part of said polyethylene wax;
[0067] 0.5 parts of said ethylene oxide wax;
[0068] 0.5 parts of the leveling agent;
[0069] 1 part of the coupling agent;
[0070] 21 parts of said plastic toner;
[0071] 1 part of the anti-ultraviolet agent;
[0072] 1.5 parts of the anti-aging agent;
[0073] Said parts are weight fractions.
Embodiment 2
[0074] Embodiment 2: the color masterbatch of the present invention is made of deionized water, polyvinyl butyral, ethanol, defoamer, stabilizer, plasticizer, dispersant, polyethylene wax, ethylene oxide wax, leveling agent , coupling agent, plastic toner, anti-ultraviolet agent, anti-aging agent;
[0075] 10 parts of said polyvinyl butyral;
[0076] 10 parts of said deionized water;
[0077] 20 parts of said ethanol;
[0078] 1.5 parts of the defoamer;
[0079] 1 part of the stabilizer;
[0080] 4.5 parts of said plasticizer;
[0081] 2 parts of the dispersant;
[0082] 3 parts of said polyethylene wax;
[0083] 3 parts of the ethylene oxide wax;
[0084] 3 parts of the coupling agent;
[0085] 2 parts of the leveling agent;
[0086] 35 parts of said plastic toner;
[0087] 2 parts of the anti-ultraviolet agent;
[0088] 3 parts of the anti-aging agent;
[0089] Said parts are weight fractions.
[0090] The preparation method of the color masterbatch of above emb...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a color masterbatch and a manufacturing method, specifically to pigmentation of a variety of plastics. The color masterbatch provided by the invention is composed of deionized water, polyvinyl butyral, ethanol, an antifoaming agent, a stabilizer, a plasticizer, a dispersant, polyethylene wax, ethylene oxide wax, a leveling agent, a coupling agent, plastic pigment powder, an anti-ultraviolet agent and an anti-ageing agent. The color masterbatch provided by the invention is prepared from a variety of raw materials in reasonable proportion, has excellent dispersion uniformity, smoothness, flexibility and low-temperature resistance, and significantly improves the quality of a product; the color masterbatch provided by the invention has two shapes of powder and granule, thereby meeting different addition requirements of powdered resins (like PVC) and granular resins (like PMMA) and achieving the effect of uniform pigmentation; and the color masterbatch provided by the invention is applicable to pigmentation of resins like PVC, ABS, PMMA, PS, polyurethane and epoxy resin.
Description
technical field [0001] The invention relates to a new color masterbatch and a manufacturing method, in particular to the coloring of various plastics. Background technique [0002] At present, the manufacturing method of color masterbatch in domestic enterprises is the blending and granulation of resin powder and toner. The color masterbatch produced by this method has two shortcomings. Unevenness causes uneven dispersion, and it is easy to produce crystal points and have obvious color difference when producing plastic films; 2. When using powder resin to produce products, the color masterbatch cannot be blended evenly with powder resin, so it can only be used when producing products with powder resin The color masterbatch cannot be used in the color powder; the color masterbatch of the present invention has a particle size of 1-3 microns, is uniformly dispersed, has no crystal points, has good gloss with less dosage, has no color difference, and has wide applicability. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more