Composite cored wire of solid metal calcium and magnesium-rare earth alloy containing various elements

A technology of magnesium rare earth alloy and metal calcium, which is applied in the field of alloy powder cored wire

Inactive Publication Date: 2017-05-10
浙江宝信炉料股份有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide a composite cored wire of solid metal calcium and magnesium rare earth alloy containing multiple elements, which can make the process of calcium and magnesium stable and smooth by adding the cored wire into the microalloyed steel Obtain a higher absorption rate, so that the current problems can be better solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044]A composite cored wire of solid metal calcium and magnesium rare earth alloy containing multiple elements, the outer layer of the cored wire is a common steel strip with a thickness of 0.3-0.5 mm, and the core layer includes a rare earth magnesium alloy powder layer, an intermediate protective layer and a solid The core metal calcium wire, the solid core metal calcium wire is wrapped by the middle protective layer, the rare earth magnesium alloy powder layer wraps the middle protective layer, the mass ratio of the solid core metal calcium wire to the rare earth magnesium alloy powder layer is 1:3, and the rare earth magnesium alloy powder layer The particle size is less than 3mm, and the rare earth magnesium alloy powder is composed of the following element components by mass percentage:

[0045] Mg 10%,

[0046] Ca 2.0%,

[0047] Al 1.5%,

[0048] Si 25%,

[0049] Ti 2.0%,

[0050] Ba 3.0%,

[0051] Mn 4.0%,

[0052] Nb 1.0%,

[0053] V 0.5%,

[0054] Rare Earth...

Embodiment 2

[0060] A composite cored wire of solid metal calcium and magnesium rare earth alloy containing multiple elements, the outer layer of the cored wire is a common steel strip with a thickness of 0.3-0.5 mm, and the core layer includes a rare earth magnesium alloy powder layer, an intermediate protective layer and a solid The core metal calcium wire, the solid core metal calcium wire is wrapped by the middle protective layer, the rare earth magnesium alloy powder layer wraps the middle protective layer, the mass ratio of the solid core metal calcium wire to the rare earth magnesium alloy powder layer is 1:3, and the rare earth magnesium alloy powder layer The particle size is less than 3mm, and the rare earth magnesium alloy powder is composed of the following element components by mass percentage:

[0061] Mg 15%,

[0062] Ca 2.5%,

[0063] Al 2.0%,

[0064] Si 30%,

[0065] Ti 25%,

[0066] Ba 2.0%,

[0067] Mn 3.0%,

[0068] Nb 1.0%,

[0069] V 0.5%,

[0070] Rare Earth...

Embodiment 3

[0076] A composite cored wire of solid metal calcium and magnesium rare earth alloy containing multiple elements, the outer layer of the cored wire is a common steel strip with a thickness of 0.3-0.5 mm, and the core layer includes a rare earth magnesium alloy powder layer, an intermediate protective layer and a solid The core metal calcium wire, the solid core metal calcium wire is wrapped by the middle protective layer, the rare earth magnesium alloy powder layer wraps the middle protective layer, the mass ratio of the solid core metal calcium wire to the rare earth magnesium alloy powder layer is 1:3, and the rare earth magnesium alloy powder layer The particle size is less than 3mm, and the rare earth magnesium alloy powder is composed of the following element components by mass percentage:

[0077] Mg 18%,

[0078] Ca 1.5%,

[0079] Al 2.0%

[0080] Si 30%,

[0081] Ti 1.5%,

[0082] Ba 2.5%,

[0083] Mn 3.0%,

[0084] Nb 1.0%,

[0085] V 0.5%,

[0086] Rare Earth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an alloy powder cored wire, in particular to a composite cored wire of solid metal calcium and magnesium-rare earth alloy containing various elements. An outer layer of the cored wire is an ordinary steel strip with a thickness of 0.3-0.5 millimeter; a core layer comprises a rare-earth magnesium alloy powder layer, an intermediate protective layer and a solid metal calcium wire; the solid metal calcium wire is wrapped with the intermediate protective layer; the rare-earth magnesium alloy powder layer wraps the intermediate protective layer; the mass ratio of the solid metal calcium wire to the rare-earth magnesium alloy powder layer is 1:(2-5); the particle size of the rare-earth magnesium alloy powder layer is less than or equal to 3 mm. Calcium and magnesium processing processes can be stabilized through adding into micro-alloyed steel by adopting a cored wire method, and the higher absorption rate is obtained, so that the currently-confronted problem is better solved. The storage time is longer, the yield is more stable, and the economic benefits are significant.

Description

technical field [0001] The invention relates to an alloy powder cored wire. Background technique [0002] my country's steel industry is at its peak in history. In the next few years, it is estimated that my country's annual steel output will reach 1.8 billion tons, and the cored wire market will reach more than 5 billion yuan. According to the statistics of the World Iron and Steel Association, in 2011, the total steel output of all countries in the world reached 1.6 billion tons, an increase of 15%; while China ranked first in the world with an output of 700 million tons. In addition, with the continuous advancement of science and technology, various projects Structural design tends to be high-parameter, lightweight and large-scale. The performance of steel materials requires higher strength and better toughness. Core-spun wire feeding processing technology plays an indispensable and important role in this. [0003] Obtaining products with higher purity and higher uniform...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/06C21C7/064C21C7/00
CPCC21C7/06C21C7/0006C21C7/0056C21C7/0645
Inventor 凌春源
Owner 浙江宝信炉料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com