Method for improving bonding strength of coating

A combination strength and coating technology, which is applied in the direction of coating, metal material coating process, fusion spraying, etc., can solve the problems of reduced life, high porosity, and crack expansion of sprayed coatings, so as to improve the bonding strength and prolong The effect of service performance

Inactive Publication Date: 2017-05-17
ACADEMY OF ARMORED FORCES ENG PLA
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the relatively high porosity of the sprayed coating itself, there are defects such as inclusions and fiber cracks, which make the sprayed coating easy to form cracks and expand during service, resulting in reduced service life
[0005] Texturing has been widely used in the research of anti-friction and anti-wear, and the performance of materials has been greatly improved through the method of texturing. The main reason why texturing can improve the tribological properties of materials is that it can Store wear debris and lubricating oil to provide continuous lubrication to the friction surface, but there are few studies on texturing sprayed coatings, using textured different shapes to change contact conditions and then improving the fatigue resistance of sprayed coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving bonding strength of coating
  • Method for improving bonding strength of coating
  • Method for improving bonding strength of coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1 Preparation of a double-layer texture-coupled coating

[0025] first step:

[0026] Firstly, the substrate is cleaned and polished, and the substrate is preferably stainless steel, specifically FV520B.

[0027] Step two:

[0028] Fabrication of Textured Patterns on Substrate Surfaces Using a Laser Process

[0029] First, make circular and triangular combined textures, circular and grooved combined textures, grid textures, and hexagonal texture patterns in the drawing software, and then use laser processing to prepare textures on the surface of the substrate patterns, such as figure 1 shown.

[0030] Among them, the side length of the hexagonal texture is 150 microns, and the spacing is 200 microns, as shown in 1-1.

[0031] Circular and groove-shaped combined texture, in which the width angle of the groove is 150 microns, the pitch is 200 microns, and the circles with a diameter of 100 microns and a longitudinal pitch of 200 microns are arranged at the pi...

Embodiment 3

[0040] Example 3 The rolling contact fatigue test was carried out on the coating prepared in Example 1, and the slip rate of contact fatigue was changed to observe the anti-fatigue performance of the coating under different slip rate conditions.

[0041] In order to measure various properties of the coating, a NovaNanoSEM450 scanning electron microscope was used to observe the geometric shape of the texture after spraying.

[0042] In order to test the effect of different texture patterns on the fatigue resistance of sprayed coatings, the rolling contact fatigue testing machine was used to test the fatigue properties of sprayed coatings.

[0043] 1. The bonding strength between the coating and the substrate under different shapes and textures on the surface of the substrate

[0044] The bonding strength of the coating is tested by a tensile testing machine, the model of the tensile testing machine used is: MTS809 electronic universal material testing machine. The manufacturer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for improving the bonding strength of a coating. According to the method, through biological bionics simulation, a texturing pattern is prepared on the surface of a base body, and then the coating is prepared on the surface of the base body with the texturing pattern. According to the method, texturing is adopted as a spraying pretreatment means, the bonding strength of the spraying coating is improved through texturing, and accordingly the service performance of the coating is improved.

Description

technical field [0001] The invention relates to the technical field of spraying materials, in particular to a method for improving the bonding strength of coatings. Background technique [0002] Due to the relatively high porosity of the sprayed coating itself, there are defects such as inclusions and fiber cracks, which make the sprayed coating easy to form cracks and expand during the service process, resulting in reduced service life. The improvement of the performance of the existing surface coating is mainly through the use of secondary processing technologies such as laser remelting and surface strengthening after the coating is formed. Although these technical means have played a certain role in improving the performance of the coating, the macroscopic performance is the material internal The external characterization of structure and quality, so these technologies cannot substantially improve the service performance of the fixed internal structure coating. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C4/02C23C4/134C23C4/10
CPCC23C4/02C23C4/10
Inventor 王海斗邢志国王晓丽谭娜马国政
Owner ACADEMY OF ARMORED FORCES ENG PLA